Mesogen containing compounds

ABSTRACT

Compounds including at least one mesogenic substructure and at least one long flexible segment and methods of synthesizing the same are disclosed. Formulations which include various embodiments of the mesogen containing compounds and their use in articles of manufacture and ophthalmic devices are also disclosed.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. Nos. 12/163,116 and 12/163,180 which were filed Jun. 27, 2008, and each of which is hereby specifically incorporated by reference.

BACKGROUND

The present invention relates generally to mesogen containing compounds, formulations thereof, optical elements, liquid crystal polymers and methods of making the same.

The molecules of a liquid crystal (“LC”) tend to align with one another in a preferred direction, yielding a fluid material with anisotropic optical, electromagnetic, and mechanical properties. The mesogen is the fundamental unit of a LC which induces the structural order in the liquid crystals.

Liquid crystal polymers (“LCPs”) are polymers capable of forming regions of highly ordered structure while in a liquid phase. LCPs have a wide range of uses, ranging from strong engineering plastics to delicate gels for LC displays. The structure of LCPs may consist of densely packed fibrous polymer chains that provide self-reinforcement almost to the melting point of the polymer.

Dichroism may occur in LCs due to either the optical anisotropy of the molecular structure or the presence of impurities or the presence of dichroic dyes. As used herein, the term “dichroism”, means the ability to absorb one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other.

Conventional, linearly polarizing elements, such as linearly polarizing lenses for sunglasses and linearly polarizing filters, are typically formed from stretched polymer sheets containing a dichroic material, such as a dichroic dye. Consequently, conventional linearly polarizing elements are static elements having a single, linearly polarizing state. Accordingly, when a conventional linearly polarizing element is exposed to either randomly polarized radiation or reflected radiation of the appropriate wavelength, some percentage of the radiation transmitted through the element will be linearly polarized. As used herein the term “linearly polarize” means to confine the vibrations of the electric vector of light waves to one direction or plane.

Further, conventional linearly polarizing elements are typically tinted. That is, conventional linearly polarizing elements contain a coloring agent (i.e., the dichroic material) and have an absorption spectrum that does not vary in response to actinic radiation. As used herein “actinic radiation” means electromagnetic radiation, such as ultraviolet and visible radiation that is capable of causing a response. The color of the conventional linearly polarizing element will depend upon the coloring agent used to form the element, and most commonly, is a neutral color (for example, brown or gray). Thus, while conventional linearly polarizing elements are useful in reducing reflected light glare, because of their tint, they are not well suited for use under certain low-light conditions. Further, because conventional linearly polarizing elements have only a single, tinted linearly polarizing state, they are limited in their ability to store or display information.

As discussed above, conventional linearly polarizing elements are typically formed using sheets of stretched polymer films containing a dichroic material. As used herein the term “dichroic” means capable of absorbing one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other. Thus, while dichroic materials are capable of preferentially absorbing one of two orthogonal plane polarized components of transmitted radiation, if the molecules of the dichroic material are not suitably positioned or arranged, no net linear polarization of transmitted radiation will be achieved. That is, due to the random positioning of the molecules of the dichroic material, selective absorption by the individual molecules will cancel each other such that no net or overall linear polarizing effect is achieved. Thus, it is generally necessary to suitably position or arrange the molecules of the dichroic material by alignment with another material in order to achieve a net linear polarization.

In contrast to the dichroic elements discussed above, conventional photochromic elements, such as photochromic lenses that are formed using conventional thermally reversible photochromic materials, are generally capable of converting from a first state, for example, a “clear state,” to a second state, for example, a “colored state,” in response to actinic radiation, and then reverting back to the first state in response to thermal energy. As used herein, the term “photochromic” means having an absorption spectrum for at least visible radiation that varies in response to at least actinic radiation. Thus, conventional photochromic elements are generally well suited for use in both low-light conditions and bright conditions. However, conventional photochromic elements that do not include linearly polarizing filters are generally not adapted to linearly polarize radiation. That is, the absorption ratio of conventional photochromic elements, in either state, is generally less than two. As used herein, the term “absorption ratio” refers to the ratio of absorbance of radiation linearly polarized in a first plane to the absorbance of the same wavelength radiation linearly polarized in a plane orthogonal to the first plane, wherein the first plane is taken as the plane with the highest absorbance. Therefore, conventional photochromic elements cannot reduce reflected light glare to the same extent as conventional linearly polarizing elements. Thus, photochromic-dichroic materials have been developed. Photochromic-dichroic materials are materials that display photochromic properties (i.e., having an absorption spectrum for at least visible radiation that varies in response to at least actinic radiation) and dichroic properties (i.e., capable of absorbing one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other).

Photochromic materials and photochromic-dichroic materials may be incorporated into a substrate or an organic material, for example a polymer substrate, including LCP substrates. When photochromic materials and photochromic-dichroic materials undergo a change from one state to another, the molecule(s) of the photochromic compound or photochromic-dichroic compound may undergo a conformational change from one conformational state to a second conformational state. This conformational change may result in a change in the amount of space that the compound occupies. However, for certain photochromic materials and certain photochromic-dichroic materials to effectively transition from one state to another, for example to transition from a clear state to a colored state, to transition from a colored state to a clear state, to transition from a non-polarized state to a polarized state, and/or to transition from a polarized state to a non-polarized state, the photochromic compound or photochromic-dichroic compound must be in an chemical environment that is sufficiently flexible to allow the compound to transition from one conformational state to the second conformational state at a rate that is sufficient to provide the desired response on over an acceptable time frame. Therefore, new polymeric materials, such as new LCPs, and materials to form these new materials are necessary to further develop photochromic and photochromic-dichroic materials and substrates.

BRIEF SUMMARY OF THE DISCLOSURE

Various aspects of the present disclosure relate to novel mesogen containing compounds and formulations formed therefrom, optical elements, liquid crystal polymers and methods of making the same.

The present disclosure provides for a mesogen containing compound represented by one of the following structures:

wherein,

-   a) each X is independently:     -   i) a group R,     -   ii) a group represented by -(L)_(y)-R,     -   iii) a group represented by -(L)-R,     -   iv) a group represented by -(L)_(w)-Q;     -   v) a group represented by

-   -   vi) a group represented by -(L)_(y)-P; or     -   vi) a group represented by -(L)_(w)-[(L)_(w)-P]_(y);

-   b) each P is a reactive group independently selected from a group Q,     amino, alkylamino, nitro, acrylate, methacrylate, 2-chloroacrylate,     2-phenylacrylate, acryloylphenylene, acrylamide, methacrylamide,     2-chloroacrylamide, 2-phenylacrylamide, oxetane, glycidyl, cyano,     vinyl ether, vinyl ester, a styrene derivative, siloxane,     ethyleneimine derivatives, or substituted or unsubstituted chiral or     non-chiral monovalent or divalent groups chosen from steroid     radicals, terpenoid radicals, alkaloid radicals and mixtures     thereof, wherein the substituents are independently chosen from     alkyl, alkoxy, amino, cycloalkyl, alkylalkoxy, fluoroalkyl, cyano,     cyanoalkyl, cyanoalkoxy or mixtures thereof, or P is a structure     having from 2 to 4 reactive groups or P is an unsubstituted or     substituted ring opening metathesis polymerization precursor;

-   c) the group Q is hydroxy, amine, alkenyl, alkynyl, azido, silyl,     silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol, isocyanato,     thioisocyanato, acryloxy, methacryloxy, 2-(acryloxy)ethylcarbamyl,     2-(methacryloxy)ethylcarbamyl, aziridinyl, allyloxycarbonyloxy,     epoxy, carboxylic acid, carboxylic acid derivatives particularly     selected from carboxylic ester, amide and carboxylic anhydride, or     acyl halide, preferably the carboxylic acid derivatives are selected     from itaconic acid ester, maleic acid derivatives, fumaric acid     derivatives, unsubstituted cinnamic acid derivatives, cinnamic acid     derivatives that are substituted with at least one of methyl,     methoxy, cyano and halogen;

-   d) each L is independently chosen for each occurrence, the same or     different, from a single bond, a polysubstituted, monosubstituted,     unsubstituted or branched spacer independently chosen from arylene,     (C₁-C₃₀)alkylene, (C₁-C₃₀)alkylenecarbonyloxy,     (C₁-C₃₀)alkyleneamino, (C₁-C₃₀)alkyleneoxy,     (C₁-C₃₀)perfluoroalkylene, (C₁-C₃₀)perfluoroalkyleneoxy,     (C₁-C₃₀)alkylenesilyl, (C₁-C₃₀)dialkylenesiloxyl,     (C₁-C₃₀)alkylenecarbonyl, (C₁-C₃₀)alkyleneoxycarbonyl,     (C₁-C₃₀)alkylenecarbonylamino, (C₁-C₃₀)alkyleneaminocarbonyl,     (C₁-C₃₀)alkyleneaminocarbonyloxy,     (C₁-C₃₀)alkyleneaminocarbonylamino, (C₁-C₃₀)alkyleneurea,     (C₁-C₃₀)alkylenethiocarbonylamino,     (C₁-C₃₀)alkyleneaminocarbonylthio, (C₂-C₃₀)alkenylene,     (C₁-C₃₀)thioalkylene, (C₁-C₃₀)alkylenesulfone, or     (C₁-C₃₀)alkylenesulfoxide, wherein each substituent is independently     chosen from (C₁-C₅)alkyl, (C₁-C₅)alkoxy, fluoro, chloro, bromo,     cyano, (C₁-C₅)alkanoate ester, isocyanato, thioisocyanato, or     phenyl;

-   e) the group R is selected from hydrogen, C₁-C₁₈ alkyl, C₁-C₁₈     alkoxy, C₁-C₁₈ alkoxycarbonyl, C₃-C₁₀ cycloalkyl, C₃-C₁₀     cycloalkoxy, poly(C₁-C₁₈ alkoxy), or a straight-chain or branched     C₁-C₁₈alkyl group that is unsubstituted or substituted with cyano,     fluoro, chloro, bromo, or C₁-C₁₈ alkoxy, or poly-substituted with     fluoro, chloro, or bromo; and

-   f) the groups Mesogen-1 and Mesogen-2 are each independently a rigid     straight rod-like liquid crystal group, a rigid bent rod-like liquid     crystal group, or a rigid disc-like liquid crystal group;

-   g) the group T is selected from P and hydrogen, aryl, alkyl, alkoxy,     alkylalkoxy, alkoxyalkoxy, polyalkylether, (C₁-C₆)alkyl     (C₁-C₆)-alkoxy(C₁-C₆)alkyl, polyethyleneoxy and polypropyleneoxy.     wherein w is an integer from 1 to 26, y is an integer from 2 to 25,     z is 1 or 2, provided that when:

-   (i) the group X is represented by R, then w is an integer from 2 to     25, and z is 1;

-   (ii) the group X is represented by -(L)_(y)-R, then w is 1, y is an     integer from 2 to 25, and z is 1;

-   (iii) the group X is represented by -(L)_(w)-R, then w is an integer     from 3 to 26, and z is 2;

-   (iv) the group X is represented by -(L)_(w)-Q; then if P is     represented by the group Q at least one Q is selected from hydroxy,     azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol,     isocyanato, thioisocyanato, 2-(acryloxy)ethylcarbamyl,     2-(methacryloxy)ethyl-carbamyl, aziridinyl, allyloxycarbonyloxy,     carboxylic acid, carboxylic ester, amide, carboxylic anhydride, and     acyl halide, then w is 1, and z is 1; and if P is other than the     group Q, then each w is independently an integer from 1 to 26, and z     is 1;

-   (v) the group X is represented by

then w is 1, y is an integer from 2 to 25, with the proviso that -(L)_(y)- comprises at least two groups L that are different from a single bond and z is 1;

-   (vi) the group X is represented by -(L)_(y)-P, with the proviso that     at least one P is different from an oxetane functional group, then w     is 1, y is an integer from 2 to 25, and z is 1 and -(L)_(y)-     comprises a linear sequence of at least 25 bonds, preferably at     least 30 bonds between the mesogen and P; -   (vii) the group X is represented by -(L)_(w)-[(L)_(w)-P]_(y), then     each w is independently an integer from 1 to 25, y is an integer     from 2 to 6, whereby and z is 1; and in -(L)_(y)- and -(L)_(w)- no     two arylene groups are linked by a single bond.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

Aspects of the present disclosure will be better understood when read in conjunction with the figures, in which:

FIGS. 1-13 illustrate exemplary methods for synthesizing certain embodiments of the mesogen containing compounds described herein. In particular:

FIG. 1 illustrates Lewis acid catalyzed or base catalyzed processes for synthesizing a mesogen containing soft chain acrylate system;

FIGS. 2A and 2B illustrate a process for synthesizing a bi-mesogen containing compound having a structure according to Formula V;

FIGS. 3 and 4 illustrate two processes for synthesizing bi-mesogen containing compounds having structures according to Formula IV;

FIG. 5 illustrates the use of a Mitsunobo coupling reaction for synthesizing a bi-mesogen containing compound having a structure according to Formula IV;

FIG. 6 illustrates a process for synthesizing mesogen containing compounds having a structure according to Formula VI or VII;

FIG. 7 illustrates the use of a polycarbonate linking group according to certain embodiments of Formula II;

FIG. 8 illustrates a process for synthesizing a mesogen containing compound having a structure according to Formula III;

FIG. 9 illustrates a process for synthesizing a bi-mesogen containing compound having a structure according to Formula VI;

FIGS. 10 and 11 illustrate processes for synthesizing mesogen containing compounds having structures according to Formula VI;

FIG. 12 illustrates a process for synthesizing mesogen containing compounds having structures according to Formula VI or VII; and

FIG. 13 illustrates a process for synthesizing mesogen containing compounds having a structure according to Formula VIII.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Mesogen containing compounds and liquid crystal compositions and formulations containing the mesogen containing compounds according to the present disclosure will now be described. The mesogen containing compounds disclosed herein provide novel structures that may be used for a variety of applications, including, for example, formulations and compositions that may be used, for example liquid crystal polymers (“LCPs”), in optical elements including for example, ophthalmic elements, display elements, windows, and mirrors. According to certain aspects of the present disclosure the mesogen containing compounds of the present disclosure may act as monomers for the formation of LCPs.

The mesogen is the fundamental unit of a liquid crystal (“LC”), which induces the structural order in the liquid crystal. The mesogenic portion of the LC typically comprises a rigid moiety which aligns with other mesogenic components in the LC composition, thereby aligning the LC molecules in one direction. The rigid portion of the mesogen may consist of a rigid molecular structure, such as a mono or polycyclic ring structure, including, for example a mono or polycyclic aromatic ring structures. Examples of potential mesogens are set forth in greater detail herein and include those mesogenic compounds set forth in Demus et al., “Flussige Kristalle in Tabellen,” VEB Deutscher Verlag für Grundstoffindustrie, Leipzig, 1974 and “Flussige Kristalle in Tabellen II,” VEB Deutscher Verlag für Grundstoffindustrie, Leipzig, 1984. LCs may also include one or more flexible portions in the LC molecule. The one or more flexible portions may impart fluidity to the LC. LCs may exist in a non-ordered state or an ordered (or aligned) state. The LC molecules in the non-ordered state will adopt an essentially random orientation, that is there will be no general orientation to the LC molecules. The LC molecules in the ordered or aligned state will generally adopt an orientation where the mesogenic portions of the LC molecules are at least partially aligned throughout the LC material. As used herein, the terms “align” or “aligned” means to bring into suitable arrangement or position by interaction with another material, compound or structure. In certain embodiments, the mesogenic portions of the LC molecules may be at least partially aligned in a parallel orientation. In other embodiments, the mesogenic portions of the LC molecules may be at least partially aligned in a helical orientation, such as in a reflective polarizer.

The mesogen containing compounds of the present disclosure may be used for a variety of functions including LC compositions and as monomers for the synthesis of LCPs. The mesogen containing compounds of the present disclosure may behave as monomers to form polymers or may act as non-monomeric components, such as non-monomeric LC components. The mesogen containing compounds may form crosslinked networks or LCPs. As used herein the term “compound” means a substance formed by the union of two or more elements, components, ingredients, or parts and includes, molecules and macromolecules (for example polymers and oligomers) formed by the union of two or more elements, components, ingredients, or parts. The compositions formed from the mesogen containing compounds may have a variety of uses, including, as layers, such as, cured coatings and films on at least a portion of a substrate, which may impart certain desired characteristics to the substrate, and as articles of manufacture, such as, molded articles, assembled articles and cast articles. For example, the compositions formed from the mesogen containing compounds may be used, for example, as at least partial layers, coatings or films on at least a portion of a substrate which may impart certain desired characteristics to the substrate, such as, for use in optical data storage applications, as photomasks, as decorative pigments; in cosmetics and for security applications (see, for example U.S. Pat. No. 6,217,948; as curable resins for medical, dental, adhesive and stereolithographic applications (see, for example, U.S. Pat. No. 7,238,831); as articles of manufacture, such as, molded assembled, or cast articles for use in the aforementioned applications and various related devices.

The mesogen containing compositions may be formulated into LCs and/or LCPs which may be used or incorporated into optical elements such as, for example, ophthalmic elements, display elements, windows, mirrors, active and passive liquid crystal cells, elements and devices, and other LC or LCP containing articles of interest, such as, polarizers, optical compensators (see, for example, U.S. Pat. No. 7,169,448), optical retarders (see, for example, U.S. Reissue Pat. No. RE39,605 E), color filters, and waveplates for lightwave circuits (see, for example, U.S. Pat. No. 7,058,249). For example, the LCPs may be used to form optical films such as retarders, wave guides, reflectors, circular polarizers, wide view angle films, etc. Specific embodiments of the mesogen containing compounds may find particular use as LC monomers for the formation of ophthalmic elements which further comprise at least one photochromic or photochromic-dichroic material or compound. As will be described in more detail herein, the mesogen containing materials of various embodiments of the present disclosure may be particularly suited to give the desired kinetic properties for certain photochromic or photochromic-dichroic materials, such as ophthalmic elements and optical elements. In other embodiments, the LCPs may also be used as a host material for dyes, such as photosensitive and non-photosensitive materials. Photosensitive materials may include organic photochromic materials such as thermally and non-thermally reversible materials as well as photochromic/dichroic material, inorganic photochromic materials, fluorescent or phosphorescent materials and non-linear optical materials (“NLOs”). Non-photosensitive materials may include fixed tint dyes, dichroic materials, thermochroic materials, and pigments.

The mesogen containing compounds of the present disclosure generally comprise at least one mesogen unit, at least one reactive group, and at least one flexible linking group which may be from 1 to 500 atomic bonds in linear length and may therefore act as LCs, which may be incorporated into materials or compositions which display LC properties or may be used as LC monomers, for example, for the formation of LCPs.

According to one embodiment, the mesogen containing compounds of the present disclosure may be represented by a compound having Formula I:

In Formula I, each X may be independently represented by: (i) a group —R; (ii) a group represented by the structure -(L)_(y)-R; (iii) a group represented by the structure -(L)-R; (iv) a group represented by the structure -(L)_(w)-Q; (v) a group represented by the structure:

(vi) a group represented by -(L)_(y)-P; or (vii) a group represented by -(L)_(w)-[(L)_(w)-P]_(y). Further, in Formula I, each group P represents a reactive group as defined above. For example the reactive group may react with a group, react with a comonomer or a reactive group on a developing polymer such that the structure corresponding to Formula I or a residue thereof is incorporated into the polymer.

Further, in certain embodiments P may be a reactive group comprising a polymerizable group, wherein the polymerizable group may be any functional group adapted to participate in a polymerization reaction. Examples of polymerization reactions include those described in the definition of “polymerization” in Hawley's Condensed Chemical Dictionary Thirteenth Edition, 1997, John Wiley & Sons, pages 901-902. For example polymerization reactions include: “addition polymerization,” in which free radicals are the initiating agents that react with the double bond of a monomer by adding to it on one side at the same time producing a new free electron on the other side; “condensation polymerization,” in which two reacting molecules combine to form a larger molecule with elimination of a small molecule, such as a water molecule; and “oxidative coupling polymerization.” For example P may be an unsubstituted or substituted ring opening metathesis polymerization precursor. Further examples of polymerizable groups include hydroxy, acryloxy, methacryloxy, 2-(acryloxy)ethylcarbamyl, 2-(methacryloxy)ethylcarbamyl, isocyanato, aziridine, allyloxycarbonyloxy, and epoxy, e.g., oxiranylmethyl. In other embodiments, P may have a structure having a plurality of reactive groups, such as the reactive groups disclosed herein. For example, P may have a structure having from 2 to 4 reactive groups, as described herein. In certain embodiment, having multiple reactive groups on P may allow for more effective incorporation into a polymer or allow for cross-linking between individual polymer strands. Suitable examples of P groups with multiple reactive groups include diacryloyloxy(C₁-C₆)alkyl; diacryloyloxyaryl; triacryloyloxy(C₁-C₆)alkyl; triacryloyloxyaryl; tetraacryloyloxy(C₁-C₆)alkyl; tetraacryloyloxyaryl; dihydroxy(C₁-C₆)alkyl; trihydroxy(C₁-C₆)alkyl; tetrahydroxy(C₁-C₆)alkyl; diepoxy(C₁-C₆)alkyl; diepoxyaryl; triepoxy(C₁-C₆)alkyl; triepoxyaryl; tetraepoxy(C₁-C₆)alkyl; tetraepoxyaryl; diglycidyloxy(C₁-C₆)alkyl; diglycidyloxyaryl; triglycidyloxy(C₁-C₆)alkyl; triglycidyloxyaryl; tetraglycidyloxy(C₁-C₆)alkyl; and tetraglycidyloxyaryl.

Further, with reference to Formula I, each group Q may represent hydroxy, amine, alkenyl, alkynyl, azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), isocyanato, thiol, thioisocyanato, carboxylic acid, carboxylic ester, amide, carboxylic anhydride, or acyl halide. In certain embodiments, the group Q may act as a reactive group such that a mesogen containing compound comprising at least one group Q may be incorporated into the backbone of a polymer or copolymer. For example, Q may be a polymerizable group, such as those described herein, including a group selected from hydroxy, acryloxy, methacryloxy, 2-(acryloxy)ethylcarbamyl, 2-(methacryloxy)ethylcarbamyl, isocyanato, thiol, thioisocyanato, aziridine, allyloxycarbonyloxy, carboxylic acid or carboxylic acid derivative, and epoxy, e.g., oxiranylmethyl. As used herein, the terms “(meth)acryloxy” and “(meth)acryloyloxy” are used interchangeably and refer to a substituted or unsubstituted prop-2-en-1-oyloxy structure.

As described herein and with reference to Formula I, the groups L, (L)_(y) or (L)_(w) represents a linking group preferably, having a linear length of from 1 to 500 atomic bonds. That is, for the general structure F-L-E, the longest linear length of the linking group between groups F and E (where groups F and E may each generally represent any of groups P, R, Q, X, T or a mesogen) may range from 1 to 500 bonds (inclusive of the intervening atoms). It should be understood that when discussing the linear length of the linking group, one of ordinary skill in the art will understand that the length of the linking group may be calculated by determining the length of each of the bonds in the linear sequence and the distance occupied by the various intervening atoms in the linear sequence of the linking group and totaling the values. In certain embodiments, the longest linear sequence of bonds may be at least 25 bonds between the linked groups. In other embodiments, the longest linear sequence of bonds may be at least 30 bonds. In still other embodiments, the longest linear sequence of bonds may be at least 50 bonds. It has been determined that, in certain embodiments, a linking group L with at least 25 bonds improves a variety of benefits for the resulting mesogen containing compound. For example, a linking group of at least 25 bonds may improve the solubilities of the additives, such as the photochromic compounds in compositions comprising the mesogen containing compounds; may provide for faster or improved alignment properties of the compositions comprising the mesogen containing compounds; and/or may lower the viscosity of a composition comprising the mesogen containing compound.

Each group L may be independently chosen for each occurrence, the same or different, from a single bond, a polysubstituted, monosubstituted or unsubstituted spacer as defined above. “w” is represented by an integer from 1 to 26, “y” is represented by an integer from 2 to 25, and “z” is either 1 or 2. It should be noted that when more than one L group occurs in sequence, for example in the structure (L)_(y) or (L)_(w) where “y” and/or “w” is an integer greater than 1, then the adjacent L groups may or may not have the same structure. That is, for example, in a linking group having the structure -(L)₃- or -L-L-L- (i.e., where “y” or “w” is 3), each group -L- may be independently chosen from any of the groups L recited above and the adjacent -L- groups may or may not have the same structure. For example, in one exemplary embodiment, -L-L-L- may represent —(C₁-C₃₀)alkylene-(C₁-C₃₀)alkylene-(C₁-C₃₀)alkylene- (i.e., where each occurrence of -L- is represented by (C₁-C₃₀)alkylene, where each adjacent (C₁-C₃₀)alkylene group may have the same or different number of carbons in the alkylene group). In another exemplary embodiment, -L-L-L- may represent -arylene-(C₁-C₃₀)alkylsilylene-(C₁-C₃₀)alkenoxy- (i.e., where each occurrence of -L- differs from the adjacent groups -L-). Thus, the structure of (L)_(y) or (L)_(w) should be understood as covering all possible combinations of the various sequences of the linking groups -L-, including those where some or all of the adjacent -L- groups are the same and where all the adjacent -L- groups are different, provided that no two arylene groups are linked by a single bond.

Still with reference to Formula I, the group R represents an end group as defined above.

With further reference to Formula I, the groups Mesogen-1 and Mesogen-2 are each independently a rigid straight rod-like liquid crystal group, a rigid bent rod-like liquid crystal, or a rigid disc-like liquid crystal group. The structures for Mesogen-1 and Mesogen-2 may be any suitable mesogenic group known in the art, for example, any of those recited in Demus et al., “Flüssige Kristalle in Tabellen,” VEB Deutscher Verlag für Grundstoffindustrie, Leipzig, 1974 or “Flüssige Kristalle in Tabellen II,” VEB Deutscher Verlag für Grundstoffindustrie, Leipzig, 1984. Further, according to certain embodiments, the groups Mesogen-1 and Mesogen-2 may independently have a structure represented by: —[S¹]_(c)-[G¹-[S²]_(d)]_(d′)-[G²-[S³]_(e)]_(e′)-[G³-[S⁴]_(f)]_(f′)—S⁵— The mesogen structure, above, is further defined such that each group each G¹, G², and G³ may independently be chosen for each occurrence from: a divalent group chosen from: an unsubstituted or a substituted aromatic group, an unsubstituted or a substituted alicyclic group, an unsubstituted or a substituted heterocyclic group, and mixtures thereof, wherein substituents are chosen from: thiol, amide, hydroxy(C₁-C₁₈)alkyl, isocyanato(C₁-C₁₈)alkyl, acryloyloxy, acryloyloxy(C₁-C₁₈)alkyl, halogen, C₁-C₁₈ alkoxy, poly(C₁-C₁₈ alkoxy), amino, amino(C₁-C₁₈)alkylene, C₁-C₁₈ alkylamino, di-(C₁-C₁₈)alkylamino, C₁-C₁₈ alkyl, C₂-C₁₈ alkene, C₂-C₁₈ alkyne, C₁-C₁₈ alkyl(C₁-C₁₈)alkoxy, C₁-C₁₈ alkoxycarbonyl, C₁-C₁₈ alkylcarbonyl, C₁-C₁₈ alkyl carbonate, aryl carbonate, perfluoro(C₁-C₁₈)alkylamino, di-(perfluoro(C₁-C₁₈)alkyl)amino, C₁-C₁₈ acetyl, C₃-C₁₀ cycloalkyl, C₃-C₁₀ cycloalkoxy, isocyanato, amido, cyano, nitro, a straight-chain or branched C₁-C₁₈ alkyl group that is mono-substituted with cyano, halo, or C₁-C₁₈ alkoxy, or poly-substituted with halo, and a group comprising one of the following formulae: -M(T)_((t-1)) and -M(OT)_((t-1)), wherein M is chosen from aluminum, antimony, tantalum, titanium, zirconium and silicon, T is chosen from organofunctional radicals, organofunctional hydrocarbon radicals, aliphatic hydrocarbon radicals and aromatic hydrocarbon radicals, and t is the valence of M. Further, in the mesogenic structure, “c”, “d”, “e”, and “f” may be each independently chosen from an integer ranging from 0 to 20, inclusive and “d′”, “e′” and “f′” are each independently an integer from 0 to 4 provided that a sum of d′+e′+f′ is at least 1. Still with reference to the mesogenic structure above, the groups S represent spacer groups such that each of groups S¹, S², S³, S⁴, and S⁵ may be independently chosen for each occurrence from a spacer unit chosen from:

-   (A) —(CH₂)_(g)—, —(CF₂)_(h)—, —Si(CH₂)_(g)—, or —(Si(CH₃)₂O)_(h)—,     wherein “g” is independently chosen for each occurrence from 1 to 20     and “h” is a whole number from 1 to 16 inclusive; -   (B) —N(Z)—, —C(Z)═C(Z)—, —C(Z)═N—, —C(Z′)₂—C(Z′)₂—, or a single     bond, wherein Z is independently chosen for each occurrence from     hydrogen, C₁-C₆alkyl, cycloalkyl and aryl, and Z′ is independently     chosen for each occurrence from C₁-C₆ alkyl, cycloalkyl and aryl; or -   (C) —O—, —C(O)—, —C≡C—, —N═N—, —S—, —S(O)—, —S(O)(O)—, —(O)S(O)O—,     —O(O)S(O)O— or straight-chain or branched C₁-C₂₄ alkylene residue,     said C₁-C₂₄ alkylene residue being unsubstituted, mono-substituted     by cyano or halo, or poly-substituted by halo; -   provided that when two spacer units comprising heteroatoms are     linked together the spacer units are linked so that heteroatoms are     not directly linked to each other and when S₁ and S₅ are linked to     another group, they are linked so that two heteroatoms are not     directly linked to each other.

According to various embodiments disclosed herein, in the structure of the mesogen, above, “c”, “d”, “e”, and “f” each can be independently chosen from an integer ranging from 1 to 20, inclusive; and “d′”, “e′” and “f′” each can be independently chosen from 0, 1, 2, 3, and 4, provided that the sum of d′+e′+f′ is at least 1. According to other embodiments disclosed herein, “c”, “d”, “e”, and “f” each can be independently chosen from an integer ranging from 0 to 20, inclusive; and “d′”, “e′” and “f′” each can be independently chosen from 0, 1, 2, 3, and 4, provided that the sum of d′+e′+f′ is at least 2. According to still other embodiments disclosed herein, “c”, “d”, “e”, and “f” each can be independently chosen from an integer ranging from 0 to 20, inclusive; and “d′”, “e′” and “f′” each can be independently chosen from 0, 1, 2, 3, and 4, provided that the sum of d′+e′+f′ is at least 3. According to still other embodiments disclosed herein, “c”, “d”, “e”, and “f” each can be independently chosen from an integer ranging from 0 to 20, inclusive; and “d′”, “e′” and “f′” each can be independently chosen from 0, 1, 2, 3, and 4, provided that the sum of d′+e′+f′ is at least 1.

The group T is selected from P as defined above and hydrogen, aryl, alkyl, alkoxy, alkylalkoxy, alkoxyalkoxy, polyalkylether, (C₁-C₆)alkyl(C₁-C₆)-alkoxy(C₁-C₆)alkyl, polyethyleneoxy and polypropyleneoxy

Finally, with reference to Formula I, the structure of the mesogen containing compound requires that:

-   (i) the group X is represented by R, then w is an integer from 2 to     25, and z is 1; -   (ii) the group X is represented by -(L)_(y)-R, then w is 1, y is an     integer from 2 to 25, and z is 1; -   (iii) the group X is represented by -(L)_(w)-R, then w is an integer     from 3 to 26, and z is 2; -   (iv) the group X is represented by -(L)_(w)-Q; then if P is     represented by the group Q at least one Q is selected from hydroxy,     azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol,     isocyanato, thioisocyanato, 2-(acryloxy)ethylcarbamyl,     2-(methacryloxy)ethyl-carbamyl, aziridinyl, allyloxycarbonyloxy,     carboxylic acid, carboxylic ester, amide, carboxylic anhydride, and     acyl halide, then w is 1, and z is 1; and if P is other than the     group Q, then each w is independently an integer from 1 to 26, and z     is 1; -   (vi) the group X is represented by

then w is 1, y is an integer from 2 to 25, with the proviso that -(L)_(y)- comprises at least two groups L that are different from a single bond and z is 1;

-   (vi) the group X is represented by -(L)_(y)-P, with the proviso that     at least one P is different from an oxetane functional group, then w     is 1, y is an integer from 2 to 25, and z is 1 and -(L)_(y)-     comprises a linear sequence of at least 25 bonds, preferably at     least 30 bonds between the mesogen and P; -   (viii) the group X is represented by -(L)_(w)-[(L)_(w)-P]_(y), then     each w is independently an integer from 1 to 25, y is an integer     from 2 to 6, whereby and z is 1; and in -(L)_(y)- and -(L)_(w)- no     two arylene groups are linked by a single bond.

According to certain embodiments of the mesogen containing compound, the mesogen containing compound may be a functional mono-mesogen containing compound (i.e., a mesogen containing compound that contains one mesogenic structure). According to one embodiment, the functional mono-mesogen containing compound may have a structure represented by Formula I, wherein the group X is represented by —R, “w” is an integer from 2 to 25, and “z’ is 1. According to another embodiment, the functional mono-mesogen containing compound may have a structure represented by Formula I, wherein the group X is represented by -(L)_(y)-R, “w” is 1, “y” is an integer from 2 to 25, and “z” is 1.

According to other embodiments of the mesogen containing compound, the mesogen containing compound may be a functional bi-mesogen containing compound (i.e., a mesogen containing compound that contains two mesogenic structures (which may be the same or different)). For various embodiments, the structures of the functional bi-mesogen containing compound will have a long chain linking group between the two mesogenic units. According to one embodiment, the functional bi-mesogen containing compound may have a structure represented by Formula I, wherein the group X is represented by

w is 1, y is an integer from 2 to 25, with the proviso that -(L)_(y)- comprises at least two groups L that are different from a single bond and z is 1.

In another embodiment of the mesogen containing compound, the mesogen containing compound may be a functional mono-mesogen containing compound (i.e., a mesogen containing compound that contains one mesogenic structure). The functional mono-mesogen containing compound may have a structure represented by Formula I, wherein the group X is represented by -(L)_(w)-Q and if P is represented by the group Q at least one Q is selected from hydroxy, azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol, isocyanato, thioisocyanato, 2-(acryloxy)ethylcarbamyl, 2-(methacryloxy)ethylcarbamyl, aziridinyl, allyloxycarbonyloxy, carboxylic acid, carboxylic ester, amide, carboxylic anhydride, and acyl halide, then w is 1, and z is 1; and if P is other than the group Q, then each w is independently an integer from 1 to 26, and z is 1. According to these embodiments, the mesogen containing compound is a di-functional monomer that may be incorporated into a polymer backbone. That is, the mesogen containing group will be incorporated into the polymer backbone and be attached at each end to the formed polymer by the residues of the group(s) Q. As used herein, the term “residue” means that which remains after reaction of a reactive group. In another embodiment, the functional mono-mesogen containing compound may have a structure represented by Formula I, wherein the group X is represented by the -(L)_(y)-P, with the proviso that at least one P is different from an oxetane functional group “w” is 1, “y” is an integer from 2 to 25, and “z” is 1; and -(L)_(y)- comprises a linear sequence of at least 25 bonds, preferably of at least 30 bonds between the mesogen and P. In specific embodiments, -(L)_(y)- may comprise a linear sequence of at least 50 bonds between the mesogen and P. In another embodiment, the mesogen containing compound may have a structure according to Formula I wherein the group X is represented by the structure -(L)_(w)-[(L)_(w)-P]_(y), each “w” is independently an integer from 1 to 25, “y” is an integer from 2 to 6, and “z” is 1. According to these embodiments, the mesogen containing compound may have from 3 to 7 reactive groups P.

According to various embodiments, the mesogen containing compound of the present disclosure, as represented by Formula I, may be a liquid crystal monomer. As used herein, the term “liquid crystal monomer” means a monomeric compound that may display liquid crystal properties in the monomeric state and/or in the polymeric state. That is, the liquid crystal monomer may display liquid crystal properties by itself and/or after it has been incorporated into a polymer or copolymer to form a LCP. One skilled in the art will recognize that when the mesogen compound is in the polymeric state, it has been reacted with other monomers and/or co-monomers to form the polymer and is therefore a residue of the liquid crystal monomer.

Thus, embodiments of the present disclosure also contemplate a polymer or copolymer which comprises the mesogen containing compounds or residues thereof according to the various embodiments described herein. For example, according to one embodiment, the polymer or copolymer may comprise the mesogen containing compound, such as a monomeric compound which is suspended or mixed in the polymer or copolymer composition. In another embodiment, the polymer or copolymer may comprise a residue of the mesogen containing compound. According to one example, the residue of the mesogen containing compound may be incorporated into the polymeric structure, for example, as part of the polymeric backbone, or as a monomer incorporated into the backbone and forming a side chain off the backbone. In another example, the residue of the mesogen containing compound may have been reacted with another reactant (thereby forming the residue) and the product of that reaction may be suspended or mixed into the polymer or copolymer.

According to certain embodiments, the polymer compositions comprising the mesogen containing compounds or residues thereof, as described herein, may be liquid crystal polymers. For example, the LCPs may be an anisotropic LCP, an isotropic LCP, a thermotropic LCP or a lyotropic LCP. In various embodiments, the LCPs may display at least one of a nematic phase, a smectic phase, a chiral nematic phase (i.e., a cholesteric phase), a discotic phase (including chiral discotic), a discontinuous cubic phase, a hexagonal phase, a bicontinuous cubic phase, a lamellar phase, a reverse hexagonal columnar phase, or an inverse cubic phase. In addition, in certain LCPs of the present disclosure, the LC monomers or residues thereof may transition from one phase to another, for example, in response to thermal energy or actinic radiation.

In particular embodiments, the present disclosure provides a liquid crystal monomer represented by the structure according to Formula II or Formula III:

According to these embodiments, the group P in either Formula II or III may be a reactive group such as those set forth in the listing for P described herein and including those P groups comprising polymerizable groups, a plurality of reactive groups, or ring opening metathesis polymerization precursors. The group Q may independently be any of those groups listed for group Q herein. Further, in either Formula II or III, the group (L) may be independently chosen for each occurrence, which may be the same or different, from the listing of possible (L) groups set forth herein. In either Formula II or III, the group R may be selected from the listing of possible R groups set forth herein. The mesogen component in either Formula II or III may be a rigid straight rod-like liquid crystal group, a rigid bent rod-like liquid crystal group, or a rigid disc-like liquid crystal group, such as the mesogens set forth herein including, those having the structure: —[S¹]_(c)-[G¹-[S²]_(d)]_(d′)-[G²-[S³]_(e)]_(e′)-[G³-[S⁴]_(f)]_(f′)—S⁵— as further defined herein. In addition, in Formulae II and II, “w” may be an integer ranging from 2 to 25 and “y” may be an integer ranging from 2 to 25.

In other embodiments, the present disclosure provides for a bi-mesogen liquid crystal monomer represented by the structure according to Formula IV or Formula V:

According to these embodiments, each group P in either Formula IV or V may independently be a reactive group such as those set forth in the listing for P described herein and including those P groups comprising polymerizable groups, a plurality of reactive groups, or ring opening metathesis polymerization precursors. The group Q may independently be any of those groups listed for group Q herein. Further, in either Formula IV or V, the group (L) may be independently chosen for each occurrence, which may be the same or different, from the listing of possible (L) groups set forth herein. In either Formula IV or V, each group R may be independently selected from the listing of possible R groups set forth herein. The mesogen components in either Formula IV or V may have rigid straight rod-like liquid crystal groups, rigid bent rod-like liquid crystal groups, rigid disc-like liquid crystal groups or a combination thereof. Thus, Mesogen-1 and Mesogen-2 of either Formula IV or V may be independently selected from the mesogen structures set forth herein including those having the structure: —[S¹]_(c)-[G¹-[S²]_(d)]_(d′)-[G²-[S³]_(e)]_(e′)-[G³-[S⁴]_(f)]_(f′)—S⁵— as further defined herein. In addition, in Formulae IV and V, “w” may be an integer ranging from 2 to 25.

In still another embodiment, the present disclosure provides for a bi-functional liquid crystal monomer represented by the structure according to Formula VI:

as defined above with respect to the structure according to Formula IX being -(L)_(w)-Q.

In further embodiments, the present disclosure provides for a liquid crystal monomer represented by the structure according to Formula VII:

as defined above with respect to the structure according to Formula IX being -(L)_(y)-P.

In further embodiments, the present disclosure provides for a liquid crystal monomer represented by the structure according to Formula VIII:

as defined above with respect to the structure according to Formula IX being -(L)_(w)-[(L)_(w)-P]_(y).

According to the various embodiments of the mesogen containing compounds disclosed herein, the structure of the mesogen containing compound, for example as represented by Formulae I-VIII as described in detail herein, may be designed to include a long flexible linking group between one or more portions of the compound. For example, in the various structures of the mesogen containing compounds disclosed herein, the linking groups -(L)_(y)- and/or -(L)_(w)- and in certain cases the group -(L)- (for example, when -(L)- comprises at least 25 linear bonds) may be a long flexible linking group comprising a long linear sequence of chemical bonds, ranging from 25 to 500 chemical bonds in length, between the two groups linked by the linking group. In certain embodiments the linking groups may comprise a long linear sequence of chemical bonds ranging from 30 to 500 chemical bonds in length between the two groups. In other embodiments the linking groups may comprise a long linear sequence of chemical bonds ranging from 50 to 500 chemical bonds in length between the two groups. As used with reference to the linking group, the chemical bonds in the linear sequence between the groups linked by the linking group may be covalent or polar covalent chemical bonds, such as covalent or polar covalent σ-bonds and may also include one or more π-bonds (although the π-bonds are not included when calculating the length of chemical bonds in the linear sequence). Further, it will be understood by those skilled in the art that the linking group also comprises those intervening atoms through which the linear sequence of bonds are associated.

As will be described in greater detail herein, it is believed that the one or more flexible linking group in the mesogen containing compounds disclosed herein impart certain desirable characteristics to the compound and compositions, such as cured compositions, formed therefrom. For example, while not wishing to be limited by any interpretation, it is believed that the one or more flexible linking group in the mesogen containing compound or residue thereof may result in cured compositions made therefrom having a “softer” structure. As used herein, with reference to the character of cured compositions, such as LCPs, layers, coatings, and coated articles made from the compounds, the term “softer” refers to compositions exhibiting a Fischer microhardness typically less than 150 Newtons/mm², e.g, from 0 to 149.9 Newtons/mm². Cured compositions having a softer structure may display desired or improved characteristics, for example, improved LC character, improved photochromic performance, and improved dichroic performance. For example, for cured compositions such as a polymer, a copolymer or blends of (co)polymers, it may be desirable to have hard and soft segments or components in the polymer. The concept that cured polymers may be composed of hard and soft segments or components is known in the art (see, for example, “Structure-Property-Relationship in Polyurethanes”, Polyurethane Handbook, G. Oertel, editor, 2nd ed. Hanser Publishers, 1994, pp 37-53). Typically the hard segment or component includes a crystalline or semi-crystalline region within the cured polymer structure, whereas the soft segment or component includes a more amorphous, non-crystalline or rubbery region. In certain embodiments, the contribution of the structure of a component or monomer residue in a polymer to either the hardness or softness of the resulting polymer may be determined, for example, by measuring the Fischer microhardness of the resulting cured polymer. The physical properties of the polymers are derived from their molecular structure and are determined by the choice of building blocks, e.g., the choice of monomer and other reactants, additives, the ratio of hard and soft segments, and the supramolecular structures caused by atomic interactions between polymer chains. Materials and methods for the preparation of polymers such as polyurethanes are described in Ullmann's Encyclopedia of Industrial Chemistry, 5th ed., 1992, Vol. A21, pages 665-716.

For example, in the photochromic and/or dichroic materials and cured layers and coatings described herein, it is believed that the soft segments or components of the polymeric material or cured layers and coatings may provide an improved solubilizing environment for the photochromic, photochromic-dichroic, and/or dichroic compound(s) to reversibly transform from a first state to a second state, while the hard segments or components of the polymeric material or coating provides structural integrity for the material or coating and/or prevent migration of the transformable compounds. In one application for photochromic and/or dichroic materials, a balance of soft and hard components in the polymer may achieve desired benefits of a suitable cured material or cured layer or coating, i.e., a material, layer, or coating having a Fischer microhardness ranging from 0 to 150 Newtons/mm² that also exhibits good photochromic and/or dichroic response characteristics. In another application, the photochromic and/or dichroic material may be located in a cured polymeric material having a Fischer microhardness less than 60 Newtons/mm², e.g. from 0 to 59.9 Newtons/mm², or alternatively from 5 to 25 N/mm², and coated with or contained within a harder polymeric material that provides structural strength. In a further application, the photochromic and/or dichroic material may already be within a soft polymeric material such as a soft polymeric shell that could be incorporated in a hard polymeric coating or material, e.g., a material having a Fischer microhardness greater than 150 Newtons/mm², e.g. 200 Newtons/mm² or even higher.

Other embodiments of the present disclosure provide for compositions, articles of manufacture, optical elements, LC compositions, LC cells, and the like, which comprise at least one mesogen containing compound or residue thereof represented by the structure of Formula I as described in detail herein.

According to certain embodiments, the present disclosure provides for a liquid crystal (LC) composition comprising a mesogen containing compound or residue thereof, as described herein.

The LC compositions may further comprise a liquid crystal polymer, including, for example a cured LCP. The liquid crystal polymer may comprise a residue of a first liquid crystal monomer, wherein the residue of the first LC monomer is the residue of the mesogen containing compound represented by the structure of Formula I as defined herein. In specific embodiments, the LCP may be a copolymer wherein the copolymer comprising the residue of the mesogen containing compound wherein the residue of the mesogen containing compound is incorporated into the copolymer, for example, as a co-monomer residue. That is, in certain embodiments, the residue of the mesogen containing compound may be incorporated into the main chain of the copolymer (i.e., the main chain of the residue is incorporated completely into the main chain of the copolymer) or in other embodiments, the residue of the mesogen containing compound may be incorporated into the copolymer as a side-chain off the main chain (for example, the residue may be bonded to the main chain by the reactive group P, with the remainder of the residue being a side-chain of the copolymer main chain). In various embodiments, where the residue of the mesogen containing compound, as represented by Formula I, is incorporated into the main chain of the copolymer, the group X may be represented by -(L)-Q, P is represented by the group Q, “w” is 1, and “z” is 1.

General synthetic methods have been developed to synthesize the scaffolds of the mesogen containing compounds represented by Formulae I-VIII. Exemplary embodiments of approaches to the Formulae structures are illustrated in the Figures. For example, referring to FIG. 1, a mesogen containing compound having a soft chain linker with a reactive group (hydroxyl or (meth)acrylate group) may be synthesized by either a Lewis acid catalyzed process or a base catalyzed process using excess caprolactone. The resulting mesogen containing compound corresponds to a structure represented by Formula II.

In another embodiment, a synthesis for a bi-mesogen containing compound having a structure corresponding to Formula V is set forth in FIGS. 2A and 2B. According to this representative synthesis, a structure having a reactive group P, wherein P is hydroxyl or (meth)acrylate may be readily synthesized from 6-chlorohexanol. Referring to FIGS. 3 and 4, bi-mesogen containing compounds having structures corresponding to Formula IV may be synthesized from starting hydroxy carboxylic acids that are either commercially available or readily prepared in the lab. According to these Figures, the bi-mesogen portion of the compound is incorporated in the latter portion of the synthetic route. FIG. 5 illustrates one approach to bond formation between free hydroxyl groups on the linker portion to a hydroxy substituted mesogen scaffold to form a structure according to Formula IV. This approach utilizes a Mitsunobu-type coupling process to form ether linkages in the mesogen containing structure.

Referring now to FIG. 6, a synthetic approach to a mesogen containing compound represented by the structure of Formula VI or VII. According to this synthetic approach, an acrylate substituted hydroxymesogen may be functionalized with a soft linker side chain using either Lewis acid catalysis or base catalysis (see, FIG. 1) and caprolactone. The resulting hydroxyl end group may correspond to group P or Q or may be further functionalized by conversion to a reactive ester functionality, for example, an acrylate or methacrylate ester. In another approach to soft linker chains illustrated in FIG. 7, a polycarbonate linker may be synthesized under Lewis acid catalysis using excess 1,3-dioxan-2-one. The resulting hydroxy terminated linker may then be further functionalized by conversion of a reactive ester functionality, for example, an acrylate or methacrylate ester.

FIG. 8 illustrates one approach to a mesogen containing compound having a structure represented by Formula III. According to this approach, a mesogen containing compound having a reactive functional group P on the mesogen side and a non-reactive group R on the soft linker group side is synthesized using a caprolactone based linker. Referring now to FIG. 9, one approach to the synthesis of a mesogen containing compound represented by Formula IV, wherein soft caprolactone derived linker groups are attached by a succinate diester.

Referring now to FIGS. 10 and 11, mesogen containing compounds having structures according to Formula VI may be synthesized with hydroxyl end groups protected as the tetrahydro-2H-pyranyl ethers. According to these synthetic strategies, the mesogen is incorporated into the structure as the final step in the synthesis. Referring to FIG. 12, a approach to mesogen containing compounds represented by Formula VI or VII, wherein the mesogen structure is flanked by two soft caprolactone based linkers with a reactive group P or Q are synthesized. According to FIG. 12, when the reactive group P or Q is hydroxyl, it may be further functionalized by esterification of the hydroxyl group with (meth)acryloyl chloride to form a reactive ester functionality. Referring to FIG. 13, a mesogen containing structure having multiple reactive groups P, as represented by Formula VIII is synthesized. According to this approach, a polyhydroxy compound is used to establish a branching point in the structure. It should be noted that the synthetic schemes presented in FIGS. 1-13 are presented for illustration purposes only and are not meant to imply any preferred approach to the synthesis of mesogen containing compounds represented by Formulae I-VIII. One having ordinary skill in the art of organic synthesis would recognize that numerous other synthetic approaches are possible based on the structure of the target mesogen containing compound. Such alternate synthetic approaches are within the scope of the present disclosure.

In specific embodiments, the polymer may be a block or non-block copolymer comprising the residue of the mesogen containing compound incorporated into the copolymer. For example, in certain embodiments, the polymer may be a block copolymer comprising the residue of the mesogen containing compound incorporated into the copolymer, for example as a residue incorporated into the main chain of the copolymer or as a side-chain off the main chain of the copolymer. In certain embodiments, the block copolymer may comprise hard blocks and soft blocks. According to these embodiments, the mesogen containing compound may be incorporated into the hard block, the soft block, or both the hard block and soft block. In other embodiments, the mesogen containing compound may be dissolved (but not incorporated) into one of the blocks of the block copolymer, such as, for example, the hard block or the soft block. In other embodiments, the polymer may be a non-block copolymer (i.e., a copolymer that does not have large blocks of specific monomer residues), such as a random copolymer, an alternating copolymer, periodic copolymers, and statistical copolymers. For example, one or both of the co-monomer residues of the copolymer may be the mesogen containing compound, as described herein. The present disclosure is also intended to cover copolymers of more than two different types of co-monomer residues.

According to particular embodiments, the cured LCP may be a “soft” or a “hard” polymer, as defined herein. For example, in certain embodiments of the LCP may have a Fischer microhardness of less than from 0 to 200 Newtons/mm². In other embodiments, the LCP may have an average number of at least 20 bonds between adjacent intra- or inter-strand cross-links on a polymer backbone. That is, in a linear sequence of bonds on a polymer backbone, there is at least a linear sequence of 20 bonds between one cross-link and the next adjacent cross-link. While not wishing to be limited by any interpretation, it is believed that when the intra- or inter-strand cross-links on the backbone of a polymer, such as a cured LCP described herein, are far apart, for example, at least 20 bonds, the resulting polymer strands are more flexible and the resulting polymer has “softer” characteristics. As described herein, a polymer with “soft” characteristics may be desirable in certain applications, such as ophthalmic applications, for example, photochromic applications.

In certain embodiments of the LC compositions of the present disclosure, the LC compositions may further comprise at least one of photochromic compound, a dichroic compound, a photochromic-dichroic compound, a photosensitive material, a non-photosensitive material, and one or more additives. According to these embodiments, the one or more additives may be a liquid crystal, a liquid crystal property control additive, a non-linear optical material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer, a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent, a free radical scavenger, a coupling agent, a tilt control additive, a block or non-block polymeric material, or an adhesion promoter. As used herein, the term “photochromic compounds” includes thermally reversible photochromic materials and non-thermally reversible photochromic materials, which are generally capable of converting from a first state, for example a “clear state,” to a second state, for example a “colored state,” in response to actinic radiation, and reverting back to the first state in response to thermal energy and actinic radiation, respectively. As used herein the term “photochromic” means having an absorption spectrum for at least visible radiation that varies in response to at least actinic radiation. As used herein “actinic radiation” means electromagnetic radiation, such as ultraviolet and visible radiation that is capable of causing a response. As used herein the term “dichroic” means capable of absorbing one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other. As used herein, the term “photosensitive material” includes materials that physically or chemically respond to electromagnetic radiation, such as, for example, phosphorescent materials or fluorescent materials. As used herein, the term “non-photosensitive materials” includes materials that do not respond to electromagnetic radiation, such as fixed tint dyes or thermochromic materials.

According to those embodiments wherein the LC compositions comprise at least one of a photochromic compound, a dichroic compound or a photochromic-dichroic compound, the photochromic compound may comprise a photochromic group chosen from a thermally or non-thermally reversible pyran, a thermally or non-thermally reversible oxazine, or a thermally or non-thermally reversible fulgide. Also included are inorganic photochromic materials. As used herein, the term “non-thermally reversible” means adapted to switch from a first state to a second state in response to actinic radiation, and to revert back to the first state in response to actinic radiation.

Examples of thermally reversible photochromic pyrans from which photochromic compound may be chosen and that may be used in conjunction with various embodiments disclosed herein include benzopyrans, naphthopyrans, e.g., naphtho[1,2-b]pyrans, naphtho[2,1-b]pyrans, indeno-fused naphthopyrans, such as those disclosed in U.S. Pat. No. 5,645,767 at col. 2, line 16 to col. 12, line 57; and heterocyclic-fused naphthopyrans, such as those disclosed in U.S. Pat. No. 5,723,072 at col. 2, line 27 to col. 15, line 55; U.S. Pat. No. 5,698,141 at col. 2, line 11 to col. 19, line 45; U.S. Pat. No. 6,153,126 at col. 2, line 26 to col. 8, line 60; and U.S. Pat. No. 6,022,497 a line 21 to col. 11, line 46; spiro-9-fluoreno[1,2-b]pyrans; phenanthropyrans; quinopyrans; fluoroanthenopyrans; spiropyrans, e.g., spiro(benzindoline)naphthopyrans, spiro(indoline)benzopyrans, spiro(indoline) naphthopyrans, spiro(indoline)quinopyrans and spiro(indoline)pyrans. More specific examples of naphthopyrans and the complementary organic photochromic substances are described in U.S. Pat. No. 5,658,501 at col. 1, line 64 to col. 13, line 17. Spiro(indoline)pyrans are also described in the text, Techniques in Chemistry, Volume III, “Photochromism”, Chapter 3, Glenn H. Brown, Editor, John Wiley and Sons, Inc., New York, 1971.

Examples of thermally reversible photochromic oxazines from which the photochromic compounds may be chosen and that may be used in conjunction with various embodiments disclosed herein include benzoxazines, naphthoxazines, and spiro-oxazines, e.g., spiro(indoline)naphthoxazines, spiro(indoline)pyridobenzoxazines, spiro(benzindoline) pyridobenzoxazines, spiro(benzindoline)naphthoxazines, spiro(indoline)benzoxazines, spiro(indoline)fluoranthenoxazine, and spiro(indoline)quinoxazine.

Examples of thermally reversible photochromic fulgides from which the photochromic compounds may be chosen and that may be used in conjunction with various embodiments disclosed herein include: fulgimides, and the 3-furyl and 3-thienyl fulgides and fulgimides, which are disclosed in U.S. Pat. No. 4,931,220 at column 2, line 51 to column 10, line 7, and mixtures of any of the aforementioned photochromic materials/compounds. Examples of non-thermally reversible photochromic compounds from which the photochromic compounds may be chosen and that may be used in conjunction with various embodiments disclosed herein include the photochromic compounds disclosed in US Patent Application Publication 2005/0004361 at paragraphs [0314] to [0317].

In certain embodiments, the photochromic compound may be an inorganic photochromic compound. Examples of suitable include crystallites of silver halide, cadmium halide and/or copper halide. Other examples of inorganic photochromic materials may be prepared by the addition of europium(II) and/or cerium(II) to a mineral glass, such as a soda-silica glass. According to one embodiment, the inorganic photochromic materials may be added to molten glass and formed into particles that are incorporated into the compositions of the present disclosure to form microparticles comprising such particulates. The glass particulates may be formed by any of a number of various methods known in the art. Suitable inorganic photochromic materials are further described in Kirk Othmer Encyclopedia of Chemical Technology, 4th ed., volume 6, pages 322-325.

Other embodiments of the compositions may comprise a photosensitive material, including luminescent dyes, such as a phosphorescent dye or a fluorescent dye. As known to those skilled in the art, after activation the phosphorescent dyes and fluorescent dyes emit visible radiation when an atom or molecule passes from a higher to a lower electronic state. One difference between the two dye types is that the emission of luminescence after exposure to radiation from the fluorescent dye occurs sooner than that from a phosphorescent dye.

Fluorescent dyes known to those skilled in the art may be used as photosensitive materials in various embodiments of the present disclosure. For a listing of various fluorescent dyes, see, Haugland, R. P. Molecular Probes Handbook for Fluorescent Probes and Research Chemicals, 6th ed., 1996. Examples of fluorescent dyes include anthracenes tetracenes, pentacenes, rhodamines, benzophenones, coumarins, fluoresceins, perylenes, and mixtures thereof.

Phosphorescent dyes known to those skilled in the art may be used as photosensitive materials in various embodiments of the present disclosure. Suitable examples of phosphorescent dyes include, metal-ligand complexes such as tris(2-phenylpyridine)iridium [Ir(ppy)₃] and 2,3,7,8,12,13,17,18-octaethyl-21H,23H-porphyrin platimum(II) [PtOEP]; and organic dyes such as eosin (2′,4′,5′,7′-tetrabromofluorescein), 2,2′-bipyridine and erthrosin (2′,4′,5′,7′-tetraiodofluorescein).

Examples of non-photosensitive materials suitable for use in the compositions of the present disclosure include fixed-tint dyes. Examples of suitable fixed-tint dyes may include nitrobenzene dyes, azo dyes, anthraquinone dyes, naphthoquinone dyes, benzoquinone dyes, phenothiazine dyes, indigoid dyes, xanthene dyes, pheanthridine dyes, phthalocyanin dyes and dyes derived from triarylmethane. These fixed-tint dyes may be used alone or as mixtures with other fixed-tint dyes or other chromophoric compounds (such as photochromic compounds).

Suitable examples of dyes used with suitable other chemicals to make thermochromic materials include substituted phenylmethanes and fluorans, such as 3,3′-dimethoxyfluoran (yellow); 3-chloro-6-phenylaminofluoran (orange); 3-diethylamino-6-methyl-7-chlorofluoran (vermilion); 3-diethyl-7,8-benzofluoran (pink); Crystal Violet lactone (blue); 3,3′,3″-tris(p-dimethylaminophenyl)phthalide (purplish blue); Malachite Green lactone (green); 3,3;-bis(pdimethylaminophenyl)phthalide (green); 3-diethylmaino-6-methyl-7-phenylaminofluoran (black), indolyl phthalides, spiropyrans, coumarins, fulgides, etc. Further, thermochromic materials may also include cholesteric liquid crystals and mixtures of cholesteric liquid crystals and nematic liquid crystals.

According to one specific, embodiment, the photochromic compound may comprise at least two photochromic groups, wherein the photochromic groups are linked to one another via linking group substituents on the individual photochromic groups. For example, the photochromic groups can be polymerizable photochromic groups or photochromic groups that are adapted to be compatible with a host material (“compatibilized photochromic group”). Examples of polymerizable photochromic groups which can be chosen and that are useful in conjunction with various embodiments disclosed herein are disclosed in U.S. Pat. No. 6,113,814 at column 2, line 24 to column 22, line 7. Examples of compatiblized photochromic groups which can be chosen and that are useful in conjunction with various embodiments disclosed herein are disclosed in U.S. Pat. No. 6,555,028 at column 2, line 40 to column 24, line 56.

Other suitable photochromic groups and complementary photochromic groups are described in U.S. Pat. No. 6,080,338 at column 2, line 21 to column 14, line 43; U.S. Pat. No. 6,136,968 at column 2, line 43 to column 20, line 67; U.S. Pat. No. 6,296,785 at column 2, line 47 to column 31, line 5; U.S. Pat. No. 6,348,604 at column 3, line 26 to column 17, line 15; U.S. Pat. No. 6,353,102 at column 1, line 62 to column 11, line 64; and U.S. Pat. No. 6,630,597 at column 2, line 16 to column 16, line 23.

As set forth above, in certain embodiments the photochromic compound may be a photochromic pyran. According to these embodiments, the photochromic compound may be represented by Formula IX:

With reference to Formula IX, A is a substituted or unsubstituted aromatic ring or a substituted or unsubstituted fused aromatic ring chosen from: naphtho, benzo, phenanthro, fluorantheno, antheno, quinolino, thieno, furo, indolo, indolino, indeno, benzofuro, benzothieno, thiopheno, indeno-fused naphtho, heterocyclic-fused naphtho, and heterocyclic-fused benzo. According to these embodiments, the possible substituents on the aromatic or fused aromatic ring are disclosed in U.S. Pat. Nos. 5,458,814; 5,466,398; 5,514,817; 5,573,712; 5,578,252; 5,637,262; 5,650,098; 5,651,923; 5,698,141; 5,723,072; 5,891,368; 6,022,495; 6,022,497; 6,106,744; 6,149,841; 6,248,264; 6,348,604; 6,736998; 7,094,368, 7,262,295 and 7,320,826. According to Formula IX, “i” may be the number of substituent(s) R′ attached to ring A, and may range from 0 to 10. Further, with reference to Formula IX, B and B′ may each independently represent a group chosen from:

-   -   a metallocenyl group (such as those described in U.S. Patent         Application Publication 2007/0278460 at paragraph [0008] to         [0036]);     -   an aryl group that is mono-substituted with a reactive         substituent or a compatiblizing substituent (such as those         discussed in U.S. Patent Application Publication 2007/0278460 at         paragraph [0037] to [0059]);     -   9-julolidinyl, an unsubstituted, mono-, di- or tri-substituted         aryl group chosen from phenyl and naphthyl, an unsubstituted,         mono- or di-substituted heteroaromatic group chosen from         pyridyl, furanyl, benzofuran-2-yl, benzofuran-3-yl, thienyl,         benzothien-2-yl, benzothien-3-yl, dibenzofuranyl,         dibenzothienyl, carbazoyl, benzopyridyl, indolinyl and         fluorenyl, wherein the aryl and heteroaromatic substituents are         each independently: hydroxy, aryl, mono- or         di-(C₁-C₁₂)alkoxyaryl, mono- or di-(C₁-C₁₂)alkylaryl, haloaryl,         C₃-C₇ cycloalkylaryl, C₃-C₇ cycloalkyl, C₃-C₇ cycloalkyloxy,         C₃-C₇ cycloalkyloxy(C₁-C₁₂)alkyl, C₃-C₇         cycloalkyloxy(C₁-C₁₂)alkoxy, aryl(C₁-C₁₂)alkyl,         aryl(C₁-C₁₂)alkoxy, aryloxy, aryloxy(C₁-C₁₂)alkyl,         aryloxy(C₁-C₁₂)alkoxy, mono- or         di-(C₁-C₁₂)alkylaryl(C₁-C₂)alkyl, mono- or         di-(C₁-C₁₂)alkoxyaryl(C₁-C₁₂)alkyl, mono- or         di-(C₁-C₁₂)alkylaryl(C₁-C₁₂)alkoxy, mono- or         di-(C₁-C₁₂)alkoxyaryl(C₁-C₁₂)alkoxy, amino, mono- or         di-(C₁-C₁₂)alkylamino, diarylamino, piperazino,         N—(C₁-C₁₂)alkylpiperazino, N-arylpiperazino, aziridino,         indolino, piperidino, morpholino, thiomorpholino,         tetrahydroquinolino, tetrahydroisoquinolino, pyrrolidino, C₁-C₁₂         alkyl, C₁-C₁₂ haloalkyl, C₁-C₁₂ alkoxy,         mono(C₁-C₁₂)alkoxy(C₁-C₁₂)alkyl, acryloxy, methacryloxy, halogen         or —C(═O)R¹, wherein R¹ represents a group, such as, —OR²,         —N(R³)R⁴, piperidino or morpholino, wherein R² represents a         group, such as, allyl, C₁-C₆ alkyl, phenyl, mono(C₁-C₆)alkyl         substituted phenyl, mono(C₁-C₆)alkoxy substituted phenyl,         phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkyl substituted         phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkoxy substituted         phenyl(C₁-C₃)alkyl, C₁-C₆ alkoxy(C₂-C₄)alkyl or C₁-C₆ haloalkyl,         and R³ and R⁴ each independently represents a group, such as,         C₁-C₆ alkyl, C₅-C₇ cycloalkyl or a substituted or an         unsubstituted phenyl, wherein said phenyl substituents are each         independently C₁-C₆ alkyl or C₁-C₆ alkoxy;

an unsubstituted or mono-substituted group chosen from pyrazolyl, imidazolyl, pyrazolinyl, imidazolinyl, pyrrolidino, phenothiazinyl, phenoxazinyl, phenazinyl and acridinyl, wherein said substituents are each independently C₁-C₁₂ alkyl, C₁-C₁₂ alkoxy, phenyl or halogen;

a 4-substituted phenyl, the substituent being a dicarboxylic acid residue or derivative thereof, a diamine residue or derivative thereof, an amino alcohol residue or derivative thereof, a polyol residue or derivative thereof, —(CH₂)—, —(CH₂)_(k)— or —[O—(CH₂)_(k)]_(q)—, wherein “k” represents an integer ranging from 2 to 6 and “q” represents an integer ranging from 1 to 50, and wherein the substituent is connected to an aryl group of another photochromic material; a group represented by:

wherein W represents a group, such as, —CH₂— or oxygen; Y represents a group, such as, oxygen or substituted nitrogen, provided that when Y represents substituted nitrogen, W represents —CH₂—, the substituted nitrogen substituents being hydrogen, C₁-C₁₂ alkyl or C₁-C₁₂ acyl; each R⁵ independently represents a group, such as, C₁-C₁₂ alkyl, C₁-C₁₂ alkoxy, hydroxy or halogen; R⁶ and R⁷ each independently represent a group, such as, hydrogen or C₁-C₁₂ alkyl; and “j” represents an integer ranging from 0 to 2; or

a group represented by:

wherein R⁸ represents a group, such as, hydrogen or C₁-C₁₂ alkyl, and R⁹ represents a group, such as, an unsubstituted, mono- or di-substituted naphthyl, phenyl, furanyl or thienyl, wherein said naphthyl, phenyl, furanyl and thienyl substituents are each independently C₁-C₁₂ alkyl, C₁-C₁₂ alkoxy or halogen. Alternatively, B and B′ may represent groups that together form a fluoren-9-ylidene or mono- or di-substituted fluoren-9-ylidene, each of said fluoren-9-ylidene substituents independently being C₁-C₁₂ alkyl, C₁-C₁₂ alkoxy or halogen.

Further, with reference to Formula IX, R′ may be a substituent on a ring in Formula IX, wherein if R′ is a substituent on an sp³ hybridized carbon, each R′ may be independently selected from: a metallocenyl group; a reactive substituent or a compatiblizing substituent; perhalo(C₁-C₁₀)alkyl, a perhalo(C₂-C₁₀)alkenyl, a perhalo(C₃-C₁₀)alkynyl, a perhalo(C₁-C₁₀)alkoxy or a perhalo(C₃-C₁₀)cycloalkyl; a group represented by —O(CH₂)_(a)(CJ₂)_(b)CK₃, wherein K is a halogen, J is hydrogen or halogen, “a” is an integer ranging from 1 to 10, and “b” is an integer ranging from 1 to 10; a silicon-containing group represented by one of

wherein R¹⁰, R¹¹, and R¹² are each independently C₁-C₁₀ alkyl, C₁-C₁₀ alkoxy or phenyl; hydrogen, hydroxy, C₁-C₆ alkyl, chloro, fluoro, C₃-C₇ cycloalkyl, allyl or C₁-C₈ haloalkyl; morpholino, piperidino, pyrrolidino, an unsubstituted, mono- or di-substituted amino, wherein said amino substituents are each independently C₁-C₆ alkyl, phenyl, benzyl or naphthyl; an unsubstituted, mono-, di- or tri-substituted aryl group chosen from phenyl, naphthyl, benzyl, phenanthryl, pyrenyl, quinolyl, isoquinolyl, benzofuranyl, thienyl, benzothienyl, dibenzofuranyl, dibenzothienyl, carbazolyl or indolyl, wherein the aryl group substituents are each independently halogen, C₁-C₆ alkyl or C₁-C₆ alkoxy; —C(═O)R¹³, wherein R¹³ is hydrogen, hydroxy, C₁-C₆ alkyl, C₁-C₆ alkoxy, amino, mono- or di-(C₁-C₆)alkylamino, morpholino, piperidino, pyrrolidino, an unsubstituted, mono- or di-substituted phenyl or naphthyl, an unsubstituted, mono- or di-substituted phenoxy, an unsubstituted, mono- or di-substituted phenylamino, wherein said phenyl, naphthyl, phenoxy, and phenylamino substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; —OR¹⁴, wherein R¹⁴ is C₁-C₆ alkyl, phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkyl substituted phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkoxy substituted phenyl(C₁-C₃)alkyl, C₁-C₆ alkoxy(C₂-C₄)alkyl, C₃-C₇ cycloalkyl, mono(C₁-C₄)alkyl substituted C₃-C₇ cycloalkyl, C₁-C₈ chloroalkyl, C₁-C₈ fluoroalkyl, allyl or C₁-C₆ acyl, —CH(R¹⁵)R¹⁶, wherein R¹⁵ is hydrogen or C₁-C₃ alkyl, and R¹⁶ is —CN, —CF₃ or —COOR¹⁷, wherein R¹⁷ is hydrogen or C₁-C₃ alkyl, or —C(═O)R¹⁸, wherein R¹⁸ is hydrogen, C₁-C₆ alkyl, C₁-C₆ alkoxy, amino, mono- or di-(C₁-C₆)alkylamino, an unsubstituted, mono- or di-substituted phenyl or naphthyl, an unsubstituted, mono- or di-substituted phenoxy or an unsubstituted, mono- or di-substituted phenylamino, wherein said phenyl, naphthyl, phenoxy and phenylamino substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; a 4-substituted phenyl, the substituent being a dicarboxylic acid residue or derivative thereof, a diamine residue or derivative thereof, an amino alcohol residue or derivative thereof, a polyol residue or derivative thereof, —(CH₂)—, —(CH₂)_(k)— or —[O—(CH₂)_(k)]_(q)—, wherein “k” is an integer ranging from 2 to 6 and “q” is an integer ranging from 1 to 50, and wherein the substituent is connected to an aryl group on another photochromic material; —CH(R¹⁹)₂, wherein R¹⁹ is —CN or —COOR²⁰, wherein R²⁰ is hydrogen, C₁-C₆ alkyl, C₃-C₇ cycloalkyl, phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkyl substituted phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkoxy substituted phenyl(C₁-C₃)alkyl or an unsubstituted, mono- or di-substituted phenyl or naphthyl, wherein said phenyl and naphthyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; —CH(R²¹)R²², wherein R²¹ is hydrogen, C₁-C₆ alkyl or an unsubstituted, mono- or di-substituted phenyl or naphthyl, wherein said phenyl and naphthyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy, and R²² is —C(═O)OR²³, —C(═O)R²⁴ or —CH₂OR²⁵, wherein R²³ is hydrogen, C₁-C₆ alkyl, C₃-C₇ cycloalkyl, phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkyl substituted phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkoxy substituted phenyl(C₁-C₃)alkyl or an unsubstituted, mono- or di-substituted phenyl or naphthyl, wherein said phenyl and naphthyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy, R²⁴ is hydrogen, C₁-C₆ alkyl, amino, mono(C₁-C₆)alkylamino, di(C₁-C₆) alkylamino, phenylamino, diphenylamino, (mono- or di-(C₁-C₆)alkyl substituted phenyl)amino, (mono- or di-(C₁-C₆)alkoxy substituted phenyl)amino, di(mono- or di-(C₁-C₆)alkyl substituted phenyl)amino, di(mono- or di-(C₁-C₆)alkoxy substituted phenyl)amino, morpholino, piperidino or an unsubstituted, mono- or di-substituted phenyl or naphthyl, wherein said phenyl or naphthyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy, and R²⁵ is hydrogen, —C(═O)R²³, C₁-C₆ alkyl, C₁-C₃ alkoxy (C₁-C₆)alkyl, phenyl(C₁-C₆)alkyl, mono-alkoxy substituted phenyl(C₁-C₆)alkyl or an unsubstituted, mono- or di-substituted phenyl or naphthyl, wherein said phenyl or naphthyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; or two R′ groups on the same atom together form an oxo group, a spiro-carbocyclic group containing 3 to 6 carbon atoms or a spiro-heterocyclic group containing 1 to 2 oxygen atoms and 3 to 6 carbon atoms including the spirocarbon atom, said spiro-carbocyclic and spiro-heterocyclic groups being annellated with 0, 1 or 2 benzene rings; or

when R′ is a substituent on an sp² hybridized carbon, each R′ may be independently: hydrogen; C₁-C₆ alkyl; chloro; fluoro; bromo; C₃-C₇ cycloalkyl; an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; —OR²⁶ or —OC(═O)R²⁶ wherein R²⁶ is hydrogen, amine, alkylene glycol, polyalkylene glycol, C₁-C₆ alkyl, phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkyl substituted phenyl(C₁-C₃)alkyl, mono(C₁-C₆)alkoxy substituted phenyl(C₁-C₃)alkyl, (C₁-C₆)alkoxy(C₂-C₄)alkyl, C₃-C₇ cycloalkyl, mono(C₁-C₄)alkyl substituted C₃-C₇ cycloalkyl or an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; a reactive substituent or a compatiblizing substituent; a 4-substituted phenyl, said phenyl substituent being a dicarboxylic acid residue or derivative thereof, a diamine residue or derivative thereof, an amino alcohol residue or derivative thereof, a polyol residue or derivative thereof, —(CH₂)—, —(CH₂)_(k)— or —[O—(CH₂)_(k)]_(q)—, wherein “k” is an integer ranging from 2 to 6, and “q” is an integer ranging from 1 to 50, and wherein the substituent is connected to an aryl group on another photochromic material; —N(R²⁷)R²⁸, wherein R²⁷ and R²⁸ are each independently hydrogen, C₁-C₈ alkyl, phenyl, naphthyl, furanyl, benzofuran-2-yl, benzofuran-3-yl, thienyl, benzothien-2-yl, benzothien-3-yl, dibenzofuranyl, dibenzothienyl, benzopyridyl, fluorenyl, C₁-C₈ alkylaryl, C₃-C₈ cycloalkyl, C₄-C₁₆ bicycloalkyl, C₅-C₂₀ tricycloalkyl or C₁-C₂₀ alkoxy(C₁-C₆)alkyl, or R²⁷ and R²⁸ come together with the nitrogen atom to form a C₃-C₂₀ hetero-bicycloalkyl ring or a C₄-C₂₀ hetero-tricycloalkyl ring; a nitrogen containing ring represented by:

wherein each —V— is independently chosen for each occurrence from —CH₂—, —CH(R²⁹)—, —C(R²⁹)₂—, —CH(aryl)—, —C(aryl)₂- and —C(R²⁹)(aryl)-, wherein each R²⁹ is independently C₁-C₆ alkyl and each aryl is independently phenyl or naphthyl; —U— is —V—, —O—, —S—, —S(O)—, —SO₂—, —NH—, —N(R²⁹)— or —N(aryl)-; “s” is an integer ranging from 1 to 3; and “r” is an integer ranging from 0 to 3, provided that if” “r is 0 then —U— is the same as —V—; a group represented by:

wherein each R³⁰ is independently C₁-C₆ alkyl, C₁-C₆ alkoxy, fluoro or chloro; R³¹, R³² and R³³ are each independently hydrogen, C₁-C₆ alkyl, phenyl or naphthyl, or R³¹ and R³² together form a ring of 5 to 8 carbon atoms; and “p” is an integer ranging from 0 to 3; or a substituted or an unsubstituted C₄-C₁₈ spirobicyclic amine or a substituted or an unsubstituted C₄-C₁₈ spirotricyclic amine, wherein said substituents are each independently aryl, C₁-C₆ alkyl, C₁-C₆ alkoxy or phenyl(C₁-C₆)alkyl;

or R′ may be a metallocenyl group; perfluoroalkyl or perfluoroalkoxy; —C(═O)R³⁴ or —SO₂R³⁴, wherein each R³⁴ is independently hydrogen, C₁-C₆ alkyl, —OR³⁵ or —NR³R³⁷, wherein R³⁵, R³⁶ and R³⁷ are each independently hydrogen, C₁-C₆ alkyl, C₅-C₇ cycloalkyl, alkylene glycol, polyalkylene glycol or an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; —C(═C(R³⁸)₂)R³⁹, wherein each R³⁸ is independently —C(═O)R³⁴, —OR³⁵, —OC(═O)R³⁵, —NR³⁶R³⁷, hydrogen, halogen, cyano, C₁-C₆ alkyl, C₅-C₇ cycloalkyl, alkylene glycol, polyalkylene glycol or an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy, and R³⁹ is hydrogen, C₁-C₆ alkyl, C₅-C₇ cycloalkyl, alkylene glycol, polyalkylene glycol or an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; or —C≡CR⁴⁰ or —CEN wherein R⁴⁰ is —C(═O)R³⁴, hydrogen, C₁-C₆ alkyl, C₅-C₇ cycloalkyl or an unsubstituted, mono- or di-substituted phenyl, wherein said phenyl substituents are each independently C₁-C₆ alkyl or C₁-C₆ alkoxy; or a least one pair of adjacent R′ groups together form a group represented by:

wherein D and D′ are each independently oxygen or the group —NR²⁷—; or two R′ groups on adjacent atoms come together form an aromatic or heteroaromatic fused group, said fused group being benzo, indeno, dihydronaphthalene, indole, benzofuran, benzopyran or thianaphthene.

In other embodiments, the LC compositions of the present disclosure may comprise a dichroic compound. Suitable dichroic compounds are described in detail in U.S. Pat. No. 7,097,303 at column 7, lines 6 to 60. Other examples of suitable conventional dichroic compounds include azomethines, indigoids, thioindigoids, merocyanines, indans, quinophthalonic dyes, perylenes, phthaloperines, triphenodioxazines, indoloquinoxalines, imidazo-triazines, tetrazines, azo and (poly)azo dyes, benzoquinones, naphthoquinones, anthroquinone and (poly)anthroquinones, anthropyrimidinones, iodine and iodates. In another embodiment, the dichroic material can be a polymerizable dichroic compound. That is, according to this embodiment, the dichroic material can comprise at least one group that is capable of being polymerized (i.e., a “polymerizable group” or “reactive group”). For example, in one embodiment the at least one dichroic compound can have at least one alkoxy, polyalkoxy, alkyl, or polyalkyl substituent terminated with at least one polymerizable group. As used herein the term “dichroic” means capable absorbing one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other. As used herein, the terms “linearly polarize” or “linearly polarization” mean to confine the vibrations of the electric vector of light waves to one direction. Accordingly, dichroic dyes are capable of absorbing one of two orthogonal plane polarized components of transmitted radiation more strongly than the other, thereby resulting in linear polarization of the transmitted radiation. However, while dichroic dyes are capable of preferentially absorbing one of two orthogonal plane polarized components of transmitted radiation, if the molecules of the dichroic dye are not aligned, no net linear polarization of transmitted radiation will be achieved. That is, due to the random positioning of the molecules of the dichroic dye, selective absorption by the individual molecules can cancel each other such that no net or overall linear polarizing effect is achieved. Thus, it is generally necessary to align the molecules of the dichroic dye in order to achieve a net linear polarization. An alignment facility such as described in U.S. Patent Application Publication 2005/0003107 at paragraphs [0008] to [0126], may be used to facilitate the positioning of an optically anisotropic dye, such as a dichroic dye, thereby achieving a desired optical property or effect.

Still other embodiments of the LC compositions herein may comprise a photochromic-dichroic compound. As used herein the term “photochromic-dichroic” means displaying both photochromic and dichroic (i.e., linearly polarizing) properties under certain conditions, which properties are at least detectible by instrumentation. Accordingly, “photochromic-dichroic compounds” are compounds displaying both photochromic and dichroic (i.e., linearly polarizing) properties under certain conditions, which properties are at least detectible by instrumentation. Thus, photochromic-dichroic compounds have an absorption spectrum for at least visible radiation that varies in response to at least actinic radiation and are capable of absorbing one of two orthogonal plane polarized components of at least transmitted radiation more strongly than the other. Additionally, as with conventional photochromic compounds discussed above, the photochromic-dichroic compounds disclosed herein can be thermally reversible. That is, the photochromic-dichroic compounds can switch from a first state to a second state in response to actinic radiation and revert back to the first state in response to thermal energy.

Further, according to various embodiments disclosed herein, the mesogen containing material can be adapted to allow the at least one photochromic compound, dichroic compound, or photochromic-dichroic compound to switch from a first state to the second state at a desired rate. Generally speaking conventional photochromic/dichroic compounds can undergo a transformation from one isomeric form to another in response to actinic radiation, with each isomeric form having a characteristic absorption spectrum and/or polarization characteristic. The photochromic compound, dichroic compound, or photochromic-dichroic compounds according to various embodiments disclosed herein undergo a similar isomeric transformation. The rate or speed at which this isomeric transformation (and the reverse transformation) occurs depends, in part, upon the properties of the cured layer comprising the mesogen containing compound surrounding the photochromic compound, dichroic compound, or photochromic-dichroic compound (that is, the “host”). It is believed by the inventors the rate of transformation of the photochromic/dichroic compound(s) will depend, in part, upon the flexibility of the chain segments of the host, that is, the mobility or viscosity of the chain segments of the host. In particular it is believed that the rate of transformation of the photochromic compound, dichroic compound, or photochromic-dichroic compound will generally be faster in hosts having flexible chain segments than in hosts having stiff or rigid chain segments. Therefore, according to certain embodiments disclosed herein, wherein the at least partial layer comprising a composition comprising the mesogen containing compound is a host, the composition can be adapted to allow the photochromic compound, dichroic compound, or photochromic-dichroic compound to transform between various isomeric states at desired rates. For example, the composition can be adapted by adjusting one or more of the molecular weight and the cross-link density of the mesogen containing compound or residue thereof.

For example, according to various embodiments disclosed herein, the at least one photochromic-dichroic compound can have a first state having a first absorption spectrum, a second state having a second absorption spectrum that is different from the first absorption spectrum, and can be adapted to switch from the first state to the second state in response to at least actinic radiation and to revert back to the first state in response to thermal energy. Further, the photochromic-dichroic compound can be dichroic (i.e., linearly polarizing) in one or both of the first state and the second state. For example, although not required, the photochromic-dichroic compound can be linearly polarizing in an activated state and non-polarizing in the bleached or faded (i.e., not activated) state. As used herein, the term “activated state” refers to the photochromic-dichroic compound when exposed to sufficient actinic radiation to cause the at least a portion of the photochromic-dichroic compound to switch from a first state to a second state. Further, although not required, the photochromic-dichroic compound can be dichroic in both the first and second states. For example, the photochromic-dichroic compound can linearly polarize visible radiation in both the activated state and the bleached state. Further, the photochromic-dichroic compound can linearly polarize visible radiation in an activated state, and can linearly polarize UV radiation in the bleached state. Examples of suitable photochromic-dichroic compounds that may be included in the LC compositions described herein include those disclosed in U.S. Patent Application Publication 2005/0012998 at paragraphs [0089] to [0339]. In addition, a general structure for certain photochromic dichroic compounds is presented in U.S. Pat. No. 7,342,112 at column 5, line 35 to column 31, line 3 and Table V spanning columns 97-102.

For example, it is contemplated that the photochromic compounds and/or photochromic-dichroic compounds disclosed herein can be used alone or in conjunction with another conventional organic photochromic compound (as discussed above), in amounts or ratios such that the LC compositions into which the photochromic or photochromic-dichroic compounds are incorporated, or onto which the LC compositions are applied (for example, the substrate), can exhibit a desired color or colors, either in an activated or a “bleached” state. Thus the amount of the photochromic or photochromic-dichroic compounds used is not critical provided that a sufficient amount is present to produce a desired photochromic effect. As used herein, the term “photochromic amount” refers to the amount of the photochromic or photochromic-dichroic compound necessary to produce the desired photochromic effect.

The LC compositions and other articles according to various embodiments disclosed herein can comprise any amount of the photochromic compound, dichroic compound and/or photochromic-dichroic necessary to achieve the desired optical properties, such as photochromic properties and dichroic properties.

According to specific embodiments of the LC compositions, the compositions may further comprise an additive selected from a liquid crystal, a liquid crystal property control agent, a non-linear optical material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer (such as ultraviolet light absorbers and light stabilizers such as hindered amine light stabilizers (HALS)), a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent (such as a surfactant), a free radical scavenger, or an adhesion promoter (such as hexane diol diacrylate and coupling agents).

Liquid crystal materials used herein may be chosen from liquid crystal polymers, liquid crystal pre-polymers, and liquid crystal monomers. As used herein the term “pre-polymer” means partially polymerized materials.

Liquid crystal monomers that are suitable for use in conjunction with various embodiments disclosed herein include mono-functional as well as multi-functional liquid crystal monomers. Further, according to various embodiments disclosed herein, the liquid crystal monomer can be a cross-linkable liquid crystal monomer, and can further be a photocross-linkable liquid crystal monomer. As used herein the term “photocross-linkable” means a material, such as a monomer, a pre-polymer or a polymer, that can be cross-linked on exposure to actinic radiation.

Examples of cross-linkable liquid crystal monomers suitable for use according to various embodiments disclosed herein include liquid crystal monomers having functional groups chosen from acrylates, methacrylates, allyl, allyl ethers, alkynes, amino, anhydrides, epoxides, hydroxides, isocyanates, blocked isocyanates, siloxanes, thiocyanates, thiols, urea, vinyl, vinyl ethers and blends thereof. Examples of photocross-linkable liquid crystal monomers suitable for use according to various embodiments disclosed herein include liquid crystal monomers having functional groups chosen from acrylates, methacrylates, alkynes, epoxides, thiols, and blends thereof. Other suitable cross-linking functional groups will be known to those with ordinary skill in the art.

Liquid crystal polymers and pre-polymers that are suitable for use in conjunction with various embodiments disclosed herein include thermotropic liquid crystal polymers and pre-polymers, and lyotropic liquid crystal polymers and pre-polymers. Further, the liquid crystal polymers and pre-polymers can be main-chain polymers and pre-polymers or side-chain polymers and pre-polymers. Additionally, according to various embodiments disclosed herein, the liquid crystal polymer or pre-polymer can be cross-linkable, and further can be photocross-linkable.

Examples of suitable liquid crystal polymers and pre-polymers that are suitable for use according to various embodiments disclosed herein include main-chain and side-chain polymers and pre-polymers having functional groups chosen from acrylates, methacrylates, allyl, allyl ethers, alkynes, amino, anhydrides, epoxides, hydroxides, isocyanates, blocked isocyanates, siloxanes, thiocyanates, thiols, urea, vinyl, vinyl ethers, and blends thereof. Examples of photocross-linkable liquid crystal polymers and pre-polymers that are suitable for use according to various embodiments disclosed herein include those polymers and pre-polymers having functional groups chosen from acrylates, methacrylates, alkynes, epoxides, thiols, and blends thereof.

In certain embodiments, one or more surfactants may be used. Surfactants include materials otherwise known as wetting agents, anti-foaming agents, emulsifiers, dispersing agents, leveling agents etc. Surfactants can be anionic, cationic and nonionic, and many surfactants of each type are available commercially. Examples of nonionic surfactants that may be used include ethoxylated alkyl phenols, such as the IGEPAL® DM surfactants or octyl-phenoxypolyethoxyethanol sold as TRITON® X-100, an acetylenic diol such as 2,4,7,9-tetramethyl-5-decyne-4,7-diol sold as SURFYNOL® 104, ethoxylated acetylenic diols, such as the SURFYNOL®400 surfactant series, fluoro-surfactants, such as the FLUORAD® fluorochemical surfactant series, and capped nonionics such as the benzyl capped octyl phenol ethoxylates sold as TRITON® CF87, the propylene oxide capped alkyl ethoxylates, which are available as the PLURAFAC® RA series of surfactants, octylphenoxyhexadecylethoxy benzyl ether, polyether modified dimethylpolysiloxane copolymer in solvent sold as BYK®-306 additive by Byk Chemie and mixtures of such recited surfactants.

Embodiments of non-linear optical (NLO) materials may include substantially any organic material that exhibits non-linear optical properties and forms crystals, which are currently available or may be synthesized in the future. Examples include the following organic compounds: N-(4-nitrophenyl)-(L)-prolinol (NPP); 4-N,N-dimethylamino-4′-N′-methyl-stilbazolium tosylate (DAST); 2-methyl-4-nitroaniline (MNA); 2-amino-5-nitropyridine (2A5NP); p-chlorophenylurea (PCPU); and 4-(N,N-dimethylamino)-3-acetamidonitrobenzene (DAN). Further examples of suitable NLO materials are disclosed in U.S. Pat. No. 6,941,051 at column 4, lines 4-37.

Examples of thermal stabilizers may include a basic nitrogen-containing compound for example, biurea, allantoin or a metal salt thereof, a carboxylic acid hydrazide, e.g., an aliphatic or aromatic carboxylic acid hydrazide, a metal salt of an organic carboxylic acid, an alkali or alkaline earth metal compound, a hydrotalcite, a zeolite and an acidic compound (e.g., a boric acid compound, a nitrogen-containing cyclic compound having a hydroxyl group, a carboxyl group-containing compound, a (poly)phenol, butylated hydroxytoluene, and an aminocarboxylic acid) or mixtures thereof.

Examples of mold release agents include esters of long-chain aliphatic acids and alcohols such as pentaerythritol, guerbet alcohols, long-chain ketones, siloxanes, alpha.-olefin polymers, long-chain alkanes and hydrocarbons having 15 to 600 carbon atoms.

Rheology control agents are thickeners that are typically powders that may be inorganic, such as silica, organic such as microcrystalline cellulose or particulate polymeric materials. Gelators or gelling agents are often organic materials that can also affect the thixotropy of the material in which they are added. Examples of suitable gelators or gelling agents include natural gums, starches, pectins, agar-agar, and gelatins. Gelators or gelling agents may often be based on polysaccharides or proteins.

Free radical scavengers include synthetic pseudopeptides resistant to hydrolysis such as Carcinine hydrochloride; lipoamino acids such as L-lysine lauroylmethionine; plant extracts containing multi-enzymes; natural tocopherol and related compounds as well as compounds containing an active hydrogen such as —OH, —SH, or —NRH group. Further examples of free radical scavengers are chosen from the group of sterically hindered amines (HALS=hindered amine light stabilizer) which, unlike customary light protection agents, are not based on the absorption of the irradiated light or on the quenching of the absorbed light, but essentially on the ability to scavenge or to replace free radicals and hydroperoxides formed during the photodegradation of polymeric materials and antioxidants.

Adhesion promoters include adhesion promoting organo-silane materials, such as aminoorganosilane materials, silane coupling agents, organic titanate coupling agents and organic zirconate coupling agents described in U.S. Patent Application Publication 2004/0207809 at paragraphs [0033] to [0042]. Further examples of adhesion promoters include zirco-aluminate adhesion promoting compounds that are commercially available from Rhone-Poulenc. Preparation of aluminum-zirconium complexes is described in the U.S. Pat. Nos. 4,539,048 and 4,539,049. These patents describe zirco-aluminate complex reaction products corresponding to the empirical formula:

(Al₂(ORO)_(a)A_(b)B_(c))_(X)(OC(R₂)O)_(Y)(ZrA_(d)B_(e))_(Z) wherein X, Y, and Z are at least 1, R₂ is an alkyl, alkenyl, aminoalkyl, carboxyalkyl, mercaptoalkyl, or epoxyalkyl group, having from 2 to 17 carbon atoms, and the ratio of X:Z is from about 2:1 to about 5:1. Additional zirco-aluminate complexes are described in U.S. Pat. No. 4,650,526.

Examples of dyes that can be present in the at least partial coating according to various embodiments disclosed herein include organic dyes that are capable of imparting a desired color or other optical property to the at least partial coating.

As used herein, the term “alignment promoter” means an additive that can facilitate at least one of the rate and uniformity of the alignment of a material to which it is added. Examples of alignment promoters that can be present in the at least partial coatings according to various embodiments disclosed herein include those described in U.S. Pat. No. 6,338,808 and U.S. Patent Publication No. 2002/0039627.

Examples of kinetic enhancing additives that can be present in the at least partial coating according to various embodiments disclosed herein include epoxy-containing compounds, organic polyols, and/or plasticizers. More specific examples of such kinetic enhancing additives are disclosed in U.S. Pat. No. 6,433,043 and U.S. Patent Publication No. 2003/0045612.

Examples of photoinitiators that can be present in the at least partial coating according to various embodiments disclosed herein include cleavage-type photoinitiators and abstraction-type photoinitiators. Examples of cleavage-type photoinitiators include acetophenones, α-aminoalkylphenones, benzoin ethers, benzoyl oximes, acylphosphine oxides and bisacylphosphine oxides or mixtures of such initiators. A commercial example of such a photoinitiator is DAROCURE® 4265, which is available from Ciba Chemicals, Inc. Examples of abstraction-type photoinitiators include benzophenone, Michler's ketone, thioxanthone, anthraquinone, camphorquinone, fluorone, ketocoumarin or mixtures of such initiators.

Another Example of a photoinitiator that can be present in the LC compositions according to various embodiments disclosed herein is a visible light photoinitiator. Examples of suitable visible light photoinitiators are set forth at column 12, line 11 to column 13, line 21 of U.S. Pat. No. 6,602,603.

Examples of thermal initiators include organic peroxy compounds and azobis(organonitrile) compounds. Specific examples of organic peroxy compounds that are useful as thermal initiators include peroxymonocarbonate esters, such as tertiarybutylperoxy isopropyl carbonate; peroxydicarbonate esters, such as di(2-ethylhexyl)peroxydicarbonate, di(secondary butyl)peroxydicarbonate and diisopropylperoxydicarbonate; diacyperoxides, such as 2,4-dichlorobenzoyl peroxide, isobutyryl peroxide, decanoyl peroxide, lauroyl peroxide, propionyl peroxide, acetyl peroxide, benzoyl peroxide and p-chlorobenzoyl peroxide; peroxyesters such as t-butylperoxy pivalate, t-butylperoxy octylate and t-butylperoxyisobutyrate; methylethylketone peroxide, and acetylcyclohexane sulfonyl peroxide. In one embodiment the thermal initiators used are those that do not discolor the resulting polymerizate. Examples of azobis(organonitrile) compounds that can be used as thermal initiators include azobis(isobutyronitrile), azobis(2,4-dimethylvaleronitrile) or a mixture thereof.

Examples of polymerization inhibitors include: nitrobenzene, 1,3,5,-trinitrobenzene, p-benzoquinone, chloranil, DPPH, FeCl₃, CuCl₂, oxygen, sulfur, aniline, phenol, p-dihydroxybenzene, 1,2,3-trihydroxybenzene, and 2,4,6-trimethylphenol.

Examples of solvents that can be present in the LC compositions according to various embodiments disclosed herein include those that will dissolve solid components of the LC compositions, that are compatible with the LC compositions and the elements and substrates, and/or can ensure uniform coverage of a surface(s) to which the LC composition is applied. Potential solvents include the following: propylene glycol monomethyl ether acetate and their derivates (sold as DOWANOL® industrial solvents), acetone, amyl propionate, anisole, benzene, butyl acetate, cyclohexane, dialkyl ethers of ethylene glycol, e.g., diethylene glycol dimethyl ether and their derivates (sold as CELLOSOLVEO industrial solvents), diethylene glycol dibenzoate, dimethyl sulfoxide, dimethyl formamide, dimethoxybenzene, ethyl acetate, isopropyl alcohol, methyl cyclohexanone, cyclopentanone, methyl ethyl ketone, methyl isobutyl ketone, methyl propionate, propylene carbonate, tetrahydrofuran, toluene, xylene, 2-methoxyethyl ether, 3-propylene glycol methyl ether, and mixtures thereof.

In certain embodiments, the LC compositions of the present disclosure may further comprise at least one additional polymeric material. Suitable examples of additional polymeric materials that may be used in conjunction with various embodiments disclosed herein include, for example, homopolymers and copolymers, prepared from the monomers and mixtures of monomers disclosed in U.S. Pat. No. 5,962,617 and in U.S. Pat. No. 5,658,501 from column 15, line 28 to column 16, line 17. For example, such polymeric materials can be thermoplastic or thermoset polymeric materials, can be transparent or optically clear, and can have any refractive index required. Examples of such disclosed monomers and polymers include: polyol(allyl carbonate) monomers, e.g., allyl diglycol carbonates such as diethylene glycol bis(allyl carbonate), which monomer is sold under the trademark CR-39 by PPG Industries, Inc.; polyurea-polyurethane (polyurea-urethane) polymers, which are prepared, for example, by the reaction of a polyurethane prepolymer and a diamine curing agent, a composition for one such polymer being sold under the trademark TRIVEX by PPG Industries, Inc.; polyol(meth)acryloyl terminated carbonate monomer; diethylene glycol dimethacrylate monomers; ethoxylated phenol methacrylate monomers; diisopropenyl benzene monomers; ethoxylated trimethylol propane triacrylate monomers; ethylene glycol bismethacrylate monomers; poly(ethylene glycol) bismethacrylate monomers; urethane acrylate monomers; poly(ethoxylated bisphenol A dimethacrylate); poly(vinyl acetate); poly(vinyl alcohol); poly(vinyl chloride); poly(vinylidene chloride); polyethylene; polypropylene; polyurethanes; polythiourethanes; thermoplastic polycarbonates, such as the carbonate-linked resin derived from bisphenol A and phosgene, one such material being sold under the trademark LEXAN; polyesters, such as the material sold under the trademark MYLAR; poly(ethylene terephthalate); polyvinyl butyral; poly(methyl methacrylate), such as the material sold under the trademark PLEXIGLAS, and polymers prepared by reacting polyfunctional isocyanates with polythiols or polyepisulfide monomers, either homopolymerized or co- and/or terpolymerized with polythiols, polyisocyanates, polyisothiocyanates and optionally ethylenically unsaturated monomers or halogenated aromatic-containing vinyl monomers. Also contemplated are copolymers of such monomers and blends of the described polymers and copolymers with other polymers, for example, to form block copolymers or interpenetrating network products.

According to one specific embodiment, the additional polymeric material is chosen from polyacrylates, polymethacrylates, poly(C₁-C₁₂) alkyl methacrylates, polyoxy(alkylene methacrylates), poly (alkoxylated phenol methacrylates), cellulose acetate, cellulose triacetate, cellulose acetate propionate, cellulose acetate butyrate, poly(vinyl acetate), poly(vinyl alcohol), poly(vinyl chloride), poly(vinylidene chloride), poly(vinylpyrrolidone), poly((meth)acrylamide), poly(dimethyl acrylamide), poly(hydroxyethyl methacrylate), poly((meth)acrylic acid), thermoplastic polycarbonates, polyesters, polyurethanes, polythiourethanes, poly(ethylene terephthalate), polystyrene, poly(alpha methylstyrene), copoly(styrene-methylmethacrylate), copoly(styrene-acrylonitrile), polyvinylbutyral and polymers of members of the group consisting of polyol(allyl carbonate)monomers, mono-functional acrylate monomers, mono-functional methacrylate monomers, polyfunctional acrylate monomers, polyfunctional methacrylate monomers, diethylene glycol dimethacrylate monomers, diisopropenyl benzene monomers, alkoxylated polyhydric alcohol monomers and diallylidene pentaerythritol monomers.

According to another specific embodiment, the at least one additional polymeric material may be a homopolymer or copolymer of monomer(s) chosen from acrylates, methacrylates, methyl methacrylate, ethylene glycol bis methacrylate, ethoxylated bisphenol A dimethacrylate, vinyl acetate, vinylbutyral, urethane, thiourethane, diethylene glycol bis(allyl carbonate), diethylene glycol dimethacrylate, diisopropenyl benzene, and ethoxylated trimethylol propane triacrylate.

Still other embodiments of the present disclosure provide for optical elements. The optical elements comprise a substrate and an at least partial layer on at least a portion of the substrate. As used herein, the term “layer” includes layers, coatings, and films, which may be cured. According to these embodiments, the at least partial layer comprises the mesogen containing compound or residue thereof as described according to various embodiments of the present disclosure, such as those having a structure according to Formulae I, II, III, IV, V, VI, VII, or VIII or mixtures thereof. In other embodiments, the partial layer may comprise the LC compositions according to the various embodiments described herein. As used herein the term “optical” means pertaining to or associated with light and/or vision. For example according to various embodiments, the optical element or device can be chosen from ophthalmic elements and devices, display elements and devices, windows, mirrors, and active and passive liquid crystal cell elements and devices.

As used herein, the term “liquid crystal cell” refers to a structure containing a liquid crystal material that is capable of being ordered. Active liquid crystal cells are cells wherein the liquid crystal material is capable of being switched between ordered and disordered states or between two ordered states by the application of an external force, such as electric or magnetic fields. Passive liquid crystal cells are cells wherein the liquid crystal material maintains an ordered state. One example of an active liquid crystal cell element or device is a liquid crystal display.

As used herein the term “ophthalmic” means pertaining to or associated with the eye and vision. Examples of ophthalmic elements include corrective and non-corrective lenses, including single vision or multi-vision lenses, which may be either segmented or non-segmented multi-vision lenses (such as bifocal lenses, trifocal lenses and progressive lenses), as well as other elements used to correct, protect, or enhance (cosmetically or otherwise) vision, including contact lenses, intra-ocular lenses, magnifying lenses, and protective lenses or visors; and may also include partially formed lenses and lens blanks. As used herein the term “display” means the visible or machine-readable representation of information in words, numbers, symbols, designs or drawings. Examples of display elements and devices include screens, monitors, and security elements, including security marks and authentication marks. As used herein the term “window” means an aperture adapted to permit the transmission of radiation therethrough. Examples of windows include automotive and aircraft transparencies, filters, shutters, and optical switches. As used herein the term “mirror” means a surface that specularly reflects a large fraction of incident light.

According to specific embodiments of the optical elements, the at least partial layer, for example a cured coating layer, may further comprise at least one of a photochromic compound, a dichroic compound, a photochromic-dichroic compound, a photosensitive material, a non-photosensitive material, and/or one or more additive. The one or more additive may be chosen from a liquid crystal, a liquid crystal property control additive, a non-linear optical material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer, a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent, a free radical scavenger, and/or an adhesion promoter. Specific examples of the photochromic compounds, the dichroic compounds, the photochromic-dichroic compounds, the photosensitive materials, the non-photosensitive materials, and the additives suitable for use in the various embodiments of the ophthalmic elements are discussed in detail elsewhere in the present disclosure.

While dichroic compounds are capable of preferentially absorbing one of two orthogonal components of plane polarized light, it is generally necessary to suitably position or arrange the molecules of a dichroic compound in order to achieve a net linear polarization effect. Similarly, it is generally necessary to suitably position or arrange the molecules of a dichroic or photochromic-dichroic compound to achieve a net linear polarization effect. That is, it is generally necessary to align the molecules of the dichroic or photochromic-dichroic compound such that the long axes of the molecules of the dichroic or photochromic-dichroic compound in an activated state are generally parallel to each other. Therefore, according to various embodiments disclosed herein, the at least one dichroic or photochromic-dichroic compound is at least partially aligned. Further, if the activated state of the dichroic or photochromic-dichroic compound corresponds to a dichroic state of the material, the at least one dichroic or photochromic-dichroic compound can be at least partially aligned such that the long axis of the molecules of the dichroic or photochromic-dichroic compound in the activated state are aligned. As used herein the term “align” means to bring into suitable arrangement or position by interaction with another material, compound or structure.

In certain embodiments, the dichroic compound and/or the photochromic-dichroic compound or other anisotropic material (such as certain embodiments of the mesogen containing compounds described herein) may be at least partially aligned. At least partial alignment of compositions, such as those comprising a dichroic compound, a photochromic-dichroic compound or other anisotropic material, may be effected by at least one of exposing the at least a portion of the composition to a magnetic field, exposing the at least a portion of the composition to a shear force, exposing the at least a portion of the composition to an electric field, exposing the at least a portion of the composition to plane-polarized ultraviolet radiation, exposing the at least a portion of the composition to infrared radiation, drying the at least a portion of the composition, etching the at least a portion of the composition, rubbing the at least a portion of the composition, and aligning the at least a portion of the composition with another structure or material, such as an at least partially ordered alignment medium. It is also possible to align the dichroic compound and/or the photochromic-dichroic compound or other anisotropic material (such as certain embodiments of the mesogen containing compounds described herein) with an oriented surface. That is, liquid crystal molecules can be applied to a surface that has been oriented, for example by rubbing, grooving, or photo-alignment methods, and subsequently aligned such that the long axis of each of the liquid crystal molecules takes on an orientation that is generally parallel to the general direction of orientation of the surface. Examples of liquid crystal materials suitable for use as alignment media according to various embodiments disclosed herein include the mesogen containing compounds or residues thereof, liquid crystal polymers, liquid crystal pre-polymers, liquid crystal monomers, and liquid crystal mesogens. As used herein the term “pre-polymer” means partially polymerized materials.

For example, according to embodiments where the optical element comprises a cured layer which comprises a photochromic compound, or a photochromic-dichroic compound, the coating may be adapted to switch from a first state to a second state in response to at least actinic radiation and further be able to revert back to the first state in response to thermal energy. In other embodiments, the coating may be adapted to linearly polarize at least transmitted radiation in at least one of the first state and the second state. In certain embodiments, the coating may linearly polarize at least transmitted radiation in both the first state and the second state.

As discussed above, one embodiment provides, in part, an optical element comprising an at least partial layer or coating having a first state and a second state connected to at least a portion of at least one surface of a substrate. As used herein the term “coating” means a supported film derived from a flowable composition, which may or may not have a uniform thickness, and specifically excludes polymeric sheets. The layer or coating may be cured after application to the surface of the optical element to form a cured layer or coating. As used herein the term “sheet” means a pre-formed film having a generally uniform thickness and capable of self-support. Further, as used herein the term “connected to” means in direct contact with an object or indirect contact with an object through one or more other structures or materials, at least one of which is in direct contact with the object. Thus, according to various embodiments disclosed herein, the at least partial coating can be in direct contact with at least a portion of the substrate or it can be in indirect contact with at least a portion of the substrate through one or more other structures or materials. For example the at least partial coating can be in contact with one or more other at least partial coatings, polymer sheets or combinations thereof, at least one of which is in direct contact with at least a portion of the substrate.

According to certain embodiments, the at least partial layer may be at least partially aligned. Suitable methods for at least partially aligning the at least partial layer include, at least one of exposing the at least a portion of the composition to a magnetic field, exposing the at least a portion of the composition to a shear force, exposing the at least a portion of the composition to an electric field, exposing the at least a portion of the composition to plane-polarized ultraviolet radiation, exposing the at least a portion of the composition to infrared radiation, drying the at least a portion of the composition, etching the at least a portion of the composition, rubbing the at least a portion of the composition, and aligning the at least a portion of the composition with another structure or material, such as an at least partially ordered alignment medium. Suitable alignment methods for layers are described in greater detail in U.S. Pat. No. 7,097,303, at column 27, line 17 to column 28, line 45.

According to certain embodiments of the optical element, the at least partial layer, for example a cured layer or coating, may further comprise at least one of a photochromic compound, an at least partially aligned dichroic compound, an at least partially aligned photochromic-dichroic compound, a photosensitive material, a non-photosensitive material, and one or more additives. The one or more additives may include a liquid crystal, a liquid crystal property control additive, a NLO material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer, a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent, a free radical scavenger, a coupling agent, a tilt control additive and an adhesion promoter. Suitable examples of these compounds, materials, and additives are described in greater detail elsewhere herein, for example, those described with reference to the LC compositions of the present disclosure.

According to certain embodiments of the optical elements described herein, the at least partial layer may be adapted to switch from a first state to a second state in response to at least actinic radiation and to revert back to the first state in response to thermal energy. For example, in those embodiments where the at least partial layer comprises a photochromic compound or a photochromic-dichroic compound, the at least partial layer may be adapted to switch from a first non-colored or clear state to a second colored state in response to at least actinic radiation and to revert back to the first clear state in response to thermal energy. In other embodiments where the at least partial layer may be adapted to linearly polarize at least transmitted radiation in at least one of the first state and the second state. For example, the at least partial layer may transmit linearly polarized radiation in certain embodiments which comprise a dichroic compound or photochromic-dichroic compound.

According to specific embodiments of the optical elements of the present disclosure, the at least partial layer may comprise a polymer or copolymer comprising the residue of one or more mesogen containing compounds described herein. The at least partial layer comprising a polymer or copolymer comprising the residue of a mesogen containing compound may be a cured at least partial layer. In other embodiments, the at least partial layer may comprise a liquid crystal phase. The liquid crystal phase may be a nematic phase, a smectic phase, a chiral nematic phase, or a discotic phase.

According to another embodiment, the present disclosure provides for an ophthalmic element comprising a substrate and an at least partial layer on at least a portion of a surface of the substrate. The at least partial layer may comprise at least one of a dichroic compound, a photochromic compound or a photochromic-dichroic compound; one or more additives; a first polymer having a Fischer microhardness ranging from 0 Newtons/mm² to 150 Newtons/mm² (and in certain embodiments from 50 Newtons/mm² to 150 Newtons/mm²); and a liquid crystal monomer or residue thereof represented by any of Formulae I, II, III, IV, V, VI, VII, or VIII, as described herein. According to specific embodiments, the dichroic compound and/or the photochromic-dichroic compound may be at least partially aligned. In other embodiments, the liquid crystal monomer or residue thereof may be at least partially aligned. The additive(s) may be selected from a liquid crystal, a liquid crystal property control additive, a NLO material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer, a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent, a free radical scavenger, a coupling agent, a tilt control additive, and an adhesion promoter. Suitable dichroic compounds, photochromic compounds, photochromic-dichroic compounds and additives are described in detail herein, such as when describing the liquid crystal compositions and optical elements of the present disclosure.

In specific embodiments, the residue of the liquid crystal monomer may be incorporated in to a liquid crystal polymer. For example, the residue of the LC monomer may be incorporated into the main chain of the LCP or incorporated as a side chain attached to the main chain of the LCP. Incorporation of the LC monomer residue into an LCP is described in detail elsewhere herein.

As used herein to modify the term “state,” the terms “first” and “second” are not intended to refer to any particular order or chronology, but instead refer to two different conditions or properties. For example, the first state and the second state of the coating may differ with respect to at least one optical property, such as the absorption or linearly polarization of visible and/or UV radiation. According to certain embodiments of the ophthalmic elements described herein, the at least partial layer may be adapted to switch from a first state to a second state in response to at least actinic radiation and to revert back to the first state in response to thermal energy. For example, in those embodiments where the at least partial layer comprises a photochromic compound or a photochromic-dichroic compound, the at least partial layer may be adapted to switch from a first non-colored or clear state to a second colored state in response to at least actinic radiation and to revert back to the first clear state in response to thermal energy. Alternatively, the at least partial coating can be adapted to have a first color in the first state and a second color in the second state. In other embodiments where the at least partial layer may be adapted to linearly polarize at least transmitted radiation in at least one of the first state and the second state. For example, the at least partial layer may transmit linearly polarized radiation in certain embodiments which comprise a dichroic compound or photochromic-dichroic compound. In other embodiments, the at least partial layer may comprise a liquid crystal phase. The liquid crystal phase may be a nematic phase, a smectic phase, a chiral nematic phase, or a discotic phase. According to still other embodiments, the at least partial coating having a first state and a second state can be adapted to have a first absorption spectrum in the first state, a second absorption spectrum in the second state, and to be linearly polarizing in both the first and second states.

Still other embodiments of the present disclosure provide for a liquid crystal cell. According to these embodiments, the liquid crystal cell may comprising a first substrate having a first surface; a second substrate having a second surface; and a mesogen containing compound or residue thereof as represented by any of Formulae I, II, III, IV, V, VI, VII, or VIII, as described herein. Referring still to the liquid crystal cell, the second surface of the second substrate may be opposite and spaced apart from the first surface of the first substrate so as to define a region. The mesogen containing compound or residue thereof may be placed in the region between the first substrate and second substrate. Alternatively, the mesogen containing compound or residue thereof may be incorporated into an at least partial layer on at least one of the first surface of the first substrate, the second surface of the second substrate, or both the first and second surfaces. The liquid crystal cell may be utilized as, for example, display elements, including screens, monitors, or security elements.

According to certain embodiments, the liquid crystal cell may further comprise at least one of a photochromic compound, a dichroic compound or a photochromic-dichroic compound. Suitable photochromic compounds, dichroic compounds or photochromic-dichroic compounds are described in detail herein, such as when describing the liquid crystal compositions and optical elements of the present disclosure. In other embodiments, the liquid crystal cells may further comprise an at least partial layer connected to at least a portion of a surface of at least one of the first substrate and the second substrate, such as, the first surface and/or second surface. The at least partial layer may be a linearly polarizing layer, a circularly polarizing layer, an elliptically polarizing layer, a photochromic layer, a reflective layer, a tinted layer, a retarder layer, and a wide-angle view layer.

According to certain embodiments, the liquid crystal cell may be a pixelated cell. As used herein, the term “pixelated” means that an article, such as a display element or liquid crystal cell may be broken down into a plurality of individual pixels (i.e., single point occupying a specific location within a display, image or cell. In certain embodiments, the liquid crystal cell may be a pixilated cell comprising a plurality of regions or compartments (i.e., pixels). The characteristics of the individual pixels, such as color, polarization and the like, may be controlled relative to the other pixels in the display element, liquid crystal, or article.

According to still other embodiments, the present disclosure provides for articles of manufacture comprising a composition comprising a mesogen containing compound or residue thereof represented by any of Formulae I, II, III, IV, V, VI, VII, or VIII, as described herein. Specific articles of manufacture include molded articles, assembled articles and cast articles.

Additionally, the present disclosure also provides methods for forming liquid crystal compositions, optical elements, ophthalmic elements, liquid crystal cells and articles of manufacture, such as those described herein.

For example, according to one embodiment, the present disclosure provides methods for forming an optical element, including an ophthalmic element. The methods comprise the step of formulating a liquid crystal composition; coating at least a portion of a substrate with the liquid crystal composition; at least partially aligning at least a portion of the liquid crystal composition in the coating layer; and curing the liquid crystal coating layer. The liquid crystal composition may be as described herein. For example, in one embodiment, the liquid crystal may comprise at least one mesogen containing composition or residue thereof; at least one photochromic compound, dichroic compound, or photochromic dichroic compound; and at least one additive. The mesogen containing composition or residue may be represented by any of Formulae I, II, III, IV, V, VI, VII, or VIII, as described herein. The least one photochromic compound, dichroic compound, or photochromic dichroic compound; and at least one additive are as described herein.

Methods of at least partially aligning the at least a portion of the liquid crystal composition in the coating are described herein and in U.S. Pat. No. 7,097,303, at column 27, line 17 to column 28, line 45.

Curing the liquid crystal coating layer may include at least partially polymerizing the liquid crystal composition. Methods for at least partially polymerizing a liquid crystal composition include exposing at least a portion of the liquid crystal composition to at least one of thermal energy (for example to activate a thermal initiator); infrared radiation, ultraviolet radiation, visible radiation, gamma radiation, microwave radiation, electron radiation or combinations thereof so as to initiate the polymerization reaction of the polymerizable components or cross-linking with or without a catalyst or initiator. If desired or required, this can be followed by a heating step. According to certain embodiments, the liquid crystal coating layer may be cured to a specific hardness. For example, in certain embodiments, the liquid crystal coating layer may be cured to have a Fischer microhardness ranging from 0 to 150 Newtons/mm² that also exhibits good photochromic and/or dichroic response characteristics. In another embodiment, the liquid crystal composition may be cured to a Fischer microhardness less than 60 Newtons/mm², e.g. from 0 to 59.9 Newtons/mm², or alternatively from 5 to 25 N/mm². In still other embodiments, the liquid crystal coating layer may be cured to have a Fischer microhardness ranging from 150 N/mm² to 250 N/mm² or alternatively from 150 N/mm² to 200 N/mm².

According to specific embodiments, the at least one additive may be adapted to affect a property of the liquid crystal composition, such as adjusting the liquid crystal clear temperature of the liquid crystal composition, lowering a viscosity of the liquid crystal composition, widening a phase temperature for a nematic phase of the liquid crystal composition, stabilizing a phase of the liquid crystal composition or controlling the tilt of the liquid crystal composition.

Specific methods for forming optical elements, such as ophthalmic elements which comprise at least a partial layer, such as a layer comprising a liquid crystal composition as described herein, on at least a portion of a surface of a substrate, are described in detail in U.S. Pat. No. 7,342,112 at column 83, line 16 of column 84, line 10. These disclosed methods include methods for forming articles, such as optical elements and ophthalmic elements, which may also include at least one of a photochromic compound, a dichroic compound, or a photochromic-dichroic compound, by a variety of methods known in the art, such as imbibing, coating, overmolding, spin coating, spray coating, spray and spin coating, curtain coating, flow coating, dip coating, injection molding, casting, roll coating, and wire coating.

Generally speaking, substrates that are suitable for use in conjunction with various embodiments disclosed herein include substrates formed from organic materials, inorganic materials, or combinations thereof (for example, composite materials). Examples of substrates that can be used in accordance with various embodiments disclosed herein are described in more detail below.

Specific, examples of organic materials that may be used to form the substrates disclosed herein include polymeric materials, such as those discussed in detail above, for examples, homopolymers and copolymers, prepared from the monomers and mixtures of monomers disclosed in U.S. Pat. No. 5,962,617 and in U.S. Pat. No. 5,658,501 from column 15, line 28 to column 16, line 17. For example, such polymeric materials can be thermoplastic or thermoset polymeric materials, can be transparent or optically clear, and can have any refractive index required. Examples of such disclosed monomers and polymers include: polyol(allyl carbonate) monomers, e.g., allyl diglycol carbonates such as diethylene glycol bis(allyl carbonate), which monomer is sold under the trademark CR-39 by PPG Industries, Inc.; polyurea-polyurethane (polyurea-urethane) polymers, which are prepared, for example, by the reaction of a polyurethane prepolymer and a diamine curing agent, a composition for one such polymer being sold under the trademark TRIVEX by PPG Industries, Inc.; polyol(meth)acryloyl terminated carbonate monomer; diethylene glycol dimethacrylate monomers; ethoxylated phenol methacrylate monomers; diisopropenyl benzene monomers; ethoxylated trimethylol propane triacrylate monomers; ethylene glycol bismethacrylate monomers; poly(ethylene glycol) bismethacrylate monomers; urethane acrylate monomers; poly(ethoxylated bisphenol A dimethacrylate); poly(vinyl acetate); poly(vinyl alcohol); poly(vinyl chloride); poly(vinylidene chloride); polyethylene; polypropylene; polyurethanes; polythiourethanes; thermoplastic polycarbonates, such as the carbonate-linked resin derived from bisphenol A and phosgene, one such material being sold under the trademark LEXAN; polyesters, such as the material sold under the trademark MYLAR; poly(ethylene terephthalate); polyvinyl butyral; poly(methyl methacrylate), such as the material sold under the trademark PLEXIGLAS, and polymers prepared by reacting polyfunctional isocyanates with polythiols or polyepisulfide monomers, either homopolymerized or co- and/or terpolymerized with polythiols, polyisocyanates, polyisothiocyanates and optionally ethylenically unsaturated monomers or halogenated aromatic-containing vinyl monomers. Also contemplated are copolymers of such monomers and blends of the described polymers and copolymers with other polymers, for example, to form block copolymers or interpenetrating network products.

While herein, according to various embodiments disclosed herein, the substrate can be an ophthalmic substrate. As used herein the term “ophthalmic substrate” means lenses, partially formed lenses, and lens blanks. Examples of organic materials suitable for use in forming ophthalmic substrates according to various embodiments disclosed herein include the art-recognized polymers that are useful as ophthalmic substrates, e.g., organic optical resins that are used to prepare optically clear castings for optical applications, such as ophthalmic lenses.

Other examples of organic materials suitable for use in forming the substrates according to various embodiments disclosed herein include both synthetic and natural organic materials, including: opaque or translucent polymeric materials, natural and synthetic textiles, and cellulosic materials such as, paper and wood.

Examples of inorganic materials suitable for use in forming the substrates according to various embodiments disclosed herein include glasses, minerals, ceramics, and metals. For example, in one embodiment the substrate can comprise glass. In other embodiments, the substrate can have a reflective surface, for example, a polished ceramic substrate, metal substrate, or mineral substrate. In other embodiments, a reflective coating or layer can be deposited or otherwise applied to a surface of an inorganic or an organic substrate to make it reflective or to enhance its reflectivity.

Further, according to certain embodiments disclosed herein, the substrates may have a protective coating, such as an abrasion-resistant coating, such as a “hard coat,” on their exterior surfaces. For example, commercially available thermoplastic polycarbonate ophthalmic lens substrates are often sold with an abrasion-resistant coating already applied to its exterior surfaces because these surfaces tend to be readily scratched, abraded or scuffed. An example of such a lens substrate is the GENTEX™ polycarbonate lens (available from Gentex Optics). Therefore, as used herein the term “substrate” includes a substrate having a protective coating, such as an abrasion-resistant coating, on its surface(s).

Still further, the substrates according to various embodiments disclosed herein can be untinted, tinted, linearly polarizing, circularly polarizing, elliptically polarizing, photochromic, or tinted-photochromic substrates. As used herein with reference to substrates the term “untinted” means substrates that are essentially free of coloring agent additions (such as conventional dyes) and have an absorption spectrum for visible radiation that does not vary significantly in response to actinic radiation. Further, with reference to substrates the term “tinted” means substrates that have a coloring agent addition (such as conventional dyes) and an absorption spectrum for visible radiation that does not vary significantly in response to actinic radiation.

As used herein, the term “linearly polarizing” with reference to substrates refers to substrates that are adapted to linearly polarize radiation (i.e., confine the vibrations of the electric vector of light waves to one direction). As used herein, the term “circularly polarizing” with reference to substrates refers to substrates that are adapted to circularly polarize radiation. As used herein, the term “elliptically polarizing” with reference to substrates refers to substrates that are adapted to elliptically polarize radiation. Further, as used herein, with reference to substrates, the term “tinted-photochromic” means substrates containing a coloring agent addition as well as a photochromic material, and having an absorption spectrum for visible radiation that varies in response to at least actinic radiation. Thus, for example, the tinted-photochromic substrate can have a first color characteristic of the coloring agent and a second color characteristic of the combination of the coloring agent the photochromic material when exposed to actinic radiation.

As described herein, in certain embodiments the optical element may be a security element. Examples of security elements include security marks and authentication marks that are connected to at least a portion of a substrate, such as: access cards and passes, e.g., tickets, badges, identification or membership cards, debit cards etc.; negotiable instruments and non-negotiable instruments e.g., drafts, checks, bonds, notes, certificates of deposit, stock certificates, etc.; government documents, e.g., currency, licenses, identification cards, benefit cards, visas, passports, official certificates, deeds etc.; consumer goods, e.g., software, compact discs (“CDs”), digital-video discs (“DVDs”), appliances, consumer electronics, sporting goods, cars, etc.; credit cards; and merchandise tags, labels and packaging.

Although herein, according to this embodiment, the security element can be connected to at least a portion of a substrate chosen from a transparent substrate and a reflective substrate. Alternatively, according to certain embodiments wherein a reflective substrate is required, if the substrate is not reflective or sufficiently reflective for the intended application, a reflective material can be first applied to at least a portion of the substrate before the security mark is applied thereto. For example, a reflective aluminum coating can be applied to the at least a portion of the substrate prior to forming the security element thereon. Still further, security element can be connected to at least a portion of a substrate chosen from untinted substrates, tinted substrates, photochromic substrates, tinted-photochromic substrates, linearly polarizing, circularly polarizing substrates, and elliptically polarizing substrates.

Furthermore, security element according to the aforementioned embodiment can further comprise one or more other coatings or sheets to form a multi-layer reflective security element with viewing angle dependent characteristics as described in U.S. Pat. No. 6,641,874.

The optical elements according to various embodiments disclosed herein can further comprise at least one additional at least partial coating that can facilitate bonding, adhering, or wetting of any of the various coatings connected to the substrate of the optical element. For example, according to one embodiment, the optical element can comprise an at least partial primer coating between the at least partial coating having the first state and the second state and a portion of the substrate. Further, in some embodiments disclosed herein, the primer coating can serve as a barrier coating to prevent interaction of the coating ingredients with the element or substrate surface and vice versa.

Examples of primer coatings that can be used in conjunction with various embodiments disclosed herein include coatings comprising coupling agents, at least partial hydrolysates of coupling agents, and mixtures thereof. As used herein “coupling agent” means a material having at least one group capable of reacting, binding and/or associating with a group on at least one surface. In one embodiment, a coupling agent can serve as a molecular bridge at the interface of at least two surfaces that can be similar or dissimilar surfaces. Coupling agents, in another embodiment, can be monomers, oligomers, pre-polymers and/or polymers. Such materials include organo-metallics such as silanes, titanates, zirconates, aluminates, zirconium aluminates, hydrolysates thereof and mixtures thereof. As used herein the phrase “at least partial hydrolysates of coupling agents” means that at least some to all of the hydrolyzable groups on the coupling agent are hydrolyzed. In addition to coupling agents and/or hydrolysates of coupling agents, the primer coatings can comprise other adhesion enhancing ingredients. For example the primer coating can further comprise an adhesion-enhancing amount of an epoxy-containing material. Adhesion-enhancing amounts of an epoxy-containing material when added to the coupling agent containing coating composition can improve the adhesion of a subsequently applied coating as compared to a coupling agent containing coating composition that is essentially free of the epoxy-containing material. Other examples of primer coatings that are suitable for use in conjunction with the various embodiments disclosed herein include those described U.S. Pat. No. 6,602,603 and U.S. Pat. No. 6,150,430.

The optical elements according to various embodiments disclosed herein can further comprise at least one additional at least partial coating chosen from conventional photochromic coatings, anti-reflective coatings, linearly polarizing coatings, circularly polarizing coatings, elliptically polarizing coatings, transitional coatings, primer coatings (such as those discussed above), and protective coatings connected to at least a portion of the substrate. For example the at least one additional at least partial coating can be over at least a portion of the at least partial coating having the first state and the second state, i.e., as an overcoating; or under at least a portion of the at least partial coating, i.e., as an undercoating. Additionally or alternatively, the at least partial coating having the first state and the second state can be connected at least a portion of a first surface of the substrate and the at least one additional at least partial coating can be connected to at least a portion of a second surface of the substrate, wherein the first surface is opposite the second surface.

Examples of conventional photochromic coatings include coatings comprising any of the conventional photochromic compounds that are discussed in detail below. For example, the photochromic coatings can be photochromic polyurethane coatings, such as those described in U.S. Pat. No. 6,187,444; photochromic aminoplast resin coatings, such as those described in U.S. Pat. Nos. 4,756,973, 6,432,544 and 6,506,488; photochromic polysilane coatings, such as those described in U.S. Pat. No. 4,556,605; photochromic poly(meth)acrylate coatings, such as those described in U.S. Pat. Nos. 6,602,603, 6,150,430 and 6,025,026, and WIPO Publication WO 01/02449; polyanhydride photochromic coatings, such as those described in U.S. Pat. No. 6,436,525; photochromic polyacrylamide coatings such as those described in U.S. Pat. No. 6,060,001; photochromic epoxy resin coatings, such as those described in U.S. Pat. Nos. 4,756,973 and 6,268,055; and photochromic poly(urea-urethane) coatings, such as those described in U.S. Pat. No. 6,531,076.

Examples of linearly polarizing coatings include coatings comprising conventional dichroic compounds such as those discussed above.

As used herein the term “transitional coating” means a coating that aids in creating a gradient in properties between two coatings. For example, a transitional coating can aid in creating a gradient in hardness between a relatively hard coating and a relatively soft coating. Examples of transitional coatings include radiation-cured acrylate-based thin films.

Examples of protective coatings include abrasion-resistant coatings comprising organo silanes, abrasion-resistant coatings comprising radiation-cured acrylate-based thin films, abrasion-resistant coatings based on inorganic materials such as silica, titania and/or zirconia, organic abrasion-resistant coatings of the type that are ultraviolet light curable, oxygen barrier-coatings, UV-shielding coatings, and combinations thereof. For example, according to one embodiment, the protective coating can comprise a first coating of a radiation-cured acrylate-based thin film and a second coating comprising an organo-silane. Examples of commercial protective coatings products include SILVUE® 124 and HI-GARD® coatings, available from SDC Coatings, Inc. and PPG Industries, Inc., respectively.

According to specific embodiment, the present disclosure provides for mesogen containing compounds having the following structures as disclosed in Table 1.

TABLE 1 Structure of Specific Mesogen Containing Compounds Structure and name

1,12-bis{2-(4-(4-(4-(3-(methacryloyloxy)propyloxy)benzoyloxy)phenyl)benzoyloxy)ethyloxy) dodecyl-1,12-dione

1,12-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy) dodecyl-1,12-dione

1,10-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy) 2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluorodecyl-1,10-dione

1,12-bis{6-(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)benzoyloxy)hexyloxy)dodecyl-1,12-dione

1-{3-(4-(3-(4-(6-(4(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy)-4- oxobutoyloxy)propyloxy)benzoyloxy)propyloxy}-4-{(6-(4(4-(4-(6-methacryloyloxyhexyloxy) benzoyloxy)phenyl)benzoyloxy)hexyloxy)}butane-1,4-dione

1-{3-(4-(3-(4-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-4- oxobutanoyloxy)propyloxy)benzoyloxy)propyloxy}-4-{6-(4-(4-(trans-4-propylcyclohexyl) phenoxycarbonyl)phenoxy)hexyloxy)butane-1,4-dione

2,2′-bis (6-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexanoyloxy)-6- hexanoyloxy)diethylether

1-{6-(6-(6-(6-(6-(6-(6-(4-(6-(4-(4-(4-nonylbenzoyloxy)phenoxycarbonyl)phenoxy)hexyloxy)-4- oxobutanoyloxy)hexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6- carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy}-4- {6-(4-(6-(4-(4-(4-nonylbenzoyloxy)phenoxycarbonyl)phenoxy) hexyloxy}butane-1,4-dione

2,5-bis(4-(12-hydroxydodecyloxy)benzoyloxy))toluene

2,5-bis(4-(12-tetrahydro-2H-pyran-2-yloxydodecyloxy)benzoyloxy)toluene

2-(6-(4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)benzyloxy)phenoxy)hexyloxy)tetrahydro-2H- pyran

(1R,4R)-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl) cyclohexane-1,4-dicarboxylate

2-(6-(4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)dodecyloxy)benzoyloxy)phenoxy)hexyloxy)tetrahydro- 2H-pyran

6-(4-(4-(12-hydroxydodecyloxy)benzoyloxy)phenoxy)hexan-1-ol

2-(5-(trans-4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)cyclohexyl)benzyloxy)pentyloxy) tetrahydro-2H-pyran

6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(6-(3-(6-(4-(4-(trans-4-pentylcyclohexyl) phenoxycarbonyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy)benzoate

2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6- (tetrahydro-2H-pyran-2-yloxy)hexyl)benzoate

2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6- methacryloyloxyhexyl)benzoate

2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6- hydroxyhexyl)benzoate

6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl) phenoxylcarbonyl)phenoxy)octyloxy)-4-oxobutoyloxy)octyloxy)benzoate

6-hydroxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy) octyloxy)-4-oxobutoyloxy)octyloxy)benzoate

6-methacryloyloxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl) phenoxy)octyloxy)-4-oxobutoyloxy)octyloxy)benzoate

1,2-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)ethanone

2-(6-(4-(trans-4-(12-(1-tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy)cyclohexyl)phenoxy) hexyloxy)tetrahydro-2H-pyran

1-(11-(4-(trans-4-(4-(6-(1-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl) cyclohexyloxycarbonyl)phenoxy)undecanoxy)prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2- methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4- pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol

1,2-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)ethane

2-(6-(trans-4-(4-(12-(tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy)cyclohexyl)phenoxy)-12- oxododecanoxy)tetrahydro-2H-pyran

1-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(5-(5-(5-(5-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-5- oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2- methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl) phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en- 1-one

1-(6-(5-(5-(6-(5-(6-(5-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-5- oxopentyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(5-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)- 5-oxopentyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-propylcyclohexyl)phenyloxy)hexanoyl)hexanoyl) hexanoyl)hexanoyl)hexanoyl)hexanoyl)hexanoyl)hexanoyloxy)-prop-2-ene

1-{3-(3-methacryloyloxy-2,2-dimethylpropyloxy)-3-oxo-2-methylpropyl}-3-{(8-(4-(trans-4-(trans-4- pentylcyclohexyl)cyclohexyloxycarbonyl)phenoxy)octyloxycarbonyl) ethyl)}- hexamethylenetrisiloxane

2,5-bis(4-(8-hydroxyoctyloxy)benzoyloxy)toluene

2,5-bis(4-(8-(6-hydroxyhexyloyloxy)octyloxy)benzoyloxy)toluene

1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(8-(4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

4-{4-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexyloxy)benzoyloxy}-3-methoxy-1-ethyl cinnamate

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-hexyloxybenzoyloxy) phenoxycarbonyl) cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2- methylprop-2-en-1-one

1-(6-(6-(6-(6-(trans-4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)cyclohexyloxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy) hexanoyloxy)benzoyloxy}naphthalene

2,8-di{4-(6-(6-(6-(6-(6-(methacryloyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy) hexanoyloxy)benzoyloxy}naphthalene

2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy) benzoyloxy}naphthalene

4-{4-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxyl)octyloxy)benzoyloxy}-3-methoxy-1-ethyl cinnamate

1-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

4,4′-bis(4-(8-(tetrahydro-2H-pyran-2-yloxy)octyloxy)benzoyloxy)biphenyl

1-(6-(4-(4-(trans-4-(6-hydroxyhexyloxy)cyclohexyl)phenyloxycarbonyl)phenyloxy)hexyloxy) prop-2- en-1-one

1-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy) phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one.

4,4′-bis(4-(8-hydroxyoctyloxy)benzoyloxy)biphenyl

1-(6-(6-(6-(6-(trans-4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy) hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy) pentan- 1-one

2-(8-(4-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenoxy) octyloxy)tetrahydro-2H-pyran

8-(4-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenoxy)octan-1-ol

1,4-bis{(6-(6-(6-(6-(6-(6-(trans-4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy} butan- 1,4-dione

1-(6-(6-(6-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1,4-bis{(6-(6-(6-(6-(6-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl) phenyloxycarbonyl)phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy}butan-1,4-dione

1-(6-(8-(4-(4-(4-(4-(8-(6-methacryloyloxy)hexyloyloxy)octyloxy)benzoyloxy)phenyl) phenyloxycarbonyl)phenyloxy)octyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl) phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2- methylprop-2-en-1-one

1-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-2- methylprop-2-en-1-one.

1-(5-(5-(5-(5-(5-(5-(6-(4-(4-(trans-4-propylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-5- oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)- 2-methylprop-2-en-1-one

1-(5-(5-(6-(5-(6-(5-(6-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-5- oxopentyloxy)-2-methylprop-2-en-1-one

1-(6-(8-(4-(4-(4-(4-(8-(6-methacryloyloxy)hexyloyloxy)octyloxy)benzoyloxy)phenyl) phenyloxycarbonyl)phenyloxy)octyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(11-(4-(4-(4-(6-(11-(tetrahydro-2H-pyran-2-yloxy)undecanyloxy)benzoyloxy)phenoxycarbonyl) phenoxy)hexyloxy)prop-2-en-1-one

1,4-bis(4-(11-(tetrahydro-2H-pyran-2-yloxy)undecanyloxy)benzoyloxy)benzene

1-(6-(6-(6-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(4-(4-benzoyloxyphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy) prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-benzoyloxyphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop- 2-en-1-one

1-(3-(3-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-3- carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-2-methylprop-2-en-1-one

1-(3-(3-(3-(3-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-3- carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)- 2-methylprop-2-en-1-one

1-(6-(6-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6- oxohexyloxo)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one.

1-(5-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-2- methylprop-2-en-1-one

1-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-2- methylprop-2-en-1-one

1-(5-(5-(5-(5-(5-(5-(5-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-5- oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)- 5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one

2-(6-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)hexan-1-ol

1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(5-(5-(5-(5-(5-(5-(5-(5-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy) hexyloxy)-5- oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)- 5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-1-carbonylaminoethyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl) phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenyloxy) hexyloxy)- 6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(5-(5-(5-(5-(5-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenyloxy) hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2- methylprop-2-en-1-one

2-(6-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)undecan-1-ol

1-(6-(6-(6-(11-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl) phenyloxy)undecanyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1- one

1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methoxybenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy) phenyl)cyclohexyloxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one.

1-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy) phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-ethoxyphenoxycarbonyl)phenyloxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(4-(4-(4-ethoxyphenoxycarbonyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-phenylphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one

1-(6-(6-(6-(4-(4-phenylphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2- en-1-one

1-(6-(6-(6-(trans-4-(4-(4-phenylphenoxycarbonyl)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-phenylphenoxycarbonyl)phenyl)cyclohexyloxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one

1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl) phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol

8-(4-(4-(4-(2,3-diacryloyloxypropyloxy)benzoyloxy)phenoxycarbonyl)phenoxy) octanol

6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(2,3-diacryloyloxypropyloxy) benzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)- 6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol

8-(4-(4-(4-(11-acryloyloxyundecyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octanol

6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(11-acryloyloxyundecanyloxy)benzoyloxy)phenoxycarbonyl) phenoxy)octyloxy) 6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol

8-(4-(4-(4-(8-acryloyloxyoctyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octanol

6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(11-acryloyloxyoctyloxy)benzoyloxy)phenoxycarbonyl) phenoxy)octyloxy) 6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6- oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol

1-[3-(6-(acryloyloxy)hexanoyloxy)-2-((6-(acryloyloxy)hexanoyloxy)methyl)-2-methylpropyloxy]-4-[6- (4-((4-(4-methylbenzoyloxy)phenoxy)carbonyl)phenoxy)hexyloxy]-butan-1,4-dione

1-[3-(acryloyloxy)-2,2-bis(acryloyloxymethyl)propyloxy]-4-[8-(4-((4-(4-methylbenzoyloxy) phenoxy)carbonyl)phenoxy)octyloxy]-butan-1,4-dione

1-(6-(6-(6-(6-(6-(8-(4-(4-(4-(8-acryloyloxyoctyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy) octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy) pentan- 1-one

EXAMPLES

Examples 1-31 describe the preparation of the materials of the present invention. Example 32 describes the methods used to measure the melting points and the liquid crystal phase transition temperatures of Examples 1-31.

The following abbreviations were used for the chemicals listed:

-   Al(OiPr)₃—aluminum triisopropylate -   DHP—3,4-dihydro-2H-pyran -   DCC—dicyclohexylcarbodiimide -   DIAD—diisopropyl azodicarboxylate -   DMAP—4-dimethylaminopyridine -   PPh₃—triphenyl phosphine -   PPTS—pyridine p-toluenesulfonate -   pTSA—p-toluenesulfonic acid -   NMP—N-methyl pyrrolidone -   BHT—butylated hydroxytoluene -   TBD—1,5,7-triazabicyclo[4.4.0]dec-5-ene -   THF—tetrahydrofuran -   DMF—dimethyl formamide -   DMA—dimethyl aniline

Example 1 Step 1

To a reaction flask was added 4-hydroxybenzoic acid (90 grams (g), 0.65 mole (mol)), ethyl ether (1000 milliliters (mL)) and p-toluenesulfonic acid (pTSA) (2 g). The resulting suspension was stirred at room temperature. 3,4-Dihydro-2H-pyran (DHP) (66 g, 0.8 mol) was added to the mixture. The suspension turned clear soon after the addition of DHP and a white crystalline precipitate formed. The mixture was then stirred at room temperature overnight. The resulting precipitates were collected by vacuum filtration and washed with ethyl ether. White crystals were recovered as the product (90 g, 62% yield). Nuclear Magnetic Resonance (NMR) showed that the product had a structure consistent with 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid.

Step 2 Background

The present invention relates generally to mesogen containing compounds, formulations thereof, optical elements, liquid crystal polymers and methods of making the same.

To a reaction flask was added 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid (65.5 g, 0.295 mol) from Step 1, 4-(trans-4-pentylcyclohexyl)phenol (70.3 g, 0.268 mole), dicyclohexylcarbodiimide (DCC) (66.8 g, 0.324 mol), 4-dimethylaminopyridine (DMAP) (3.3 g) and methylene chloride (1 L). The resulting mixture was mechanically stirred at 0° C. for 30 minutes, then at room temperature for 2 hours. The resulting solids were filtered off. The solution was concentrated until white crystals started to precipitate. One liter of methanol was added into the mixture with stirring. The precipitated solid crystalline product was collected by vacuum filtration and washed with methanol. White crystals (126 g) were recovered as the product. NMR showed that the product had a structure consistent with 4-(trans-4-pentylcyclohexyl)phenyl 4-(tetrahydro-2H-pyran-2-yloxy)benzoate.

Step 3

The product from Step 2, 4-(trans-4-pentylcyclohexyl)phenyl 4-(tetrahydro-2H-pyran-2-yloxy)benzoate (120 g, 0.26 mol), was dissolved in 1,2-dichloroethane (600 mL) in an appropriate reaction flask. Methanol (300 mL) and pyridinium p-toluenesulfonate (PPTS) (9 g, 36 millimole (mmol)) was added. The mixture was heated to reflux and maintained at reflux for 6 hours. Upon standing at room temperature overnight, white crystals precipitated out which were collected by vacuum filtration. The mother liquid was concentrated and more white crystals precipitated out with the addition of methanol. The combined product (90 g) was washed with methanol (about 300 mL) three times and air dried. NMR showed that the product had a structure consistent with 4-(trans-4-pentylcyclohexyl)phenyl 4-hydroxybenzoate.

Step 4

To a reaction flask was added the product of Step 3, 4-(trans-4-pentylcyclohexyl) phenyl 4-hydroxybenzoate (70 g, 190 mmol), 6-chloro-1-hexanol (30 g, 220 mmol), N-methyl pyrrolidone (NMP) (300 mL), sodium iodide (6 g), and potassium carbonate (57 g, 410 mmol). The resulting mixture was vigorously stirred at 85-90° C. for 4 hours. The resulting mixture was extracted using 1/1 volume ratio of ethyl acetate/hexanes (1 L) and water (500 mL). The separated organic layer was washed several times with water to remove NMP and then dried over anhydrous magnesium sulfate. After concentration, acetonitrile was added to precipitate the product. White crystals (76 g) were collected by vacuum filtration. NMR showed that the product had a structure consistent with 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate.

Step 5

To a reaction flask was added the product of Step 4, 4-(trans-4-pentylcyclohexyl) phenyl 4-(6-hydroxyhexyloxy)benzoate (2 g, 4.3 mmol), epsilon-caprolactone (2.94 g, 26 mmol), aluminum triisopropoxide (0.26 g, 1.3 mmol) and methylene chloride (40 mL). The resulting mixture was stirred at room temperature for 8 hours. Butylated hydroxytoluene (BHT) (9 milligram (mg), 0.04 mmol), DMAP (0.05 g, 0.43 mmol) and N,N-diethylaniline (1.8 g, 15 mmol) was added to the mixture and the mixture was stirred for half an hour. Freshly distilled methacryloyl chloride (1.34 g, 13 mmol) was then added to the mixture. After stirring at room temperature for 8 hours, the mixture was washed with 5 weight percent NaOH aqueous solution three times, with an aqueous 1 Normal (N) HCl solution three times and then with the 5 weight percent NaOH aqueous solution one more time. Note that whenever weight percent is reported herein, it is based on the total weight of the solution. The organic layer was separated and dried over anhydrous MgSO₄. After concentration, a methanol washing was done by adding 100 mL of methanol to the recovered oil with stirring. After 10 minutes, the resulting cloudy mixture was left at room temperature. After the cloudiness of the mixture cleared, methanol on top of the mixture was decanted. This methanol wash was done three times. The recovered oil was re-dissolved in ethyl acetate, dried over anhydrous magnesium sulfate and concentrated. A viscous liquid (3.9 g) was recovered as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 6.5 as represented by the following graphic formula.

Example 2 Step 1

Under the protection of nitrogen in an appropriate reaction flask, a mixture of 1-bromo-4-(trans-4-pentylcyclohexyl)benzene (43.31 g, 0.285 mol), 4-methoxyphenylboronic acid (88.1 g, 0.285 mol), dimethyl ethylene glycol (500 mL), tetrakistriphenylphosphine palladium (0) (1.64 g, 1.4 mmol), sodium carbonate (121 g, 1.14 mol) and water (570 mL) was degassed and then refluxed for 4 hours. After cooling to room temperature, methylene chloride (1 L) and water (500 mL) was added and stirred. The organic layer was separated, dried over anhydrous MgSO₄, filtered and concentrated. The product was purified by recrystallization from ethyl acetate to yield white crystals (82 g) as product. NMR showed that the product had a structure consistent with 4-methoxy-4′-(trans-4-pentylcyclohexyl)biphenyl.

Step 2

The product of Step 1, 4-methoxy-4′-(trans-4-pentylcyclohexyl)biphenyl (80 g), and pyridine hydrochloride (300 g) were added to a reaction flask and heated to 200° C. for one hour. The resulting mixture was poured into water while hot. The product separated out as an oil. The water was decanted and the product was dissolved in methylene chloride, washed with water and a saturated sodium bicarbonate water solution several times, dried over anhydrous MgSO₄ and then concentrated. The concentrated product was recrystallized using ethanol yielding white crystals as the product (75 g). NMR showed that the product had a structure consistent with 4-hydroxy-4′-(trans-4-pentylcyclohexyl)biphenyl.

Step 3

The procedure of Step 4 of Example 1 was followed except that 4-hydroxy-4′-(trans-4-pentylcyclohexyl)biphenyl from Step 2 above was used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-hydroxybenzoate. White crystals were obtained as the product. NMR showed that the product had a structure consistent with 4-(6-hydroxyhexyloxy)-4′-(4-trans-pentylcyclohexyl)biphenyl.

Step 4

A mixture of the product from Step 3, 4-(6-hydroxyhexyloxy)-4′-(4-trans-pentylcyclohexyl)biphenyl (7.2 g, 17 mmol), epsilon-caprolactone (5.83 g, 51.1 mmol), 1,5,7-triazabicyclo[4.4.0]dec-5-ene, (TBD) (0.71 g, 5.1 mmol) and toluene (100 mL) was added to a reaction flask and stirred at room temperature for one hour. To the resulting mixture was added BHT (40 mg, 0.17 mmol), DMAP (0.2 g, 1.7 mmol) and N,N-diethylaniline (7.6 g, 51.1 mmol) and the mixture was stirred for five minutes. Freshly distilled methacryloyl chloride (5.4 g, 51.1 mmol) was then added to the mixture and stirred overnight. The resulting mixture was washed with 5 weight percent NaOH aqueous solution three times, 1 N HCl aqueous solution three times and then with 5 weight percent NaOH aqueous solution one more time. The organic layer was separated and dried over anhydrous MgSO₄. After concentration, the methanol washing procedure of Step 5 of Example 1 was followed except that 200 mL of methanol was used. The recovered oil was re-dissolved in ethyl acetate, dried over anhydrous magnesium sulfate and concentrated. A white wax (13 g) was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 3.0 as represented by the following graphic formula.

Example 3 Step 1

4-(Hexyloxy)benzoic acid (92.5 g, 0.42 mol), 1,4-dihydroquinone (229 g, 2.1 mol), DMAP (5 g, 42 mmol), tetrahydrofuran (THF) (400 mL) and methylene chloride (400 mL) were added to a reaction flask and stirred. DCC (94.2 g, 0.46 mol) was added in five portions. The resulting reaction mixture was stirred for 17 hours and the solid was filtered off. The solution was concentrated and washed with water to remove 1,4-dihydroquinone. An off-white solid (152 g) was obtained as the product. Some product was purified by silica gel column separation using a mixture of ethyl acetate and hexanes for the next step. NMR showed that the product had a structure consistent with 4-hydroxyphenyl 4-(hexyloxy)benzoate.

Step 2

The procedures of Steps 2 and 3 of Example 1 were followed except that 4-hydroxyphenyl 4-(hexyloxy)benzoate from Step 1 above and 4-(8-(tetrahydro-2H-pyran-2-yloxy)octyloxy)benzoic acid were used in place of 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid and 4-(trans-4-pentylcyclohexyl)phenol. White crystals were obtained as the product. NMR showed that the product had a structure consistent with 4-(4-(hexyloxy)benzoyloxy)phenyl 4-(8-hydroxyoctyloxy)benzoate.

Step 3

The procedure of Step 5 of Example 1 was followed except that the product of Step 2 above, 4-(4-(hexyloxy)benzoyloxy)phenyl 4-(8-hydroxyoctyloxy)benzoate, and three equivalents of epsilon-caprolactone were used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate and six equivalents of epsilon-caprolactone. White wax was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(8-(4-(4-(4-hexyloxybenzoyloxy)phenoxy-carbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 3.0 as represented by the following graphic formula.

Example 4

The product from Step 4 of Example 1, 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate (1 g, 2 mmol), epsilon-caprolactone (6.9 g, 60 mmol), TBD (0.042 g, 0.3 mmol) and toluene (10 mL) were added to a reaction flask and stirred at room temperature for one and an half hours. pTSA (1 g) was added to the mixture to quench the reaction. Methanol (150 mL) was added to the resulting reaction mixture and the product separated as an oil. After stirring for 10 minutes, the methanol was decanted and this washing step was repeated three more times. The recovered oil was re-dissolved in ethyl acetate, dried over anhydrous magnesium sulfate and concentrated. A white wax (5.8 g) was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol with n having an average distribution of 23.1 as represented by the following graphic formula.

Example 5

The procedure of Step 5 of Example 1 was followed except that eleven equivalents of epsilon-caprolactone were used in place of six equivalents of epsilon-caprolactone. White wax was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 11.0 as represented by the following graphic formula.

Example 6

The procedure of Step 5 of Example 1 was followed except that fifteen equivalents of epsilon-caprolactone were used in place of six equivalents of epsilon-caprolactone. White wax was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 15.0 as represented by the following graphic formula.

Example 7

The procedure of Step 5 of Example 1 was followed except that a mixture of four equivalents of epsilon-caprolactone and four equivalents of delta-valerolactone was used in place of six equivalents of epsilon-caprolactone. White wax was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(5-(5-(6-(5-(6-(5-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with m+n having an average distribution of 8.0 as represented by the following graphic formula.

Example 8 Step 1

To a reaction flask was added 8-chloro-1-octanol (25 g, 0.183 mol), DHP (15.4 g, 0.183 mol) and methylene chloride (300 mL) and stirred at 0° C. in an ice bath. Several crystals of pTSA-monohydrate were added and after 10 minutes, the ice bath was removed and the mixture was stirred at room temperature for an hour. Sodium bicarbonate (2 g) was added to the mixture and then the mixture was concentrated and used directly for the next step.

Step 2

To a reaction flask containing the product from Step 1 (0.183 mol) was added DMF (600 mL), sodium bicarbonate (61.5 g, 0.732 mol) and 2,5-dihydroxybenzoic acid (28.2 g, 0.183 mol). The mixture was stirred at 100-120° C. for 6 hours. Extraction was done using 2/1 volume ratio of ethyl acetate/hexane (1 L) and water (2 L) for five times. The organic layer was separated, dried over anhydrous magnesium sulfate and concentrated. The product was used directly in the next step.

Step 3

To a reaction flask containing the product from Step 2 (46.8 g, ˜0.138 mol) was added 8-chloro-1-octanol (45.5 g, 0.276 mol), potassium carbonate (76 g, 0.55 mol), potassium iodide (1 g, 6 mmol) and NMP (300 mL). The mixture was stirred at 110° C. for 4 hours. Extraction was done using 1/1 ethyl acetate/hexanes (1 L) and water (2 L). The organic layer was separated, dried over anhydrous magnesium sulfate and concentrated. The recovered oil was purified by flash column separation (1/1 volume ratio of ethyl acetate/hexanes). A clear liquid (16.2 g) was obtained as the product. NMR showed that the product had a structure consistent with 6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(8-hydroxyoctyloxy)benzoate.

Step 4

The procedure of Step 4 of Example 1 was followed except that 8-chloro-1-octanol was used in place of 6-chloro-1-hexanol. White crystals were obtained as the product. NMR showed that the product had a structure consistent with 4-(trans-4-pentylcyclohexyl) phenyl 4-(8-hydroxyoctyloxy)benzoate.

Step 5

To a reaction flask was added the product from Step 4, 4-(trans-4-pentylcyclohexyl)phenyl 4-(8-hydroxyoctyloxy)benzoate (30 g, 61 mmol), succinic anhydride (6.7 g, 67 mmol), DMAP (0.37 g, 3 mmol) and THF (150 mL) and was refluxed for 2 hours. Extraction was done using methylene chloride (1 L) and water (1 L). The organic layer was separated, dried over anhydrous MgSO₄ and concentrated. The product was recrystallized from a mixture of methylene chloride and methanol. White crystals (35 g) were obtained.

Step 6

To a reaction flask was added the product from Step 5 (7 g, 12 mmol), 6-(tetrahydropyran-2-yloxy)hexyl 2,5-di(8-hydroxyloctyloxy)benzoate from Step 3 (3 g, 6 mmol), DCC (2.4 g, 12 mmol), DMAP (0.12 g, 1 mmol) and methylene chloride (70 mL). The resulting mixture was stirred at room temperature for 4 hours. The solid was filtered off. The filtrate was concentrated and methanol was used to precipitate out the product. After further purification using a silica gel flash column separation, a white solid (10 g) was obtained as the product. NMR showed that the product had a structure consistent with 6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl) phenoxy)octyloxycarbonyl)propionyloxy)octyloxy)benzoate represented by the following graphic formula.

Example 9

To a reaction flask was added the product of Example 8 (8 g), methanol (50 mL), PPTS (0.21 g) and 1,2-dichloroethane (100 mL). The resulting mixture was refluxed for 4 hours. The solvent was removed and a white solid was recovered. The product was purified by flash chromatography (20/1 methylene chloride/acetone). A viscous oil (5 g) was recovered as the product, which solidified upon standing at room temperature. NMR showed that the product had a structure consistent with 6-hydroxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)octyloxycarbonyl)propionyloxy)octyloxy)benzoate represented by the following graphic formula.

Example 10

To a reaction flask was added the product of Example 9 (3.3 g), N,N-diethylaniline (1 g, 6.77 mmol), BHT (4 mg, 0.02 mmol), DMAP (10 mg, 0.08 mmol) and methacryloyl chloride (0.68 g, 6.55 mmol). The resulting mixture was stirred at room temperature for 17 hours. The mixture was then diluted with methylene chloride and washed with 5% NaOH aqueous solution three times, 1 N HCl aqueous solution three times and then 5% NaOH aqueous solution one more time. The organic layer was separated and dried over anhydrous MgSO₄. After concentration, the product was purified by flash column separation (50/1 methylene chloride/acetone). NMR showed that the recovered white crystals (2.5 g) had a structure consistent with 6-methacryloyloxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)octyloxycarbonyl)propionyloxy)octyloxy)benzoate represented by the following graphic formula.

Example 11

The procedure of Example 8 was followed except that 6-chlorohexan-1-ol was used in place of 8-chlorooctan-1-ol in Steps 3 and 4. A milky liquid was recovered as the product which solidified upon standing at room temperature. NMR showed that the product had a structure consistent with 6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(6-(3-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)hexyloxycarbonyl)propionyloxy)hexyloxy) benzoate as represented by the following graphic formula.

Example 12 Step 1

The procedure of Step 1 of Example 1 was followed except that 4′-hydroxybiphenyl-4-carboxylic acid and THF was used in place of 4-hydroxybenzoic acid and ethyl ether. White crystals were obtained as the product. NMR showed that the product had a structure consistent with 4′-(tetrahydro-2H-pyran-2-yloxy)biphenyl-4-carboxylic acid.

Step 2

To a reaction flask was added the product of Step 1, 4′-(tetrahydro-2H-pyran-2-yloxy)biphenyl-4-carboxylic acid (7.16 g, 24 mmol), 6-bromohexan-1-ol (4.34 g, 24 mmol), NMP (60 mL), and potassium carbonate (6.63 g, 48 mmol). The resulting mixture was vigorously stirred at 100° C. for 2 hours. The resulting mixture was extracted using 1/1 (volume) ethyl acetate/hexanes (500 mL) and water (500 mL). The organic layer was separated, washed several times with water and then dried over anhydrous magnesium sulfate. After concentration, a viscous oil (8.3 g) was recovered as the product. NMR showed that the product had a structure consistent with 6-hydroxyhexyl 4′-(tetrahydro-2H-pyran-2-yloxy)biphenyl-4-carboxylate.

Step 3

The procedures of Steps 2 and 3 of Example 1 were followed except that two equivalents of 6-hydroxyhexyl 4′-(tetrahydro-2H-pyran-2-yloxy)biphenyl-4-carboxylate from Step 2 above and one equivalent of dodecanedioic acid was used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-hydroxybenzoate and 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid. White solid was recovered as the product. NMR showed that the product had a structure consistent with bis(6-(4-(4-hydroxyphenyl)benzoyloxy)hexyl) dodecanedioate.

Step 4

The procedure of Step 2 of Example 1 was followed except that bis(6-(4-(4-hydroxyphenyl)benzoyloxy)hexyl)dodecanedioate from Step 3 above and 4-(6-(methacryloyloxy)hexyloxy)benzoic acid were used in place of 4-(trans-4-pentylcyclohexyl) phenyl 4-hydroxybenzoate and 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid. The product was further purified using a silica gel flash column separation with an ethyl acetate hexanes mixture. White crystals were recovered as the product. NMR showed that the product had a structure consistent with 1,12-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl) benzoyloxy)hexyloxy)dodecyl-1,12-dione represented by the following graphic formula.

Example 13

The procedure of Example 12 was followed except that 2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluorodecanedioic acid was used in place of dodecanedioic acid. A white solid was recovered as the product. NMR showed that the product had a structure consistent with 1,10-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy) 2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluorodecyl-1,10-dione represented by the following graphic formula.

Example 14 Step 1

The procedure of Step 4 of Example 1 was followed except that two and a half equivalents of 3-chloro-1-propanol and one equivalent of 4-hydroxybenzoic acid was used in place of 6-chloro-1-hexanol and 4-(trans-4-pentylcyclohexyl)phenyl 4-hydroxybenzoate. The product was recovered as an oil. NMR showed that the product had a structure consistent with 3-hydroxypropyl 4-(3-hydroxypropoxy)benzoate.

Step 2

The procedure of Step 5 of Example 8 was followed except that two and a half equivalents of succinic anhydride and one equivalent of the product of Step 1, 3-hydroxypropyl 4-(3-hydroxypropoxy)benzoate, were used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-(8-hydroxyoctyloxy)benzoate and succinic anhydride. The product was obtained as an oil. NMR showed that the product had a structure consistent with 4-(3-(4-(3-(4-carboxybutanoyloxy) propoxy)benzoyloxy)propoxy)-4-oxobutan-1-oic acid.

Step 3

The procedure of Example 12 was followed except that the product from Step 2 above was used in place of dodecanedioic acid. The product was recovered as an oil. NMR showed that the product had a structure consistent with 1-{3-(4-(3-(4-(6-(4(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy)-4-oxobutoyloxy) propyloxy)benzoyloxy)propyloxy}-4-{(6-(4(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy) phenyl)benzoyloxy)hexyloxy)}butane-1,4-dione represented by the following graphic formula.

Example 15 Step 1

The procedures of Steps 1, 2 and 3 of Example 1 were followed except that 4-(trans-4-propylcyclohexyl)phenol was used in place of 4-(trans-4-pentylcyclohexyl)phenol. White crystals were recovered as the product. NMR showed that the product had a structure consistent with 4-(trans-4-propylcyclohexyl)phenyl 4-hydroxybenzoate.

Step 2

To a reaction flask was added the product of Step 1, 4-(trans-4-propylcyclohexyl) phenyl 4-hydroxybenzoate (4.98 g, 14.7 mmol), polycaprolactone diol (2.6 g, 4.9 mmol, Mn 530, Aldrich catalogue number 189405), triphenyl phosphine (PPh₃) (3.86 g, 14.7 mmol), THF (40 mL) and diisopropyl azodicarboxylate (DIAD) (2.98 g, 14.7 mmol). The resulting mixture was stirred at room temperature for 20 hours. After concentration, a silica gel flash column separation using ethyl acetate hexanes mixture was used to collect the major components of the products. A white solid was recovered as the product (3.2 g). NMR showed that the product had a structure consistent with 2,2′-bis(6-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexanoyloxy)-6-hexanoyloxy)diethylether with each n having an average distribution of 2.2 as represented by the following graphic formula.

Example 16

The procedure of Example 4 was followed except that 2 equivalents of epsilon-caprolactone was used in place of 6 equivalents. A wax was obtained as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(4-(trans-4-pentylcyclohexyl) phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 2.1 as represented by the following graphic formula.

Example 17 Step 1

To a reaction flask containing a mixture of hydroquinone (110 g, 1.0 mol), pTSA (9.5 g, 0.05 mol), and 1 L of diethyl ether was added DHP (84 g, 1.0 mol) over a period of 30 min with stirring under a nitrogen atmosphere. After stirring overnight with nitrogen bubbling, the solution was extracted twice with nitrogen-purged solutions of 22.5 g of NaOH in 300 mL of water (total: 1.12 mol). The combined aqueous NaOH solutions were extracted with 300 mL of diethyl ether and cooled to 0° C. with an ice bath. Sodium bicarbonate (5.0 g) was added, and the stirred solution was slowly acidified with 64 mL of acetic acid (1.12 mol). The resulting mixture was stored at −18° C. overnight and then allowed to warm up to 0° C. The precipitated product was washed three times with 300 mL of water and dried under vacuum. The yield was 84 g (43%). NMR showed that the product had a structure consistent with 4-(tetrahydro-2H-pyran-2-yloxy) phenol.

Step 2

The procedures of Steps 2 and 3 of Example 1 were followed except that 4-(6-(acryloyloxy)hexyloxy)benzoic acid and the product of Step 1, 4-(tetrahydro-2H-pyran-2-yloxy)phenol were used in place of 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid and 4-(trans-4-pentylcyclohexyl)phenol. The product was further purified by column chromatography eluting with hexane/ethyl acetate (7:3 volume ratio) to give the final product in a form of a white powder. NMR showed that the recovered white solid had a structure consistent with 4-hydroxyphenyl 4-(6-(acryloyloxy)hexyloxy)benzoate.

Step 3

The procedures of Steps 2 and 3 of Example 1 were followed except that 4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)benzoic acid and the product of Step 2, 4-hydroxyphenyl 4-(6-(acryloyloxy)hexyloxy)benzoate were used in place of 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid and 4-(trans-4-pentylcyclohexyl)phenol. NMR showed that the product had a structure consistent with 4-(4-(6-(acryloyloxy)hexyloxy)benzoyloxy)phenyl 4-(6-hydroxyhexyloxy)benzoate.

Step 4

To a solution of epsilon-caprolactone (6.04 g, 52.9 mmol) and the product from Step 3, 4-(4-(6-(acryloyloxy)hexyloxy)benzoyloxy)phenyl 4-(6-hydroxyhexyloxy)benzoate (4.0 g, 6.6 mmol) in 400 mL of CH₂Cl₂ in a 500 mL single-necked, round-bottomed flask was added triisopropoxyaluminum (Al(OiPr)₃) (0.41 g, 2.0 mmol). The reaction was stirred for 48 hours at room temperature under nitrogen protection. The resulting solution was washed with 1 N HCl (100 mL, three times), 5 weight percent of NaOH aqueous solution (100 mL, once), and saturated brine (100 mL, three times). An appropriate amount of ethanol was added to destroy the emulsion formed. The resulting mixture was dried over anhydrous magnesium sulfate, flashed through a silica gel plug column, and the removal of the solvent yielded 9.6 g of a waxy solid (95.6%) as the product. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl) phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol with n having an average distribution of 8 as represented by the following graphic formula.

Example 18

The procedure of Example 1 was followed except that in Step 2, 4-(trans-4-propylcyclohexyl)phenol was used in place of 4-(trans-4-pentylcyclohexyl)phenol and in Step 5, 4 equivalents of 1,3-dioxan-2-one was used in place of epsilon-caprolactone. NMR showed that the product had a structure consistent with 1-(3-(3-(3-(3-(6-(4-(trans-4-propylcyclohexyl) phenoxycarbonyl)phenoxy)hexyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 3.5 as represented by the following graphic formula.

Example 19 Step 1

The procedure of Step 2 of Example 1 was followed except that 4-(8-acryloxyoctoxy)benzoic acid and 4-(trans-4-(6-hydroxyhexyloxy)cyclohexyl)phenol were used in place of 4-(tetrahydro-2H-pyran-2-yloxy)benzoic acid and 4-(trans-4-pentylcyclohexyl) phenol. The product was further purified by column separation. NMR showed that the product had a structure consistent with 4-(trans-4-(6-hydroxyhexyloxy)cyclohexyl) phenyl 4-(6-(acryloyloxy)hexyloxy)benzoate.

Step 2

The procedure of Step 5 of Example 1 was followed except that the product from Step 1 above, 4-(trans-4-(6-hydroxyhexyloxy)cyclohexyl)phenyl 4-(6-(acryloyloxy)hexyloxy) benzoate, three equivalents of epsilon-caprolactone and pentanoyl chloride were used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate, six equivalents of epsilon-caprolactone and methacryloyl chloride. NMR showed that the product had a structure consistent with 1-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl) cyclohexyloxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)pentan-1-one with n having an average distribution of 5.0 as represented by the following graphic formula.

Example 20

The procedure of Example 19 was followed except that in Step 2, four equivalents of epsilon-caprolactone were used in place of 3 equivalents, 0.5 equivalents of succinyl dichloride was used in place of pentanoyl chloride. NMR showed that the product had a structure consistent with 1,4-bis-{(6-(6-(6-(6-(6-(6-(trans-4-(4-(6-acryloyloxyhexyloxy) benzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy}butan-1,4-dione with m+n having an average distribution of 9.7 as represented by the following graphic formula.

Example 21

The procedure of Example 3 was followed except that 4-(6-acryloyloxyhexyloxy) benzoic acid was used in place of 4-(hexyloxy)benzoic acid, biphenyl-4,4′-diol was used in place of 1,4-dihydroquinone, 10 equivalents of epsilon-caprolactone was used in place of three equivalents of epsilon-caprolactone and 0.5 equivalents of succinyl dichloride was used in place of pentanoyl chloride. NMR showed that the product had a structure consistent with 1,4-bis{(6-(6-(6-(6-(6-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl) phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy}butan-1,4-dione with m+n having an average distribution of 7.2 as represented by the following graphic formula.

Example 22 Step 1

A solution of DHP (13.9 g, 165 mmol) in 10 mL of THF was added to a reaction flask containing a solution of 1,12-dodecanediol (50.0 g, 247 mmol) and a catalytic amount of PPTS in anhydrous THF (100 mL). The reaction mixture was stirred under N₂ at room temperature for 24 h and then poured into sodium bicarbonate saturated water. The organic layer was separated. The aqueous layer was extracted with ethyl acetate. The combined organic solution was dried over anhydrous magnesium sulfate, concentrated and purified with flash chromatography to give 24.8 g of product.

Step 2

To a reaction flask containing a mixture of methyl 4-hydroxybenzoate (8.7 g, 57 mmol), triphenylphosphine (15.0 g, 57 mmol) and THF (60 mL) was added dropwise a solution of diisopropyl azodicarboxylate (11.5 g, 57 mmol), the product of Step 1 above (13.6 g, 25 mmol) and THF (10 mL). The mixture was stirred at room temperature overnight. The resulting precipitates were filtered off and the filtrate was concentrated. The resulting residue was purified by flash chromatography to give 18.9 g of product. NMR showed that the product had a structure consistent with methyl 4-(12-(tetrahydro-2H-pyran-2-yloxy)dodecyloxy)benzoate.

Step 3

To a reaction flask was added a solution of the product of Step 2 above, (18.0 g, 43 mmol) and sodium hydroxide (2.56 g, 64 mmol) in methanol (100 mL) which was refluxed for 4 hours. The resulting mixture was acidified with 2 N HCl and then extracted with dichloromethane, washed with brine and water. The solvent was removed to give 18 g of product which was not further purified. NMR showed that the product had a structure consistent with 4-(12-(tetrahydo-2H-pyran-2-yloxy)dodecanyloxy)benzoic acid.

Step 4

To a reaction flask was added the product from Step 3 above (7.5 g, 18 mmol), 3-methylhydroquinone (1.12 g,11 mmol), DCC (4.0 g, 18 mmol) and DMAP (1.0 g, 8 mmol) in THF (40 mL) and stirred at room temperature for 24 h. The resulting solid was filtered out and filtrate was concentrated. The crude product was then purified with flash chromatography (hexane/ethyl acetate, 20:1 volume ratio) to give 5.2 g of product. NMR showed that the product had a structure consistent with 2,5-bis(4-(12-tetrahydro-2H-pyran-2-yloxydodecyloxy) benzoyloxy)toluene represented by the following graphic formula.

Example 23 Step 1

The procedure of Step 1 of Example 22 was followed except that 1,12-dodecanediol was used in place of 6-chloro-6-hexan-1-ol. NMR showed that the product had a structure consistent with 2-(6-chlorohexyloxy)tetrahydro-2H-pyran.

Step 2

To a reaction flask was added the product of Step 1 above (6.4 g, 29 mmol), trans-4-(trans-4-hydroxycyclohexyl)phenol (5 g, 26 mmol), K₂CO₃ (12 g, 87 mmol) and NMP (20 mL). The resulting mixture was refluxed overnight. After cooling, the mixture was poured into water, extracted with hexanes/ethyl acetate (1:1 volume ratio), and then purified with flash chromatography to give 8.5 g of product. NMR showed that the product had a structure consistent with trans-4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)cyclohexanol.

Step 3

The procedure of Step 1 of Example 22 was followed except that 12-hydroxylauric acid was used in place of 1,12-dodecanediol. NMR showed that the product had a structure consistent with 12-(tetrahydro-2H-pyran-2-yloxy)dodecanoic acid.

Step 4

The procedure of Step 4 of Example 22 was followed except that the products from Steps 2 and 3 above were used in place of 3-methylhydroquinone and the product of Step 3 of Example 22. NMR showed that the product had a structure consistent with 2-(6-(4-(trans-4-(12-(1-tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy)cyclohexyl)phenoxy)hexyloxy)tetrahydro-2H-pyran represented by the following graphic formula.

Example 24

The procedure of Step 4 of Example 22 was followed except that 12-(tetrahydro-2H-pyran-2-yloxy)dodecanoic acid, which is the product from Step 3 of Example 23, and 4-(trans-4-hydroxycyclohexyl)phenol was used in place of 4-(12-(tetrahydo-2H-pyran-2′-yloxy) dodecanyloxy)benzoic acid and 3-methylhydroquinone. NMR showed that the product had a structure consistent with 2-(6-(4-(trans-4-(12-(tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy) cyclohexyl)phenoxy)-12-oxododecanoxy)tetrahydro-2H-pyran represented by the following graphic formula.

Example 25

The procedure of Step 4 of Example 22 was followed except that 4-(8-(tetrahydro-2H-pyran-2-yloxy)octyloxy)benzoic acid and biphenyl-4,4′-diol were used in place of 4-(12-(tetrahydo-2H-pyran-2-yloxy)dodecanyloxy)benzoic acid and 3-methylhydroquinone. NMR showed that the product had a structure consistent with 4,4′-bis(4-(8-(tetrahydro-2H-pyran-2-yloxy)octyloxy)benzoyloxy)biphenyl represented by the following graphic formula.

Example 26 Step 1

The procedure of Step 4 of Example 22 was followed except that 2,6-dihydroxy naphthalene and 4-(8-hydroxyoctyloxy)benzoic acid were used in place of 4-(12-(tetrahydo-2H-pyran-2-yloxy)dodecanyloxy)benzoic acid and 3-methyl-hydroquinone. NMR showed that the product had a structure consistent with 2,6-di(8-hydroxyoctanloxy)benzoyloxy)naphthalene.

Step 2

The procedure of Step 4 of Example 17 was followed except that 2,6-di(8-hydroxyoctanyloxy)benzoyloxy)naphthalene from step 1 above and 5.5 equivalents of epsilon-caprolactone were used in place of 4-(4-(6-(acryloyloxy)hexyloxy)benzoyloxy)phenyl 4-(6-hydroxyhexyloxy)benzoate and eight equivalents of epsilon-caprolactone. NMR showed that the white waxy product had a structure consistent with 2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)benzoyloxy}naphthalene with m+n having an average distribution of 5.0 as represented by the following graphic formula.

Example 27

The procedure of Example 26 was followed except that 3 equivalents of epsilon-caprolactone was used in place of 5.5 equivalents of epsilon-caprolactone. NMR showed that the product had a structure consistent with 2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy) hexanoyloxy)hexanoyloxy)hexanoyloxy)benzoyloxy}naphthalene with m+n having an average distribution of 3 as represented by the following graphic formula.

Example 28

The procedure of Step 5 of Example 1 was followed except that the product of Step 1 of Example 26, 2,6-di-(8-hydroxyoctyloxy)benzoyl)oxy)naphthalene, and 5.5 equivalents of epsilon-caprolactone were used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate and six equivalents of epsilon-caprolactone. NMR showed that the product has a structure consistent with 2,8-di{4-(6-(6-(6-(6-(6-(methacryloyloxy)hexanoyloxy) hexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)benzoyloxy}naphthalene with m+n having an average distribution of 5 as represented by the following graphic formula.

Example 29

The procedure of Example 19 was followed except that three equivalents of methacryloyl chloride was used in place of pentanoyl chloride. NMR showed that the product has a structure consistent with 1-(6-(6-(6-(6-(trans-4-(4-(4-(6-methacryloyloxyhexyloxy)-benzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 3.5 as represented by the following graphic formula.

Example 30

The procedure of Example 21 was followed except that three equivalents of methacryloyl chloride was used in place of 0.5 equivalents of succinoyl dichloride. NMR showed that the product has a structure consistent with 1-(6-(6-(8-(4-(4-(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 2.1 as represented by the following graphic formula.

Example 31

The procedure of Step 5 of Example 1 was followed except that the product of Step 3 of Example 17, 4-(4-(6-(acryloyloxy)hexyloxy)benzoyloxy)phenyl 4-(6-hydroxyhexyloxy)benzoate, and 8 equivalents of epsilon-caprolactone were used in place of 4-(trans-4-pentylcyclohexyl)phenyl 4-(6-hydroxyhexyloxy)benzoate and six equivalents of epsilon-caprolactone. NMR showed that the product has a structure consistent with 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl) phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one with n having an average distribution of 8 as represented by the following graphic formula.

Example 32 Measurement of Melting Points and Liquid Crystal Phase Transition Temperatures

Approximately 0.1-5 mg of a sample of each of Examples 1-31 was applied to a VWR Vista Vision™ microscope slide. A FISHERFINEST® Premium cover glass was applied to the sample. The resulting microscope slide was placed onto an INSTEC® HCS302 hot stage that was mounted on the sample stage of an OLYMPUS® BX51 polarized light microscope so that the sample spot was in the optical path of the microscope. The microscope was also equipped with an INSTEC® STC200 temperature controller so that the temperature of the hot stage was controlled and a DIAGNOSTIC INSTRUMENTS 11.2 Color Mosaic camera so that the phase transitions could be observed from a computer display. Melting points for non-liquid crystal materials and phase transition temperatures of liquid crystal materials were measured by observing the samples during heating at a rate of 1° C./min starting at 25° C. The melting points and phases below 25° C. were not determined unless indicated. In some cases, the sample was heated until it reached the Isotropic phase and then cooled at 1° C./min to determine the phase transition temperatures during the cooling process as indicated in Table 2. The phases of the liquid crystals were determined according to the texture that appeared during the heating and cooling processes. Textures of Liquid Crystals by Dietrich Demus and Lothar Richter, published by Verlag Chemie, Weinheim & New York in 1978 was used in the identification of the different liquid crystal phases listed in Table 2.

TABLE 2 Phase Transition Temperature Data Example No. Phase Transition Temperature Example 1 25 Sx // 37 I Example 2 25 K+S_(A) // 100 I Example 3 25 K+Glass // 62 S_(A) // 76 N // 91 I Example 4 Heating: 25 K+Glass // 34 I, Cooling: 34 Sx Example 5 25 Sx // 49 I Example 6 25 K // 50 I Example 7 25 S_(A) // 34-38 I Example 8 25 K // 45 S_(A) // 76 N // 88 I Example 9 25 K // 51 S_(A) // 89 N // 108 I Example 10 25 K // 51 S_(A) // 77 N // 92 I Example 11 Heating: 25 K // 50 N // 96 I, Cooling: 92 N // 50 S_(B) Example 12 25 K // 80 S_(A) // 134 I Example 13 Heating: 25 S_(A) // 129 I, Cooling: 126 S_(A) Example 14 Heating: 25 S_(A) // 108 I, Cooling: 102 S_(A) Example 15 25 K+Glass // 46 N // 208 I Example 16 Heating: 25 S_(X) // 68 N // 79 I, Cooling: 73 N // 63 S_(X) Example 17 Heating: 25 N // 43 I, Cooling: 33 N Example 18 Heating: 25 S_(A) // 86-91 I, Cooling: 82-84 S_(A) Example 19 Heating: 25 Sx // 34-38 I, Cooling: 33-35 Sx // 25 K Example 20 Heating: 25 Sx // 53-61 I, Cooling: 51-56 Sx Example 21 Heating: 25 Sx // 108 Sc // 124-130 N // 133-160 I Cooling: 140-145 N // 120 Sc // 102-104 Sx Example 22 Heating: 25 Sc // 55-56 N // 97-98 I Cooling: 96-98 N // 53-54 Sc Example 23 Heating: 25 K // 50-51 I, Cooling: 20-28 K Example 24 Heating: 25 K // 51-56 I, Cooling: 46-48 Sx // 38-39 K Example 25 Heating: 25 K // 132-133 Sc // 198-200 N // 238-240 I Cooling: 235-236 N // 196-197 Sc // 123-125 K Example 26 Heating: 25 K // 60-64 I, Cooling: 47-49 K Example 27 Heating: 25 K // 86-90 I, Cooling: 70-72 K Example 28 Heating: 25 K // 53-56 I, Cooling: 42-44 K Example 29 Heating: 25 Sx // 32-36 I, Cooling: 30-34 Sx // 25 K Example 30 Heating: 25 K // 30 Sx // 113-114 Sc // 151-152 N // 153-166 I Cooling: 160-154 N // 150-152 Sc // 111-112 Sx Example 31 Heating: 25 K // 48 I, Cooling: 39 K

The following abbreviations were used in the table: S represents the Smectic phase; Sx represents the Smectic unidentified phase; SA represents the Smectic A phase; S_(B) represents the Smectic B phase; S_(C) represents the Smectic C phase; N represents the Nematic phase; I represents the Isotropic phase; K represents a crystalline structure; and Glass represents an amorphous state with no ordered structure. Note that all numbers represent the temperature in ° C. at which the adjacent phase abbreviation occurred. Each phase measured is separated by // meaning that the phase extended until the next temperature or temperature range listed. For example, 25 Sx//37 I, indicates that the Smectic unidentified phase was present from 25° C. to about 37° C. when the Isotropic phase occurred. Observation of the sample's phase started at room temperature (25° C.) and reported the next phase transition temperature unless indicated otherwise. 

1. A mesogen containing compound represented by one of the following structures:

wherein, a) each X is independently: i) a group R, ii) a group represented by -(L)_(y)-R, iii) a group represented by -(L)-R, iv) a group represented by -(L)_(w)-Q; vii) a group represented by

vi) a group represented by -(L)_(y)-P; or vii) a group represented by -(L)_(w)-[(L)_(w)-P]_(y); b) each P is a reactive group independently chosen from a group Q, amino, alkylamino, nitro, acrylate, methacrylate, 2-chloroacrylate, 2-phenylacrylate, acryloylphenylene, acrylamide, methacrylamide, 2-chloroacrylamide, 2-phenylacrylamide, oxetane, glycidyl, cyano, vinyl ether, vinyl ester, a styrene derivative, siloxane, ethyleneimine derivatives, or substituted or unsubstituted chiral or non-chiral monovalent or divalent groups chosen from steroid radicals, terpenoid radicals, alkaloid radicals and mixtures thereof, wherein the substituents are independently chosen from alkyl, alkoxy, amino, cycloalkyl, alkylalkoxy, fluoroalkyl, cyano, cyanoalkyl, cyanoalkoxy or mixtures thereof, or P is a structure having from 2 to 4 reactive groups or P is an unsubstituted or substituted ring opening metathesis polymerization precursor; c) the group Q is hydroxy, amine, alkenyl, alkynyl, azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol, isocyanato, thioisocyanato, acryloxy, methacryloxy, 2-(acryloxy)ethylcarbamyl, 2-(methacryloxy)ethylcarbamyl, aziridinyl, allyloxycarbonyloxy, epoxy, carboxylic acid, carboxylic acid derivatives selected from carboxylic ester, amide and carboxylic anhydride, or acyl halide, unsubstituted cinnamic acid derivatives, cinnamic acid derivatives that are substituted with at least one of methyl, methoxy, cyano and halogen; d) each L is independently chosen for each occurrence, the same or different, from a single bond, a polysubstituted, monosubstituted, unsubstituted or branched spacer independently chosen from arylene, (C₁-C₃₀)alkylene, (C₁-C₃₀)alkylenecarbonyloxy, (C₁-C₃₀)alkyleneamino, (C₁-C₃₀)alkyleneoxy, (C₁-C₃₀)perfluoroalkylene, (C₁-C₃₀)perfluoroalkyleneoxy, (C₁-C₃₀)alkylenesilyl, (C₁-C₃₀)dialkylenesiloxyl, (C₁-C₃₀)alkylenecarbonyl, (C₁-C₃₀)alkyleneoxycarbonyl, (C₁-C₃₀)alkylenecarbonylamino, (C₁-C₃₀)alkyleneaminocarbonyl, (C₁-C₃₀)alkyleneaminocarbonyloxy, (C₁-C₃₀)alkyleneaminocarbonylamino, (C₁-C₃₀)alkyleneurea, (C₁-C₃₀)alkylenethiocarbonylamino, (C₁-C₃₀)alkyleneaminocarbonylthio, (C₂-C₃₀)alkenylene, (C₁-C₃₀)thioalkylene, (C₁-C₃₀)alkylenesulfone, or (C₁-C₃₀)alkylenesulfoxide, wherein each substituent is independently chosen from (C₁-C₅)alkyl, (C₁-C₅)alkoxy, fluoro, chloro, bromo, cyano, (C₁-C₅)alkanoate ester, isocyanato, thioisocyanato, or phenyl; e) the group R is selected from hydrogen, C₁-C₁₈ alkyl, C₁-C₁₈ alkoxy, C₁-C₁₈ alkoxycarbonyl, C₃-C₁₀ cycloalkyl, C₃-C₁₀ cycloalkoxy, poly(C₁-C₁₈ alkoxy), or a straight-chain or branched C₁-C₁₈ alkyl group that is unsubstituted or substituted with cyano, fluoro, chloro, bromo, or C₁-C₁₈ alkoxy, or poly-substituted with fluoro, chloro, or bromo; and f) the groups Mesogen-1 and Mesogen-2 are each independently a rigid straight rod-like liquid crystal group, a rigid bent rod-like liquid crystal group, or a rigid disc-like liquid crystal group; g) the group T is selected from P and hydrogen, aryl, alkyl, alkoxy, alkylalkoxy, alkoxyalkoxy, polyalkylether, (C₁-C₆)alkyl (C₁-C₆)-alkoxy (C₁-C₆)alkyl, polyethyleneoxy and polypropyleneoxy; wherein w is an integer from 1 to 26, y is an integer from 2 to 25, z is 1 or 2, provided that when: (i) the group X is represented by R, then w is an integer from 2 to 25, and z is 1; (ii) the group X is represented by -(L)_(y)-R, then w is 1, y is an integer from 2 to 25, and z is 1; (iii) the group X is represented by -(L)_(w)-R, then w is an integer from 3 to 26, and z is 2; (iv) the group X is represented by -(L)_(w)-Q; then if P is represented by the group Q at least one Q is selected from hydroxy, azido, silyl, silylhydride, oxy(tetrahydro-2H-pyran-2-yl), thiol, isocyanato, thioisocyanato, 2-(acryloxy)ethylcarbamyl, 2-(methacryloxy)ethylcarbamyl, aziridinyl, allyloxycarbonyloxy, carboxylic acid, carboxylic ester, amide, carboxylic anhydride, and acyl halide, then w is 1, and z is 1; and if P is other than the group Q, then each w is independently an integer from 1 to 26, and z is 1; (v) the group X is represented by

then w is 1, y is an integer from 2 to 25, with the proviso that -(L)_(y)- comprises at least two groups L that are different from a single bond and z is 1; (vi) the group X is represented by -(L)_(y)-P, with the proviso that at least one P is different from an oxetane functional group, then w is 1, y is an integer from 2 to 25, and z is 1 and -(L)_(y)- comprises a linear sequence of at least 25 bonds, preferably at least 30 bonds between the mesogen and P; (vii) the group X is represented by -(L)_(w)-[(L)_(w)-P]_(y), then each w is independently an integer from 1 to 25, y is an integer from 2 to 6, whereby and z is 1; and in -(L)_(y)- and -(L)_(w)- no two arylene groups are linked by a single bond.
 2. The mesogen containing compound of claim 1, wherein the groups Mesogen-1 and Mesogen-2 independently have a structure represented by: —[S¹]_(c)-[G¹-[S²]_(d)]_(d′)-[G²-[S³]_(e)]_(e′)-[G³-[S⁴]_(f)]_(f′)—S⁵— wherein: (i) each G¹, G², and G³ is independently chosen for each occurrence from: a divalent group chosen from: an unsubstituted or a substituted aromatic group, an unsubstituted or a substituted alicyclic group, an unsubstituted or a substituted heterocyclic group, and mixtures thereof, wherein substituents are chosen from: thiol, hydroxy(C₁-C₁₈)alkyl, isocyanato(C₁-C₁₈)alkyl, acryloyloxy, acryloyloxy(C₁-C₁₈)alkyl, halogen, C₁-C₁₈ alkoxy, poly(C₁-C₁₈ alkoxy), amino, amino(C₁-C₁₈)alkylene, C₁-C₁₈ alkylamino, di-(C₁-C₁₈)alkylamino, C₁-C₁₈ alkyl, C₂-C₁₈ alkenyl, C₂-C₁₈ alkynyl, C₁-C₁₈ alkyl(C₁-C₁₈)alkoxy, C₁-C₁₈ alkoxycarbonyl, C₁-C₁₈ alkylcarbonyl, C₁-C₁₈ alkyloxycarbonyloxy, aryloxycarbonyloxy, perfluoro(C₁-C₁₈)alkylamino, di-(perfluoro(C₁-C₁₈)alkyl)amino, C₁-C₁₈ acetyl, C₃-C₁₀ cycloalkyl, C₃-C₁₀ cycloalkoxy, isocyanato, amido, cyano, nitro, a straight-chain or branched C₁-C₁₈ alkyl group that is mono-substituted with cyano, halo, or C₁-C₁₈ alkoxy, or poly-substituted with halo, and a group comprising one of the following formulae: -M(T)_((t-1)) and -M(OT)_((t-1)), wherein M is chosen from aluminum, antimony, tantalum, titanium, zirconium and silicon, T is chosen from organofunctional radicals, organofunctional hydrocarbon radicals, aliphatic hydrocarbon radicals and aromatic hydrocarbon radicals, and t is the valence of M; (ii) c, d, e, and f are each independently chosen from an integer ranging from 0 to 20, inclusive; d′, e′ and f′ are each independently an integer from 0 to 4 provided that a sum of d′+e′+f′ is at least 2; and each S¹, S², S³, S⁴, and S⁵ is independently chosen for each occurrence from a spacer unit chosen from: (A) —(CH₂)_(g)—, —(CF₂)_(h)—, —Si(CH₂)_(g)—, or —(Si(CH₃)₂O)_(h)—, wherein g is independently chosen for each occurrence from 1 to 20 and h is a whole number from 1 to 16 inclusive; (B) —N(Z)—, —C(Z)═C(Z)—, —C(Z)═N—, —C(Z′)₂—C(Z′)₂—, or a single bond, wherein Z is independently chosen for each occurrence from hydrogen, C₁-C₆ alkyl, cycloalkyl and aryl, and Z′ is independently chosen for each occurrence from C₁-C₆ alkyl, cycloalkyl and aryl; or (C) —O—, —C(O)—, —C≡C—, —N═N—, —S—, —S(O)—, —S(O)(O)—, —(O)S(O)O—, —O(O)S(O)O— or straight-chain or branched C₁-C₂₄ alkylene residue, said C₁-C₂₄ alkylene residue being unsubstituted, mono-substituted by cyano or halo, or poly-substituted by halo; provided that when two spacer units comprising heteroatoms are linked together the spacer units are linked so that heteroatoms are not directly linked to each other and when S₁ and S₅ are linked to another group, they are linked so that two heteroatoms are not directly linked to each other.
 3. The mesogen containing compound of claim 1, wherein the compound is selected from the group consisting of: a) 1,12-bis{2-(4-(4-(4-(3-(methacryloyloxy)propyloxy)benzoyloxy)phenyl)benzoyloxy)ethyloxy)dodecyl-1,12-dione; b) 1,12-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy)dodecyl-1,12-dione; c) 1,10-bis(6-(4-(4-(4-(6-(methacryloyloxy)hexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy) 2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluorodecyl-1,10-dione; d) 1,12-bis{6-(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)benzoyloxy)hexyloxy)dodecyl-1,12-dione; e) 1-{3-(4-(3-(4-(6-(4(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy)-4-oxobutoyloxy)propyloxy)benzoyloxy)propyloxy}-4-{(6-(4(4-(4-(6-methacryloyloxyhexyloxy)benzoyloxy)phenyl)benzoyloxy)hexyloxy)}butane-1,4-dione; f) 1-{3-(4-(3-(4-6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-4-oxobutanoyloxy)propyloxy)benzoyloxy)propyloxy}-4-{6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)butane-1,4-dione; g) 2,2′-bis (6-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexanoyloxy)-6-hexanoyloxy)diethylether; h) 1-{6-(6-(6-(6-(6-(6-(6-(4-(6-(4-(4-(4-nonylbenzoyloxy)phenoxycarbonyl)phenoxy)hexyloxy)-4-oxobutanoyloxy)hexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy)-6-carbonyloxyhexyloxy}-4-{6-(4-(6-(4-(4-(4-nonylbenzoyloxy)phenoxycarbonyl)phenoxy)hexyloxy}butane-1,4-dione; i) 2,5-bis(4-(12-hydroxydodecyloxy)benzoyloxy))toluene; j) 2,5-bis(4-(12-tetrahydro-2H-pyran-2-yloxydodecyloxy)benzoyloxy)toluene; k) 2-(6-(4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)benzyloxy)phenoxy)hexyloxy)tetrahydro-2H-pyran; l) (1R,4R)-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)cyclohexane-1,4-dicarboxylate; m) 2-(6-(4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)dodecyloxy)benzoyloxy)phenoxy)hexyloxy)tetrahydro-2H-pyran; n) 6-(4-(4-(12-hydroxydodecyloxy)benzoyloxy)phenoxy)hexan-1-ol; o) 2-(5-(trans-4-(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)cyclohexyl)benzyloxy)pentyloxy)tetrahydro-2H-pyran; p) 6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(6-(3-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy)benzoate; q) 2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6-(tetrahydro-2H-pyran-2-yloxy)hexyl)benzoate; r) 2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6-methacryloyloxyhexyl)benzoate; s) 2,5-bis{6-(4-(6-(4-(trans-4-propylcyclohexyl)phenoxy)hexyloxy)-4-oxobutoyloxy)hexyloxy}-1-(6-hydroxyhexyl)benzoate; t) 6-(tetrahydro-2H-pyran-2-yloxy)hexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)octyloxy)-4-oxobutoyloxy)octyloxy)benzoate; u) 6-hydroxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)octyloxy)-4-oxobutoyloxy)octyloxy)benzoate; v) 6-methacryloyloxyhexyl 2,5-bis(8-(3-(8-(4-(4-(trans-4-pentylcyclohexyl)phenoxylcarbonyl)phenoxy)octyloxy)-4-oxobutoyloxy)octyloxy)benzoate; w) 1,2-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)ethanone; x) 2-(6-(4-(trans-4-(12-(1-tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy)cyclohexyl)phenoxy)hexyloxy)tetrahydro-2H-pyran; y) 1-(11-(4-(trans-4-(4-(6-(1-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)cyclohexyloxycarbonyl)phenoxy)undecanoxy)prop-2-en-1-one; z) 1-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; aa) 1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; bb) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol; cc) 1,2-bis(4-(6-(tetrahydro-2H-pyran-2-yloxy)hexyloxy)phenyl)ethane; dd) 2-(6-(trans-4-(4-(12-(tetrahydro-2H-pyran-2-yloxy)dodecanoyloxy)cyclohexyl)phenoxy)-2-oxododecanoxy)tetrahydro-2H-pyran; ee) 1-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ff) 1-(5-(5-(5-(5-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; gg) 1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; hh) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ii) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl) phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; jj) 1-(6-(5-(5-(6-(5-(6-(5-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; kk) 1-(6-(5-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ll) 1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; mm) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; nn) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; oo) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-propylcyclohexyl)phenyloxy)hexanoyl)hexanoyl)hexanoyl)hexanoyl)hexanoyl)hexanoyl)-hexanoyl)hexanoyloxy)-prop-2-ene; pp) 1-{3-(3-methacryloyloxy-2,2-dimethylpropyloxy)-3-oxo-2-methylpropyl}-3-{(8-(4-(trans-4-(trans-4-pentylcyclohexyl)-cyclohexyloxycarbonyl)phenoxy)octyloxycarbonyl)ethyl)}-hexamethylenetrisiloxane; qq) 2,5-bis(4-(8-hydroxyoctyloxy)benzoyloxy)toluene; rr) 2,5-bis(4-(8-(6-hydroxyhexyloyloxy)octyloxy)benzoyloxy)toluene; ss) 1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; tt) 1-(6-(6-(6-(8-(4-(4-(4-hexyloxybenzoyloxy)phenoxy-carbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; uu) 4-{4-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexyloxy)benzoyloxy}-3-methoxy-1-ethyl cinnamate; vv) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ww) 1-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; xx) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; yy) 1-(6-(6-(6-(6-(trans-4-(4-(4-hexyloxybenzoyloxy)phenoxycarbonyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; zz) 2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy) hexanoyloxy)benzoyloxy}naphthalene; aaa) 2,8-di{4-(6-(6-(6-(6-(6-(methacryloyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)benzoyloxy}aphthalene; bbb) 2,8-di{4-(6-(6-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxy)hexanoyloxy)hexanoyloxy)benzoyloxy}naphthalene; ccc) 4-{4-(6-(6-(6-hydroxyhexanoyloxy)hexanoyloxyl)octyloxy)benzoyloxy}-3-methoxy-1-ethyl cinnamate; ddd) 1-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; eee) 1-(6-(6-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; fff) 4,4′-bis(4-(8-(tetrahydro-2H-pyran-2-yloxy)octyloxy)benzoyloxy)biphenyl; ggg) 1-(6-(4-(4-(trans-4-(6-hydroxyhexyloxy)cyclohexyl)phenyloxycarbonyl)phenyloxy)hexyloxy)prop-2-en-1-one; hhh) 1-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one iii) 4,4′-bis(4-(8-hydroxyoctyloxy)benzoyloxy)biphenyl; jjj) 1-(6-(6-(6-(6-(trans-4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; kkk) 1-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)pentan-1-one; lll) 2-(8-(4-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenoxy)octyloxy)tetrahydro-2H-pyran; mmm) 8-(4-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenoxy)octan-1-ol; nnn) 1,4-bis-{(6-(6-(6-(6-(6-(6-(trans-4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy}butan-1,4-dione; ooo) 1-(6-(6-(6-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ppp) 1,4-bis{(6-(6-(6-(6-(6-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl) phenyloxycarbonyl)phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy}butan-1,4-dione; qqq) 1-(6-(8-(4-(4-(4-(4-(8-(6-methacryloyloxy)hexyloyloxy)octyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenyloxy)octyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; rrr) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; sss) 1-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; ttt) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; uuu) 1-(6-(6-(6-(6-(6-(6-(6-(4-(4-(trans-4-pentylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; vvv) 1-(6-(6-(8-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; www) 1-(5-(5-(5-(5-(5-(5-(6-(4-(4-(trans-4-propylcyclohexyl)phenyloxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; xxx) 1-(5-(5-(6-(5-(6-(5-(6-(6-(4-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-6-oxohexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; yyy) 1-(6-(8-(4-(4-(4-(4-(8-(6-methacryloyloxy)hexyloyloxy)octyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenyloxy)octyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; zzz) 1-(11-(4-(4-(4-(6-(11-(tetrahydro-2H-pyran-2-yloxy)undecanyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)hexyloxy)prop-2-en-1-one; aaaa) 1,4-bis(4-(11-(tetrahydro-2H-pyran-2-yloxy)undecanyloxy)benzoyloxy)benzene; bbbb) 1-(6-(6-(6-(4-(trans-4-pentylcyclohexyl)phenoxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; cccc) 1-(6-(6-(6-(4-(4-benzoyloxyphenoxycarbonyl)phenoxy) hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; dddd) 1-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-benzoyloxyphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; eeee) 1-(3-(3-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-2-methylprop-2-en-1-one; ffff) 1-(3-(3-(3-(3-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-3-carbonyloxypropyloxy)-2-methylprop-2-en-1-one; gggg) 1-(6-(6-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxo)-2-methylprop-2-en-1-one; hhhh) 1-(6-(6-(6-(6-(6-(6-(6-(6-(8(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; iiii) 1-(5-(6-(4-(trans-4-propylcyclohexyl)phenoxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; jjjj) 1-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; kkkk) 1-(5-(5-(5-(5-(5-(5-(5-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; llll) 2-(6-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)hexan-1-ol; mmmm) 1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methylbenzoyloxy)phenyloxy carbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; nnnn) 1-(5-(5-(5-(5-(5-(5-(5-(5-(5-(6-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; oooo) 1-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methylbenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-1-carbonylaminoethyloxy)-2-methylprop-2-en-1-one; pppp) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; qqqq) 1-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; rrrr) 1-(5-(5-(5-(5-(5-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenyloxy)hexyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-5-oxo pentyloxy)-5-oxopentyloxy)-5-oxopentyloxy)-2-methylprop-2-en-1-one; ssss) 2-(6-(4-(4-(4-(6-acryloyloxy)hexyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)undecan-1-ol; tttt) 1-(6-(6-(6-(11-(4-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyl)phenyloxycarbonyl)phenyloxy)undecanyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; uuuu) 1-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-methoxybenzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; vvvv) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; wwww) 1-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; xxxx) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-methylbenzoyloxy)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; yyyy) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-ethoxyphenoxycarbonyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; zzzz) 1-(6-(6-(6-(6-(4-(4-(4-ethoxyphenoxycarbonyl)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-2-methylprop-2-en-1-one; aaaaa) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-phenylphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; bbbbb) 1-(6-(6-(6-(4-(4-phenylphenoxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; ccccc) 1-(6-(6-(6-(trans-4-(4-(4-phenylphenoxycarbonyl)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; ddddd) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(trans-4-(4-(4-phenylphenoxycarbonyl)phenyl)cyclohexyloxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)prop-2-en-1-one; eeeee) 1-(6-(6-(6-(6-(6-(6-(6-(6-(6-(4-(4-(4-(6-acryloyloxyhexyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)hexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexanol; fffff) 8-(4-(4-(4-(2,3-diacryloyloxypropyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octanol; ggggg) 6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(2,3-diacryloyloxypropyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol; hhhhh) 8-(4-(4-(4-(11-acryloyloxyundecyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octanol; iiiii) 6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(11-acryloyloxyundecanyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol; jjjjj) 8-(4-(4-(4-(8-acryloyloxyoctyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octanol; kkkkk) 6-(6-(6-(6-(6-(6-(6-(6-(8-(4-(4-(4-(11-acryloyloxyoctyloxy)benzoyloxy)phenoxycarbonyl)phenoxy)octyloxy)6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexan-1-ol; lllll) 1-[3-(6-(acryloyloxy)hexanoyloxy)-2-((6-(acryloyloxy)hexanoyloxy)methyl)-2-methylpropyloxy]-4-[6-(4-((4-(4-methylbenzoyloxy)phenoxy)carbonyl)phenoxy)hexyloxy]-butan-1,4-dione; mmmmm) 1-[3-(acryloyloxy)-2,2-bis(acryloyloxymethyl)propyloxy]-4-[8-(4-((4-(4-methylbenzoyloxy)phenoxy)carbonyl)phenoxy)octyloxy]butan-1,4-dione; and nnnnn) 1-(6-(6-(6-(6-(6-(8-(4-(4-(4-(8-acryloyloxyoctyloxy)benzoyloxy)phenyloxycarbonyl)phenoxy)octyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)-6-oxohexyloxy)pentan-1-one.
 4. The mesogen containing compound of claim 1, wherein the compound comprises a liquid crystal monomer.
 5. The mesogen containing compound of claim 1, wherein the compound comprises a di-functional monomer that can be incorporated into a polymer backbone.
 6. A polymer comprising the mesogen containing compound according to claim
 1. 7. A liquid crystal composition comprising: a mesogen containing compound according to claim 1; and optionally, a liquid crystal polymer.
 8. The composition of claim 7, wherein the liquid crystal polymer is present and comprises a block or non-block copolymer comprised of the mesogen containing compound incorporated into the copolymer.
 9. The composition of claim 7, further comprising at least one of a photochromic compound, a dichroic compound, a photochromic-dichroic compound, a photosensitive material, a non-photosensitive material, and one or more additives, wherein the one of more additives are chosen from the group consisting of a liquid crystal, a liquid crystal property control additive, a non-linear optical material, a dye, an alignment promoter, a kinetic enhancer, a photoinitiator, a thermal initiator, a surfactant, a polymerization inhibitor, a solvent, a light stabilizer, a thermal stabilizer, a mold release agent, a rheology control agent, a gelator, a leveling agent, a free radical scavenger, a coupling agent, a tilt control additive, a block or non-block polymeric material, and an adhesion promoter.
 10. The composition of claim 9, wherein the at least one photochromic compound or photochromic-dichroic compound is chosen from the group consisting of indeno-fused naphthopyrans, naphtho[1,2-b]pyrans, naphtho[2,1-b]pyrans, spirofluoroeno[1,2-b]pyrans, phenanthropyrans, quinolinopyrans, fluoroanthenopyrans, spiropyrans, benzoxazines, naphthoxazines, spiro(indoline)naphthoxazines, spiro(indoline)pyridobenzoxazines, spiro(indoline)fluoranthenoxazines, spiro(indoline)quinoxazines, fulgides, fulgimides, diarylethenes, diarylalkylethenes, diarylalkenylethenes, non-thermally reversible photochromic compounds, and mixtures thereof.
 11. An article of manufacture comprising a mesogen containing compound according to claim
 1. 12. The article of manufacture of claim 11, wherein the article is an optical element comprising: a substrate; and an at least partial layer on at least a portion of the substrate, the layer comprising said mesogen containing compound.
 13. The article of claim 12, wherein the article is an optical element, wherein the at least partial layer is at least partially aligned by exposing at least a portion of the layer to a magnetic field, an electric field, linearly polarized radiation, and/or shear force.
 14. The article of claim 12, wherein the article is an optical element, wherein the at least partial layer is adapted to switch from a first state to a second state in response to at least actinic radiation and to revert back to the first state in response to thermal energy.
 15. The article of claim 14, wherein the article is an optical element, wherein the at least partial layer is adapted to linearly polarize at least transmitted radiation in at least one of the first state and the second state.
 16. The article of claim 12, wherein the article is an optical element, wherein at least partial layer comprises a liquid crystal phase having at least one of a nematic phase, a smectic phase, or a chiral nematic phase.
 17. The of claim 12, wherein the article is an optical element chosen from an ophthalmic element, a display element; a window; a mirror; and an active and a passive liquid crystal cell element.
 18. The article of claim 17 wherein the article is an ophthalmic element chosen from a corrective lens, a non-corrective lens, a contact lens, an intra-ocular lens, a magnifying lens, a protective lens, and a visor.
 19. The article of manufacture of claim 11, wherein the article is liquid crystal cell comprising: a first substrate having a first surface; a second substrate having a second surface, wherein the second surface of the second substrate is opposite and spaced apart from the first surface of the first substrate so as to define a region; and said mesogen containing compound positioned within the region defined by the first surface and the second surface.
 20. The article of claim 19, wherein the article is a liquid crystal cell further comprising an at least partial layer chosen from linearly polarizing layers, circularly polarizing layers, elliptically polarizing layers, photochromic layers, reflective layers, tinted layers, retarder layers, and wide-angle view layers connected to at least a portion of a surface of at least one of the first substrate and the second substrate.
 21. The article of claim 19, wherein the article is a liquid crystal cell wherein the cell is a pixelated cell comprising a plurality of regions or compartments.
 22. A method of forming an ophthalmic element comprising: formulating a liquid crystal composition comprising the mesogen containing compound of claim 1; coating at least a portion of a substrate with the liquid crystal composition; at least partially aligning at least a portion of the liquid crystal composition in the coating; and curing the liquid crystal coating layer. 